Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 2.00 - 4.00 MPa | 290 - 580 psi | ASTM D412 |
Proto3000 Objet Digital Materials™ DM_9110/9410/9210/9310 Rubber-like Prototyping Polymer Primary material: TangoBlackSecondary material: VeroWhitePlus, VeroBlue, VeroBlack, FullCure720Digital Materials are made up of two Objet materials. The two materials are combined in specific concen.. |
|||
Tensile Strength at Break | 2.00 - 4.00 MPa | 290 - 580 psi | ASTM D412 |
Proto3000 Objet Digital Materials™ DM_9860/9760 Rubber-like Prototyping Polymer Primary material: TangoBlackPlus/TangoPlusSecondary material: VeroWhitePlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structu.. |
|||
Tensile Strength at Break | 2.00 - 4.00 MPa | 290 - 580 psi | ASTM D412 |
Proto3000 Objet Digital Materials™ DM_9870/9770 Rubber-like Prototyping Polymer Primary material: TangoBlackPlus/TangoPlusSecondary material: VeroWhitePlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structu.. |
|||
Tensile Strength at Break | 2.00 MPa | 290 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP 9H0300C LNP* Thermocomp* 9H0300C is a High Specific Gravity compound containing proprietary fillers. |
|||
Tensile Strength at Break | 2.00 MPa | 290 psi | After Curing |
Silikony Polskie Polastosil M-56 Silicone Rubber Rubber with strong hardness |
|||
Tensile Strength at Break | 2.00 MPa | 290 psi | After Curing |
Silikony Polskie Polastosil M-99 Silicone Rubber Rubber with strong hardness |
|||
Tensile Strength at Break | 2.00 MPa | 290 psi | ASTM D638 |
Unitika elitel UE3400 Polyester, Flake Elastomer, Rubber elasticity, Wide compatibility, Low temperature flexibilityUNITIKA l resins are thermoplastic saturated copolymeric polyester resins. l resins are expanding their applications fro.. |
|||
Tensile Strength at Break | 2.00 MPa | 290 psi | ASTM D638 |
ELASTO UK Dryflex® 400501S SBS Based Material, 50A Hardness, Natural The 400S-series is a good alternative for indoor applications and disposable articles that do not have high requirements for ageing and heat resistance. The raw materials are specially selected for.. |
|||
Tensile Strength at Break | 2.00 MPa | 290 psi | ASTM D638 |
ELASTO UK Dryflex® 402501S SBS Based Material, 50A Hardness, Black The 400S-series is a good alternative for indoor applications and disposable articles that do not have high requirements for ageing and heat resistance. The raw materials are specially selected for.. |
|||
Tensile Strength at Break | 2.00 MPa | 290 psi | ISO 37 |
ELASTO UK Dryflex® 5029-104 TPE, Modified Injection Molding Grade for Door Stops The VTC TPE Group have developed endless formulations to fulfill different properties and application requirements to optimize the finished component. VTC Dryflex® 5029-104 is specifically designe.. |
|||
Tensile Strength at Break | 2.00 MPa | 290 psi | ASTM D638 |
ExxonMobil Escorene® AD2528 Adhesive Application Resin Escorene Ultra AD 2528 is a very high flow rate, 27.6% Vinyl Acetate, copolymer, which is useful in formulating hot melt adhesives.Availability: Latin America, North America and South America Additi.. |
|||
Tensile Strength at Break | 2.00 MPa | 290 psi | ASTM D638 |
Arkema Group LOTRYL® 35 BA 40 Copolymer Ethylene - Butyl Acrylate LOTRYL® 35 BA 40 is a random copolymer of ethylene and butyl acrylate, prepared by the high pressure polymerization process. Co-monomer content is 35% in weight. LOTRYL® 35 BA 40 is particularly r.. |
|||
Tensile Strength at Break | 2.00 MPa | 290 psi | ASTM D638 |
Arkema Group LOTRYL® 37 EH 175 Copolymer Ethylene - 2-Ethylhexyl Acrylate LOTRYL® 37EH175 is a random copolymer of Ethylene and 2-Ethylhexyl Acrylate, prepared by the high pressure polymerization process. LOTRYL® 37EH175 is particularly recommended for the formulation o.. |
|||
Tensile Strength at Break | 2.00 MPa | 290 psi | ASTM D882 |
3M 2A29 (Clear) Co-Extruded Multi-Polymer Protect Tapes 3M™ Co-Extruded Multi-Polymer Protective Tapes have a medium-tack adhesive system to help provide temporary protection for a variety of surface protection applications.Information provided by 3M |
|||
Tensile Strength at Break | 2.00 MPa | 290 psi | ASTM D638 |
Arkema Group EVATANE® 33-400 Copolymer Ethylene - Vinyl Acetate EVATANE® 33-400 is a random copolymer of Ethylene and Vinyl Acetate made by high-pressure radicalar polymerisation process. EVATANE® 33-400 is stabilized with antioxidants. The High Vinyl Acetate .. |
|||
Tensile Strength at Break | 2.00 MPa | 290 psi | ASTM D882 |
3M 2A26 Co-Extruded Multi-Polymer Protect Tapes 3M™ Co-Extruded Multi-Polymer Protective Tapes have a medium-tack adhesive system to help provide temporary protection for a variety of surface protection applications.Information provided by 3M |
|||
Tensile Strength at Break | 2.00 MPa | 290 psi | ASTM D882 |
3M 2A25 Co-Extruded Multi-Polymer Protect Tapes 3M™ Co-Extruded Multi-Polymer Protective Tapes have a medium-tack adhesive system to help provide temporary protection for a variety of surface protection applications.Information provided by 3M |
|||
Tensile Strength at Break | 2.00 MPa | 290 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Stat-kon PX98038 PA 6 (Europe-Africa-Middle East) LNP* STATKON* PX98038 is a compound based on PA6 resin containing Carbon Fiber, Glass Fiber, Flame Retardant. Added features include : Flame Retardant, Electrically Conductive, Heat Stabilized.This .. |