Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	172 - 207 MPa	25000 - 30000 psi	Copper butt joint
Lucas-Milhaupt BRAZE 250 Silver Based Cadmium Free Filler Metal Characteristics:Braze 250 is an intermediate temperature silver brazing alloy with a long (325EF/180EC) melting range. It has a tendency to liquate (i.e. separate into low and high melting constitu..
Tensile Strength at Break	172 - 207 MPa	25000 - 30000 psi	Copper butt joint
Lucas-Milhaupt BRAZE 450 Silver Based Cadmium Free Filler Metal Characteristics:Braze 450 is an intermediate temperature cadmium free silver brazing filler metal with sufficient melting range (145EF) to properly braze joints with the range of fits encountered in..
Tensile Strength at Break	172 - 207 MPa	25000 - 30000 psi	Copper butt joint
Lucas-Milhaupt BRAZE 600 Silver Based Cadmium Free Filler Metal Characteristics: Braze 600 is a copper rich eutectiferous alloy, the eutectiferous portion of which is molten at 1300EF (705EC), about 25EF before the entire composition is completely fluid. Thus t..
Tensile Strength at Break	172 - 207 MPa	25000 - 30000 psi	Copper butt joint
Lucas-Milhaupt BRAZE 650 (Easy) Silver Based Cadmium Free Filler Metal Characteristics: This alloy is a intermediate silver brazing filler metals with a slight tendency to liquate (i.e. separate into low and high melting constituents) if heated slowly through their mel..
Tensile Strength at Break	172 - 207 MPa	25000 - 30000 psi	Brass butt joint
Lucas-Milhaupt BRAZE 700 (Medium) Silver Based Cadmium Free Filler Metal Characteristics: This alloy is a intermediate silver brazing filler metals with a slight tendency to liquate (i.e. separate into low and high melting constituents) if heated slowly through their mel..
Tensile Strength at Break	165 - 207 MPa	24000 - 30000 psi	Wire, Temper-Soft
Lucas-Milhaupt BRAZE 999 Commercial Grade Fine Silver Commercial grade fine silver (99.90% minimum silver) is widely used in numerous electrical, electronic, and industrial applications, such as contacts, fuse elements, lead wires, battery plated, and ..
Tensile Strength at Break	165 - 207 MPa	24000 - 30000 psi	Strip, Temper-Soft
Lucas-Milhaupt BRAZE 999 Commercial Grade Fine Silver Commercial grade fine silver (99.90% minimum silver) is widely used in numerous electrical, electronic, and industrial applications, such as contacts, fuse elements, lead wires, battery plated, and ..
Tensile Strength at Break	172 - 207 MPa	25000 - 30000 psi	Copper butt joint
Lucas-Milhaupt BRAZE 560 Characteristics:Braze 560 is a low temperature, free-flowing brazing filler metal with a slight tendency to liquate (i.e. separate into low and high melting constituents) if heated slowly through it..
Tensile Strength at Break	172 - 207 MPa	25000 - 30000 psi	Copper butt joint
Lucas-Milhaupt BRAZE 750 (Hard) Silver Based Cadmium Free Filler Metal Characteristics: This alloy is a intermediate silver brazing filler metals with a slight tendency to liquate (i.e. separate into low and high melting constituents) if heated slowly through their mel..