Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 165 MPa | 23900 psi | ISO.527 DIN.53455 |
Omnia Plastica PPS GF40 Polyphenylenesulphide Crystalline polymer based on polyphenylene sulfide with the addition of 40% glass-fibre. Very high rigidity, stiffness and flexural strength. The temperature resistance is very high: up to 240° C. .. |
|||
Tensile Strength at Break | <= 165 MPa | <= 23900 psi | ISO/R527 |
Polykemi AB SCANAMID 66 A12^ F35 NH9 Nylon 66, Glass Fiber Reinforced, Flame Retardant, Halogen Free Information provided by Polykemi AB |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | ISO 527-2 |
Pasargad Polymer Peyvand Pasamid 3P-H1135B Nylon 6, 35% Glass Fiber Reinforced Form: PelletsProcessing Method: Injection MoldingUses: Automotive Application Furniture Appliance Components Electrical PartsFastenerHousingInformation provided by Pasargad Polymer Peyvand Co |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | ISO 527-2 |
Pasargad Polymer Peyvand Pasamid 3P-H2130B1 Nylon 66, 30% Glass Fiber Reinforced Form: PelletsProcessing Method: Injection MoldingUses: Automotive Application Furniture Appliance Components Electrical PartsFastenerHousingInformation provided by Pasargad Polymer Peyvand Co |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | ISO 527-1/-2 |
DSM Akulon® K-FHG12 (Cond.) 60% Glass Reinforced Nylon 6 (North America)
(discontinued **) Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis.. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | ISO 527-1/-2 |
DSM Akulon® Ultraflow™ K-FG12 Nylon 6-60% Glass Reinforced (European Grade) (Cond)
(discontinued **) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | |
LATI Latilub 66-01M G/30 PA66, 30% Glass Fiber Reinforced, Molybdenum disulphide Filled Self-lubricating product based on Polyamide 66 (PA66). Molybdenum disulphide. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided.. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | |
LATI Latilub 66-10T G/30-V0KB1 PA66, 10% Glass Fiber Reinforced, PTFE Filled, Flame Retardant Self-lubricating product based on Polyamide 66 (PA66). PTFE. Glass fibers. UL94 V-0 classified, with red phosphorous. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North A.. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM 2300F PEI 30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming. US FDA Food Contact compliant in recognized colors. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM 2310 PEI (Europe-Africa-Middle East) 30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). Resin is RoHS compliant. UL94 V0 and 5VA listing. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM CRS5301 PEI (Asia Pacific) 30% Glass fiber filled, standard flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO conforming, UL94 V0 and 5VA listing. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM HU2310 PEI (Europe-Africa-Middle East) 30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). RoHS compliant. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP.. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP DC004E PC (Europe-Africa-Middle East) LNP* Thermocomp* DC004E is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Easy Molding. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | ISO 527-93 |
Wellman Wellamid® GF1398-BK1 Nylon 66, 30% Glass Fiber Reinforced All information provided by Wellman Engineered Resins. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® BG-25 S PA6-GF25 Product description: Grilon BG-25 S is a heat stabilized PA6 injection molding grade with 25 % glass fibers. Grilon BG-25 S has the following important properties: Excellent surface finishEasy flowi.. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | 5 mm/min; ISO 527 |
CP-Polymer-Technik Wellamid® 6000 GV 30 HW 30% Glass Fiber Nylon 6, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® XE 4105 nat PA610-GF50 Product description: Grilamid XE 4105 natural is a 50% glass fiber reinforced, heat stabilized polyamide 610 (PA610) injection molding grade. This product is to a large extent based on renewable raw.. |
|||
Tensile Strength at Break | 165 MPa | 23900 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP RF0069XZ PA 66 (Asia Pacific) LNP* THERMOCOMP* RF0069XZ is a compound based on Nylon 66 resin containing Flame Retardant, Glass Fiber. Added features of this material include: Flame Retardant. |