Polymer Property : Tensile Strength at Break = 176 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	176 MPa	25500 psi	ASTM D638
LNP Thermocomp® LF-1006 Polyetheretherketone, Glass Fiber Reinforcement (discontinued **) Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names..
Tensile Strength at Break	176 MPa	25500 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP LF006 PEEK LNP THERMOCOMP* LF006 is a compound based on Polyetheretherketone resin containing 30% Glass Fiber.
Tensile Strength at Break	176 MPa	25500 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP QF007 PA 6/10 LNP* THERMOCOMP* QF007 is a compound based on Nylon 6/10 resin containing 35% Glass Fiber.
Tensile Strength at Break	176 MPa	25500 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP QF007 PA 6/10 (Asia Pacific) LNP* Thermocomp* QF007 is a compound based on Nylon 6/10 resin containing Glass Fiber.
Tensile Strength at Break	176 MPa	25500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON REF42I PA 66 LNP* STAT-KON* REF42I is a compound based on Nylon 6/6 containing Proprietary Fillers. Added feature of this grade is: Electrically Conductive.
Tensile Strength at Break	176 MPa	25500 psi	ASTM D638
Chase Plastics CP Pryme® N130GL (DAM) Nylon 6, 30% Glass Fiber Reinforced, Internally Lubricated Information provided by Chase Plastics.
Tensile Strength at Break	176 MPa	25500 psi	ASTM D638
Chase Plastics CP Pryme® N130L Nylon 6, 30% Glass Fiber Reinforced, Lubricated Features: LubricatedForm: PelletsInformation provided by Chase Plastics.