Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 25.5 MPa | 3700 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable EAC31L Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | 2 in/min; ASTM D638 |
RheTech Products HP517-00 23% Talc Reinforced High Performance Polypropylene Copolymer, Non-UV Stabilized, Natural Applications: Interior trim moldingsSill platesTire coverInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | 2 in/min; ASTM D638 |
RheTech Products P258-01 Polypropylene Copolymer, UV Stabilized, Black Applications: Door/trunk scuffExterior grills and cowlsSteering column shroudsInterior trimInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | 2 in/min; ASTM D638 |
RheTech Products P261-01 Polypropylene Copolymer, Medium Impact, Black Applications: Radiator grille inlet supportElectrical housingsUnderhood componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | 2 in/min; ASTM D638 |
RheTech Products UVP254-01 Polypropylene Copolymer, UV Stabilized, Black Applications: Fuel filler pocketInterior trimI/P componentsCenter consoleInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | chs 2 in/min; ASTM D638 |
Network Polymers MS 175 Styrene Methyl Methacrylate Terpolymer Description: Styrene Methyl Methacrylate TerpolymerInformation provided by Network Polymers Inc. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | ASTM D638 |
Niche Polymer PPCT40BK Copolymer PP, 40% Talc Filled Information provided by Niche Polymer |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | 2 in/min; ASTM D638 |
RheTech Products HP512-01 High Stiffness Polypropylene Copolymer, UV Stabilized, Black Applications: Automotive interior applicationsSeat back trimCenter consolesInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 25.5 MPa @Thickness 2.00 mm |
3700 psi @Thickness 0.0787 in |
50mm/min; ASTM D638 |
LG Chemical KEYFLEX BT 1040D Ester Type TPE Description: Injection Molding, TPC-ET, General Purpose, Medium ModulusApplication: Antenna Cover, Injection Parts for Leisure & SportsCAS: 37282-12-5Information provided by LG Chemical |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | ASTM D412 |
Huntsman IROGRAN® A 60 E 4612 N TPU-Polyester Performance Features: Manufactures of technical parts can achieve the highest levels of: Wear and tear strengthDimensional stabilityOil resistanceLow compression setDynamic load performanceElasticit.. |
|||
Tensile Strength at Break | >= 25.5 MPa | >= 3700 psi | |
Sibur Nitrilast-40 Nitrile-Butadiene Rubber (NBR) N 3883. For production of oil-benzene resistant articles for the automobile, aviation and rubber technical industries. Rubbers on the base of Nitrilast possess good oil-benzene resistance. Rubber.. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® SD-0170 F ABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | ISO R 527 |
Stir SpA L 70 BZ (PVC) Application: Pipes and semi-rigid profilesInformation provided by STIR SpA |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | 50 mm/min; ASTM D638 |
Supreme Petrochem SP 555 Flame Retardant Polystyrene Characteristics Very good flow properties Good balance of toughness and rigidity Available in any dark colors Processing MoldingApplications Large size T.V. Cabinets VCR cabinets Electrical boxe.. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | ASTM D638 |
Teknor Apex Synres® SR 4000 Polypropylene Notes: The Specialty Compounding Division offers a proprietary line of mineral filled polyolefins, including talc and calcium carbonate filled polypropylenes. Typical applications include injection .. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | ASTM D638 |
Plastics Group Polifil® C-30 30% Calcium Carbonate-Reinforced Polypropylene Polifil® C series compounds are homopolymer polypropylene resins reinforced with fine particle size calcium carbonate. They combine high impact with stiffness, heat aging, good colorability, resist.. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | ASTM D638 |
Plastics Group Polifil® RMC-20 20% Calcium Carbonate-Reinforced Polypropylene, High Impact Polifil® RMC series compounds are high impact polypropylenes reinforced with fine particle size calcium carbonate. In addition to the highest impact possible, they possess good stiffness, heat agin.. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
Dow UNIVAL™ DMDD-6200 NT 7 High Density Polyethylene Resin (HDPE) Moderate swell Complies with U.S. FDA 21 CFR 177.1520 (c) 3.2a UNIVAL™ DMDD-6200 NT 7 is a multipurpose polymer designed for the high speed production of blow molded containers used to package hous.. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | ASTM D638 |
Amco Amalloy® B9336 Polymer Alloy Amco Amalloy B9336 is a clear performance copolymer with exceptional clarity and toughness.Stiff, with good tensile and flexural strength.Information provided by Amco Plastic Materials. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | ASTM D638 |
Americas Styrenics STYRON® 478 High Impact Polystyrene Product CharacteristicsGood glossExcellent balance of flow and stiffnessFood Contact CompliantUL Classification 94HBUSP Class VITypical ApplicationsAppliancesMedicalHousewaresConsumer electronicsIn.. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | ASTM D638 |
Americas Styrenics STYRON® 484 High Impact Polystyrene Product CharacteristicsToughnessHeat resistanceGood stiffnessFood Contact CompliantUL Classification 94HBTypical ApplicationsLidsAppliances/RefrigerationPackaging/disposablesHousewaresInformation pr.. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | cured, grit-blasted steel; ASTM D2095 |
3M Scotch-Weld™ MG100 SF Medical Grade Instant Adhesive 3M™ Scotch-Weld™ Medical Grade Instant Adhesive are intended for use on a wide variety of materials used in the construction of disposable medical assemblies. They will quickly bond metals, plasti.. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | cured, grit-blasted steel; ASTM D2095 |
3M Scotch-Weld™ SF100 Super Fast Instant Adhesive 3M™ Scotch-Weld™ Super Fast Instant Adhesives rely less on surface moisture for cure speed than standard cyanoacrylates. They are designed to join together difficult-to-bond plastics and rubbers, .. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | ISO 527-1/-2 |
DSM Arnitel® PB581-H Polyether Ester Elastomer (European Grade)
(discontinued **) Product description: Arnitel® combines the advantages of engineering thermoplastics, being easy to process with excellent mechanical properties, at the same time with the flexibility of rubbers.Arn.. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | ASTM D638 |
Amco Amalloy® B9941 Polymer Alloy Amco Amalloy B9941 is a clear performance copolymer with exceptional clarity and toughness.Good flexural and tensile strength.Information provided by Amco Plastic Materials. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | ASTM D638 |
Chase Plastics CP Pryme® PPC100NB-10M Polypropylene Copolymer Information provided by Chase Plastics. |