Polymer Property : Tensile Strength at Break = 3000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	20.7 MPa	3000 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Wire & Cable JAC31A Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne
Tensile Strength at Break	20.7 MPa	3000 psi	2 in/min; ASTM D638
RheTech Products FT5100-04 Thermoplastic Polyolefin, UV Stabilized, White Applications: IP structural componentBody side moldingInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	20.7 MPa	3000 psi	2 in/min; ASTM D638
RheTech Products HP521-00 15% Talc Reinforced High Performance Polypropylene Copolymer, Non-UV Stabilized, Natural Applications: Interior trimIP structural componentsCenter consolesInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	20.7 MPa	3000 psi	2 in/min; ASTM D638
RheTech Products HP521-372 15% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, 110D Medium Dark Pewter Applications: Interior trimIP structural componentsCenter consolesInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	20.7 MPa	3000 psi	2 in/min; ASTM D638
RheTech Products P257-01 Polypropylene Copolymer, Black Applications: Splash shield and fender linersElectrical enclosuresUnderhood componentsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	>= 20.7 MPa	>= 3000 psi	ASTM D638
Niche Polymer PPCM10BK Copolymer PP Information provided by Niche Polymer
Tensile Strength at Break	20.7 MPa	3000 psi	2 in/min; ASTM D638
RheTech Products HP521-288UV 15% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, 167A Ebony Applications: Interior trimIP structural componentsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	20.7 MPa	3000 psi	ASTM D4894
3M Dyneon™ TF 4103 PTFE 15% Glass Fiber Filled (discontinued **) Type II PTFE. Applications include valve seats, bearings, seals/gaskets, moldings, piston rings.Data provided by Dyneon.
Tensile Strength at Break	20.7 - 24.1 MPa	3000 - 3500 psi
ITW Plexus Plexusâ„¢ MA300 Methacrylate Adhesive Two-part adhesive designed for structural bonding of thermoplastic, metal, and composite assemblies.All purpose adhesive high strength.Information provided by Illinois Tool Works.
Tensile Strength at Break	20.7 MPa	3000 psi	AVG; ASTM D412 Method A
Seals Eastern 7182D Fluorocarbon-Elastomer Formulated AFLASÂ® high-temperature "sour" oil & gas service. Excellent acid and base resistance.Information provided by Seals Eastern, Inc.
Tensile Strength at Break	20.7 MPa	3000 psi	ASTM D638
Teknor Apex APEXÂ® 3611-85 Polyvinyl Chloride, Flexible Uses: Medical/Healthcare Applications Agency Ratings: NSF 61 Forms: Pellets Additional Information: Second Generation SeriesInformation Provided by Teknor Apex
Tensile Strength at Break	20.7 MPa	3000 psi	ASTM D638
Teknor Apex APEXÂ® 7500-105 Polyvinyl Chloride, Flexible Notes: 105Â°C General Purpose; RoHS Compliant Features: High Heat Resistance Uses: Connectors; Grommets; Plugs; Strain ReliefsForms: Pellets Processing Method: Injection Molding Agency Ratings: UL..
Tensile Strength at Break	20.7 MPa	3000 psi	ASTM D638
Teknor Apex APEXÂ® 7500-90 Polyvinyl Chloride, Flexible Notes: 105Â°C General Purpose; RoHS Compliant Features: High Heat Resistance Uses: Connectors; Grommets; Plugs; Strain ReliefsForms: Pellets Processing Method: Injection Molding Agency Ratings: UL..
Tensile Strength at Break	20.7 MPa	3000 psi	ASTM D638
A. Schulman POLYTROPE™ TPP 510 Injection Molding Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 510 is an injection molding grade olefinic thermoplastic elastomer. This product has excellent low temperature impact properties and flow characteristics suitable for moldi..
Tensile Strength at Break	20.7 MPa	3000 psi	ASTM D412
Teknor Apex Telcar® TL-1000-105UV Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets P..
Tensile Strength at Break	20.7 MPa	3000 psi	ASTM D638
A. Schulman POLYFORT™ FPP 4529 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 4528 is a mineral filled copolymer polypropylene for applications requiring good impact and increased stiffness with long term heat stability.Information provided by A. Sch..
Tensile Strength at Break	20.7 MPa	3000 psi	non-oriented film; ASTM D882
Total PPR Z9421 Polypropylene, Random Copolymer, Heat Sealable Film Grade Color/Clarity/Impact. TOTAL Petrochemicals Polypropylene Z9421 is a low melting, high ethylene random copolymer with improved color, optics and impact properties.Heat Sealable. The very low melting..
Tensile Strength at Break	20.7 MPa	3000 psi	at max load; ASTM D638
A. Schulman PP 1227E-01 Polypropylene High-Impact Polypropylene DescriptionPolypropylene PP 1277E-01 is a low-flow, high-impact polypropylene for film, profile, tubing and coating.Information provided by A. Schulman.
Tensile Strength at Break	20.7 MPa	3000 psi	ASTM D638
A. Schulman POLYTROPE™ TPP 1010E-01 Olefinic Elastomer For Sheet Extrusion DescriptionPolytrope TPP 1010E-01 is an olefinic elastomer designed for sheet extrusion, profile extrusion and blow molding. TPP 1010E-01 is a natural product which can be colored and UV stabilized..
Tensile Strength at Break	20.7 MPa	3000 psi	Across Flow; ASTM D412
ExxonMobil Santoprene® 103-40 Thermoplastic Elastomer A hard, black, versatile thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance for use in a wide range ..
Tensile Strength at Break	20.7 MPa	3000 psi	ASTM D638
Americas Styrenics EC6600 High Impact Polystyrene Product CharacteristicsExcellent printabilityMatte surface finishHigh heat distortion temperatureGood low temperature toughnessFood Contact CompliantTypical ApplicationsLithographic sheetPrinted toy..
Tensile Strength at Break	20.7 MPa	3000 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Flexible R339AE Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne
Tensile Strength at Break	20.7 - 24.1 MPa	3000 - 3500 psi	TM R050-36
Resinlab® EP1305LV Clear Epoxy Casting Resin Resinlab™ EP1305LV Clear is a black two-part epoxy casting resin designed to give good adhesion to metals and especially PVC. It has good wetting to most surfaces and is free flowing to penetrate c..
Tensile Strength at Break	20.7 MPa	3000 psi	2 in/min; ASTM D638
RheTech Products HP522-357 15% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, JA6A Black Applications: Center consolesAir vents louversInterior trimInjection molding conditions reported in table.Information provided by RheTech Products.