Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 15.9 MPa | 2310 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable W2402L Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
Tensile Strength at Break | 15.9 MPa | 2300 psi | 2 in/min; ASTM D638 |
RheTech Products FT4200-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural Applications: Body side moldingsGrillesElectrical housingsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 15.9 MPa | 2300 psi | 2 in/min; ASTM D638 |
RheTech Products FT4200-01 Thermoplastic Polyolefin, Non-UV Stabilized, Black Applications: Body side moldingsGrillesElectrical housingsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | 510 mm/minTensile and elongation values are largely determined by processing parameters of the end user.; ASTM D412 |
PolyOne Maxxam™ FR WC 0587-21 R2 RoHS Polypropylene, Unspecified (PP, Unspecified) Maxxam FR WC 0587-21 R2 RoHS is a flame retardant polyolefin compound characterized by low flame spread and good processability. Designed for thin wall primary wire applications.UL Yellow Card appro.. |
|||
Tensile Strength at Break | 15.9 MPa | 2300 psi | 2 in/min; ASTM D638 |
RheTech Products RCC233-01 33% Calcium Carbonate Reinforced Polypropylene Copolymer, Black, Recycled Content Applications: Fender linersSplash shieldsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 15.9 MPa | 2300 psi | |
NEU NeuSoft™ 596-50A Medical Ether TPU / SBC blend |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible B8000 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible XV 3450 Polyvinyl Chloride, Flexible (PVC, Flexible) NOTE: All ingredients used in the formulation of this compound are listed in the United States FDA Code of Federal Regulations, Title 21. The only restriction is that the plasticizer is For foods of.. |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible XV3772 Polyvinyl Chloride, Flexible (PVC, Flexible) All ingredients used in the formulation of this compound are listed in the United States FDA Code of Federal Regulations, Title 21. The only restriction is that the plasticizer is For foods of high .. |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ HC 2170 Polyvinyl Chloride, Flexible (PVC, Flexible) Geon HC 2170 is a 70 Shore A non-phthalate flexible vinyl compound made from FDA sanctioned ingredients. HC 2170 can be used for extrusion and injection molding healthcare applications.NOTE: All ing.. |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ HC 2170G Polyvinyl Chloride, Flexible (PVC, Flexible) Geon HC 2170G is a 70 Shore A non-phthalate, gamma-stable flexible vinyl compound made from FDA sanctioned ingredients. HC 2170G can be used for extrusion and injection molding healthcare applicatio.. |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible B4DC1 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible F80E Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible R252AE Polyvinyl Chloride + NBR (PVC+NBR) Information provided by PolyOne |
|||
Tensile Strength at Break | 15.9 MPa | 2300 psi | 50 mm/min; ASTM D638 |
LyondellBasell Alathon® M6080 High Density Polyethylene, Injection Molding Grade ALATHON M6080 is a narrow molecular weight distribution homopolymer that exhibits enhanced flow characteristics and good balance of stiffness and impact resistance. Typical applications include case.. |
|||
Tensile Strength at Break | 15.9 MPa | 2300 psi | ASTM D638 |
Teknor Apex APEX® 124 Polyvinyl Chloride, Flexible Notes: 80°C Jacket; RoHS Compliant Features: Good UV Resistance; Sunlight Resistant (720 hours) Uses: Flexible Cord Jacketing; Irrigation Cable Jacketing; Military Cable Jacketing; Wire and Cable.. |
|||
Tensile Strength at Break | 15.9 MPa | 2300 psi | ASTM D638 |
Teknor Apex APEX® 4167 Polyvinyl Chloride, Flexible Notes: 60°C Jacket; RoHS Compliant Features: High Gloss; Sunlight Resistant (720 hours)Uses: Flexible Cord Jacketing Forms: Pellets Wire Types: SJTW; STW; SJT; SRDT; ST; SVT Agency Ratings: UL QM.. |
|||
Tensile Strength at Break | 15.9 MPa | 2300 psi | ASTM D638 |
Teknor Apex APEX® 94-A0055A-80 Polyvinyl Chloride, Flexible Notes: 60°C General Purpose; RoHS Compliant Forms: PelletsInformation Provided by Teknor Apex |
|||
Tensile Strength at Break | 15.9 MPa | 2300 psi | ASTM D638 |
Teknor Apex Fireguard® 910L16-C13-NL Polyvinyl Chloride, Flexible Notes: RoHS Compliant Features: Flame Retardant; Low Smoke Emission Uses: Plenum Cable Jacketing Wire Types: CL2P; CL3P; CMP; FPLP; MPP; OFNP Agency Ratings: NEC Article 725; NEC Article 760; NEC Ar.. |
|||
Tensile Strength at Break | 15.9 MPa | 2300 psi | ASTM D412 |
Teknor Apex Telcar® TL-1155A Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets P.. |
|||
Tensile Strength at Break | 15.9 MPa | 2300 psi | ASTM D638 |
Westlake Plastics TPX® Polymethylpentene TPX is a lightweight, high temperature polyolefin with exceptional acoustical and electrical properties. TPX has low moisture absorption and excellent chemical resistance. It is often used for app.. |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | PVC (80)/CP80AS2(20) |
Lubrizol Estane® CP80AS2 Thermoplastic Polyurethane Type: Estane® CP80AS2 is a soft, polyester based thermoplastic polyurethane resin.Features: Outstanding compatibility with flexible PVC allowing easy dispersion without pre-compounding.Uses: Tube/H.. |
|||
Tensile Strength at Break | 15.9 MPa @Temperature 23.0 °C |
2310 psi @Temperature 73.4 °F |
ASTM D638, ISO 527-2 |
DuPont™ Surlyn® 9320 Zinc Ionomer Surlyn® 9320 is a zinc ionomer thermoplastic resin. It is available for use in conventional extrusion and injection equipment, to create various sheets or shapes. Surlyn® 9320 thermoplastic resin .. |
|||
Tensile Strength at Break | 15.9 MPa | 2300 psi | |
Abatron ROCKWELD 55-27 A/B Structural Adhesive Putty; Epoxy ROCKWELD 55-27 is a 2-component epoxy system with low density, high-strength, and no shrinkage. It is a structural adhesive putty for sculpturing, repairs and restoration of stone, concrete and maso.. |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | Press Cure 10 Minutes @ 188°C, Post Cure 16 Hours @ 250°C |
3M Dyneon™ 131TZ High Temperature Perfluoroelastomer 3M™ Dyneon™ 131TZ is a technically advanced high temperature perfluoroelastomer (HT PFE). It is designed to meet the challenges of higher temperature applications. It is classified as FFKM per AST.. |
|||
Tensile Strength at Break | 15.9 MPa | 2300 psi | Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C |
3M Dyneon™ FE 5623 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FE 5623 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul.. |
|||
Tensile Strength at Break | 15.9 MPa | 2300 psi | ASTM D638 |
ExxonMobil Escorene™ LD 705.MJ Blown Ethylene Vinyl Acetate Copolymer Product Description: Escorene Ultra LD 705.MJ is a fractional melt index, 12.8 wt% vinyl acetate copolymer specialty film resin for applications requiring outstanding heat sealability, strength, and.. |