Polymer Property : Tensile Strength at Break = 13.7 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	>= 13.7 MPa	>= 1990 psi
Sibur 153-01K 1st Grade Polyethylene for Cable Production For application of insulation and protective coverings for wiring and cables by extrusion method.
Tensile Strength at Break	>= 13.7 MPa	>= 1990 psi
Sibur 153-01K Superior Quality Polyethylene for Cable Production For application of insulation and protective coverings for wiring and cables by extrusion method.
Tensile Strength at Break	>= 13.7 MPa	>= 1990 psi
Sibur 153-02K 1st Grade Polyethylene for Cable Production For application of insulation and protective coverings for wiring and cables by extrusion method.
Tensile Strength at Break	>= 13.7 MPa	>= 1990 psi
Sibur 153-02K Superior Quality Polyethylene for Cable Production For application of insulation and protective coverings for wiring and cables by extrusion method.
Tensile Strength at Break	13.7 MPa	1990 psi	500 mm/min; GOST 11262
Sibur 15303-003 Low Density Polyethylene For production of films and film articles, including thermoset films, thin films, food contact grade films (including tight packing), general-purpose films, and bags.
Tensile Strength at Break	>= 13.7 MPa	>= 1990 psi
Sibur 153-10K Superior Quality Polyethylene for Cable Production For application of insulation and protective coverings for wiring and cables by extrusion method.
Tensile Strength at Break	>= 13.7 MPa	>= 1990 psi
Sibur ONZ-40 Compound M-258 Polyvinyl Chloride (PVC) Shall correspond to control sample, approved in accordance with the established procedure. Pores, which can be seen by eyes, are not allowed. Plastic shall no burn at stop of worm extruder for a p..
Tensile Strength at Break	>= 13.7 MPa	>= 1990 psi
Sibur 153-10K 1st Grade Polyethylene for Cable Production For application of insulation and protective coverings for wiring and cables by extrusion method.
Tensile Strength at Break	13.7 MPa	1990 psi	ASTM D638
Asahi Glass AFLAS® MZ TFE/P/VdF Fluoroelastomer AFLAS® MZ is a terpolymer composed of tetrafluoroethylene, propylene and vinylidene fluoride. AFLAS® MZ offers a good balance of chemical resistance and improved low temperature performance and is..
Tensile Strength at Break	13.7 MPa	1990 psi	ASTM D638
Bayshore Vinyl Compounds BVC 1204-70 Clear Vinyl Compound BVC 1204-70 Clear has been designed as a general purpose extrusion compound for use in spiral hose, window profiles and applications where high gloss is required. This material offers excellent ext..