Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 13.8 MPa | 2000 psi | Mixed 1:2; TM R050-36 |
Resinlab® EP1215 Clear Unfilled Epoxy Structural Adhesive Resinlab™ EP1215 Clear is a two part unfilled epoxy structural adhesive designed for bonding applications requiring high strength and good impact resistance. It cures completely at room temperature.. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | 510 mm/min; ASTM D412A |
PolyOne Synprene™ RT-5190 RoHS Black Styrene Butadiene Block Copolymer (SBC) Synprene™ thermoplastic elastomers (TPEs) are compounds based on styrenic block copolymer (SBC) technology, and can be formulated to deliver extremely low hardness values not found in other elastom.. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible A7501 Polyvinyl Chloride, Flexible (PVC, Flexible) Recommended for interior applications.Information provided by PolyOne |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM D638 |
ExxonMobil LD 641.LN Molding, Extrusion and Compounding Resin
(discontinued **) LD 641.LN is a low density homopolymer specifically designed for high performance blow molding applications. This resin is suitable for applications requiring high melt strength, flexibility, good .. |
|||
Tensile Strength at Break | >= 13.8 MPa | >= 2000 psi | Cured |
Resin Technology Group UV MX-2240 Multi-Functional Hybrid, UV-Curing, Micro-Electronic System Mix ratio 2 to 1 by volume.UV-MX 2240 is a low-viscosity, water-white photo/ chemical cross-linking encapsulant/sealant designed for micro-electronic applications. This two-part, Hybrid UV-epoxy bas.. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM D638 |
Manifattura Cattaneo RULON® 641 Polytetrafluoroethylene Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM D638 |
Manifattura Cattaneo RULON® J Polytetrafluoroethylene Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a. |
|||
Tensile Strength at Break | 13.8 - 17.2 MPa | 2000 - 2500 psi | |
ITW Plexus Plexusâ„¢ MA320 Methacrylate Adhesive Two-part adhesive designed for structural bonding of thermoplastic, metal, and composite assemblies.Excellent low temperature and toughness properties.Information provided by Illinois Tool Works. |
|||
Tensile Strength at Break | >= 13.8 MPa | >= 2000 psi | ASTM D412 Method A |
Seals Eastern 7148 Fluorocarbon-Elastomer FKM specially for oil & gas service; ED resistantInformation provided by Seals Eastern, Inc. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ISO R 527 |
Stir SpA SR 75 REF (PVC) Application: Extrusion pipe and sheath CEI 20-11 type TM-2Information provided by STIR SpA |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM D638 |
Teknor Apex APEX® 3315-NT Polyvinyl Chloride, Flexible Notes: RoHS Compliant Uses: Wire and Cable Applications Forms: PelletsInformation Provided by Teknor Apex |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM D412 |
Teknor Apex MF 150 NT Polyvinyl Chloride, Flexible Film Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMUses-Film, Medical Applications Forms-PelletsAppearance-ClearInformation provided by Teknor Apex Company |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM D412 |
Teknor Apex Telcar® TL-2370 Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets .. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM D638 |
A. Schulman POLYTROPE™ TPP 504E Extrusion Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 504 is an extrusion grade olefinic thermoplastic elastomer suitable for profile extrusion or blow molding. Characteristics of this product include excellent low temperature.. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM D638 |
ExxonMobil Escorene™ LD 730.09 Molding Ethylene Vinyl Acetate Copolymer Product Description: Escorene Ultra LD 730.09 is a high vinyl acetate copolymer with a low melting temperature and excellent strength properties and toughness.Availability: Latin America, North Amer.. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM D638 |
ExxonMobil LDPE LD 150BW Wire & Cable Low Density Polyethylene Resin Product Description: LD 150BW is a LDPE containing suitable for the production of LV and MV crosslinked insulation using the 1-step or 2-step silane technology. Through in-house compounding it can a.. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
Dow DNDA-7340 NT 7 Linear Low Density Polyethylene Resin DOW DNDA-7340 NT 7 LLDPE resin is well-suited for use in blow molding applications such as small, squeezable bottles, as well as, extruded flexible hoses and tubing. DOW DMDA-7340 NT 7 resin is als.. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C |
3M Dyneon™ FE 5520 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FE 5520 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul.. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C |
3M Dyneon™ FT 2320 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FT 2320 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul.. |
|||
Tensile Strength at Break | 13.8 - 20.7 MPa | 2000 - 3000 psi | |
Abatron AboCast 7802-1/AboCure 50-3 (80 pbw) Epoxy AboCast 7802-1 is a clear resin with low viscosity (600-800 cps.) and a weight of 9.1 lbs/gallon. AboCure 50-3 is a clear, slow converter for lower rigidity. It has an HDT of 60°C, variable ratio, .. |
|||
Tensile Strength at Break | 13.8 - 27.6 MPa | 2000 - 4000 psi | |
Abatron AboCast 7802-1/AboCure 7804-3 (80 pbw) Epoxy AboCast 7802-1 is a clear resin with low viscosity (600-800 cps.) and a weight of 9.1 lbs/gallon. AboCure 7804-3 a clear, slightly accelerated converter for lower rigidity. It has an HDT of 60°C, v.. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM-D882 |
Caplinq LINQSTAT™ VCF-40012T/2 Product Description: LINQSTAT™ VCF-Series is a black, carbon-filled, volume-conductive polyethylene film designed to provide both physical and static protection in numerous semiconductor, electroni.. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM-D882 |
Caplinq LINQSTAT™ VCF-41014B Product Description: LINQSTAT™ VCF-Series is a black, carbon-filled, volume-conductive polyethylene film designed to provide both physical and static protection in numerous semiconductor, electroni.. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM-D882 |
Caplinq LINQSTAT™ VCF-43036B Product Description: LINQSTAT™ VCF-Series is a black, carbon-filled, volume-conductive polyethylene film designed to provide both physical and static protection in numerous semiconductor, electroni.. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM-D882 |
Caplinq LINQSTAT™ VCF-80036S/2 Product Description: LINQSTAT™ VCF-Series is a black, carbon-filled, volume-conductive polyethylene film designed to provide both physical and static protection in numerous semiconductor, electroni.. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | ASTM D882 |
3M 4F94 Fire Retardant Carpet Protective Tape 3M™ Fire Retardant Carpet Protective Tape 4F94 is a flame retardant, thicker polyethylene tape with a very high-tack adhesive system used for temporary protection of carpets during construction or .. |
|||
Tensile Strength at Break | 13.8 MPa | 2000 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible R242AE Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |