Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 99.0 MPa | 14400 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® 3413HF PC (Asia Pacific) 30% glass reinforced, high flow PC. |
|||
Tensile Strength at Break | 99.0 MPa | 14400 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP DFL24 PC (Europe-Africa-Middle East) LNP* Lubricomp* DFL24 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. |
|||
Tensile Strength at Break | 99.0 MPa | 14400 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP DFL34 PC (Europe-Africa-Middle East) LNP* Lubricomp* DFL34 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. |
|||
Tensile Strength at Break | 99.0 MPa | 14400 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® 3413HF PC 30% glass reinforced, high flow PC. |
|||
Tensile Strength at Break | 99.0 MPa | 14400 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRILOY RF203 PA 66 (Europe-Africa-Middle East) LNP* LUBRILOY* RF203 is a compound based on PA 66 resin containing Glass Fiber, Proprietary Lubricant. Added features include: Internally Lubricated. |
|||
Tensile Strength at Break | 99.0 MPa | 14400 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON DX02728C PC LNP STAT-KON* DX02728C is a compound based on Polycarbonate resin containing Proprietary Filler(s) Added features of this material include: Clean Compounding System, Electrically Conductive. |
|||
Tensile Strength at Break | 99.0 MPa | 14400 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® 780 PBT 40% gl/min, UL94 V-0 rated. Nonblooming flame retardant. Circuit breaker handles/housings, motor coil housings. |
|||
Tensile Strength at Break | 99.0 MPa | 14400 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® 780 PBT (Asia Pacific) 40% gl/min, UL94 V-0 rated. Nonblooming flame retardant. Circuit breaker handles/housings, motor coil housings. |
|||
Tensile Strength at Break | 99.0 MPa | 14400 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-KON DX99873C PC LNP STAT-KON* DX99872C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Clean Compounding System, Electrically Conductive. |
|||
Tensile Strength at Break | 99.0 MPa | 14400 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON WEF42I PBT LNP* STAT-KON* WEF42I is a compound based on PBT resin containing 10% Carbon Fiber, 20% Glass Fiber. Added features of this grade include: High Impact, Electrically Conductive. |
|||
Tensile Strength at Break | 99.0 MPa | 14400 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP DX06313 PC (Asia Pacific) Polycarbonate base, 30% glass fiber reinforced, impact modified material. Thinwall housing, mobile phone. Some light color grades may have lower impact data than nature and black grade. |
|||
Tensile Strength at Break | 99.0 MPa | 14400 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP JF006LXZ PES LNP* THERMOCOMP* JF006LXZ is a compound based on Polyethersulfone resin containing 30% Glass Fiber. Added features of this material include: Low Extractible. |
|||
Tensile Strength at Break | 99.0 MPa | 14400 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP JF006LXZ PES (Asia Pacific) LNP* Thermocomp* JF006LXZ is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Low Extractible. |
|||
Tensile Strength at Break | 99.0 MPa | 14400 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP KF004A Acetal Homopolymer LNP THERMOCOMP* KF004A is a compound based on Acetal Homopolymer resin containing 20% Glass Fiber. |
|||
Tensile Strength at Break | 99.0 MPa | 14400 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Verton NV0041EV_GY7E147 PC+ABS Preliminary data for 20% long fiber single pellet non-halogen FR color filled PC/ABSThis data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 99.0 MPa | 14400 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP IF003 PA 6/12 LNP THERMOCOMP* IF003 is a compound based on Nylon 6/12 resin containing 15% Glass Fiber. |
|||
Tensile Strength at Break | 99.0 MPa | 14400 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP RX93402 PA 66 LNP THERMOCOMP* RX93402 is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Flame Retardant. |
|||
Tensile Strength at Break | 99.3 MPa | 14400 psi | ASTM D638 |
A. Schulman ComAlloy® E-12812 Easy Flow Glass Reinforced Nylon 66 Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength at Break | 99.0 MPa | 14400 psi | ASTM D638 |
Unitika UG-100-20 Engineering Plastic Excellent creep resistance, dimensional stability at high temperatureInformation provided by Unitika Ltd. |
|||
Tensile Strength at Break | 99.3 MPa | 14400 psi | ASTM D638 |
A. Schulman ComAlloy® E-12812 Easy Flow Glass Reinforced Nylon 66 Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength at Break | 99.0 MPa | 14400 psi | ISO 527-2 |
Tisan TISLAMID® 6 30% Glass Filled Impact Modified Nylon 6 TISLAMID has a wide area of application in electric/electronic, automotive, durable goods and telecommunications industries. It demonstrates characteristics such as Excellent chemical resistanceElec.. |
|||
Tensile Strength at Break | 99.0 MPa | 14400 psi | ISO 527-2 |
Tisan TISLAMID® 6 30% Glass Filled Impact Modified, Heat Stabilized Nylon 6 TISLAMID has a wide area of application in electric/electronic, automotive, durable goods and telecommunications industries. It demonstrates characteristics such as Excellent chemical resistanceElec.. |
|||
Tensile Strength at Break | 99.3 MPa | 14400 psi | ASTM D638 |
A. Schulman ComAlloy® E-12812 Easy Flow Glass Reinforced Nylon 66 Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength at Break | 99.0 MPa | 14400 psi | ISO 527 |
Azoty Tarnow™ TARNOFORM 500 GF6 POM 30% glass fiber reinforced, high flow injection molding grade, suitable for applications where high strength and stiffness is required, combined with higher flowability during molding.Information pr.. |
|||
Tensile Strength at Break | 99.0 MPa | 14400 psi | 0.2 in/min; ASTM Test |
BASF Ultramid® 8233G HS BK-102 33% Glass Filled PA6 (Conditioned) Ultramid 8233G HS BK-102 is a heat stabilized, weather resistant, 33% glass fiber reinforced PA6 injection molding compound offering excellent strength, stiffness, high temperature performance and d.. |
|||
Tensile Strength at Break | 99.0 MPa | 14400 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOTUF PF006I PA 6 LNP THERMOTUF* PF006I is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: High Impact. |