Polymer Property : Tensile Strength at Break = 30.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	20.0 - 30.0 MPa	2900 - 4350 psi	ASTM D638-03
Proto3000 Objet DurusWhite FullCure430 Polypropylene-like Prototyping Polymer Objet’s FullCure® Materials family of proprietary acrylic-based photopolymer materials enables Objet users to create highly accurate, finely detailed 3D models and parts for a wide range of Rapid ..
Tensile Strength at Break	28.0 - 30.0 MPa	4060 - 4350 psi	ASTM D683
Loxim 830 02T HB Polypropylene Compound, 30% Talc Filled, Flame Retardant Information provided by Loxim Industries
Tensile Strength at Break	14.0 - 30.0 MPa @Thickness 2.00 mm	2030 - 4350 psi @Thickness 0.0787 in	50 mm/min; ASTM D638
Solvay Specialty Polymers SolefÂ® 31508 Polyvinylidene Fluoride (PVDF) SolefÂ® 31508 PVDF copolymer is a low viscosity and very flexible grade for Wire & Cable applications.Features: Copolymer; Good Flexibility; Low ViscosityUses: Wire & Cable ApplicationsAdditional ..
Tensile Strength at Break	14.0 - 30.0 MPa @Thickness 2.00 mm	2030 - 4350 psi @Thickness 0.0787 in	50 mm/min; ASTM D638
Solvay Specialty Polymers SolefÂ® 32008 Polyvinylidene Fluoride (PVDF) SolefÂ® 32008 PVDF copolymer is a low viscosity and very flexible grade for Wire & Cable applications.Features: Copolymer; Good Flexibility; Low ViscosityUses: Wire & Cable ApplicationsAdditional ..
Tensile Strength at Break	20.0 - 30.0 MPa	2900 - 4350 psi	ZCI-T-008
Zeon Chemicals Zetpol® 2020 Hydrogenated Nitrile Elastomomer Zetpol 2020 is a highly saturated copolymer of butadiene and acrylonitrile with high tensile strength, good heat resistance, good chemical resistance to aggressive fluids, and an excellent balance o..
Tensile Strength at Break	20.0 - 30.0 MPa	2900 - 4350 psi	ZCI-T-008
Zeon Chemicals Zetpol® 2020L Hydrogenated Nitrile Elastomomer Zetpol 2020L is a highly saturated copolymer of butadiene and acrylonitrile with high tensile strength, good heat resistance, good chemical resistance to aggressive fluids, and an excellent balance ..
Tensile Strength at Break	15.0 - 30.0 MPa	2180 - 4350 psi	TM-019G
AorTech Biomaterials Elast-Eon™ E5-325 Biomedical Polyurethane Pellets Elast-Eon™ 5-325 is a polyurethane with a 32.5% hard segment content and a mixed polyether/siloxane soft segment. It comes in pellet form. The pellets are colorless to yellowish and are soluble in ..
Tensile Strength at Break	15.0 - 30.0 MPa	2180 - 4350 psi	TM-019G
AorTech Biomaterials Elast-Eon™ E5-325 Biomedical Polyurethane Pellets Elast-Eon™ 5-325 is a polyurethane with a 32.5% hard segment content and a mixed polyether/siloxane soft segment. It comes in pellet form. The pellets are colorless to yellowish and are soluble in ..
Tensile Strength at Break	14.0 - 30.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C	2030 - 4350 psi @Thickness 0.0787 in, Temperature 73.4 °F	Type IV, 50 mm/min; ASTM D638
Solvay Specialty Polymers Solef® 31508 Polyvinylidene Fluoride (PVDF) (Unverified Data**) Solef® 31508 PVDF copolymer is a low viscosity and very flexible grade for Wire & Cable applications.Information provided by Solvay Specialty Polymers.