Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 37.0 MPa | 5370 psi | |
Plastcom SLOVALEN PH 49 GF 10 GB 20 PP, 20% glass beads, 10% glass fibre, coupling agent FeaturesModified homopolymer PP for injection moulding, chemically reinforced with 10 % glass fiber and 20% glass beads, contains themodifier of mechanical properties. Increased strength in comparis.. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Geloy FXTW26SK ASA Next generation Geloy XTW ASA for high heat exterior applications. Outstanding weatherability and toughness. Metallic sparkle VisualFx.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Geloy XTWM206 ASA Next generation ASA optimized for outstanding weatherability, colorability and higher heat applications requiring UV exposure resistance.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Geloy XTWM206 ASA (Europe-Africa-Middle East) Next generation ASA optimized for outstanding weatherability, colorability and higher heat applications requiring UV exposure resistance.This data was supplied by SABIC-IP for the Europe-Africa-Midd.. |
|||
Tensile Strength at Break | <= 37.0 MPa | <= 5370 psi | ISO/R527 |
Polykemi AB POLYshine PBT D241 PBT, Impact Modified Information provided by Polykemi AB |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® FXE4271L PC (Asia Pacific) Lexan* FXE4271L is a 10% glass filled, impact modified polycarbonate with excellent light-shield capability. It is designed for high flow, superior surface appearance, enhance release and good impac.. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ISO 527 |
SABIC Innovative Plastics LNP FARADEX AS002 ABS (Asia Pacific) LNP* Faradex* AS002 is a compound based on Acrylonitrile Butadiene Styrene resin containing Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Geloy FXTW26SK ASA (Asia Pacific) Next generation Geloy XTW ASA for high heat exterior applications. Outstanding weatherability and toughness. Metallic sparkle VisualFx.This data was supplied by SABIC-IP for the Asia Pacific region... |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ISO 527 |
Total Finathene® 53140 HDPE, blow molding, sheet
(discontinued **) Finathene® 53140 is a high density polyethylene produced by the slurry loop low pressure polymerization process FINATHENE® 53140 has been especially developed for the manufacturing of blow molded .. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ISO R 527 |
Fainplast Compounds RH 306/W Rigid PVC, Antishock Extrusion Antishock profiles |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ISO R 527 |
Fainplast Compounds RK 435 Rigid PVC, Extrusion Lead Free Electrical channels |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ISO R 527 |
Fainplast Compounds RKS 325/W-UV Rigid PVC, Antishock Extrusion Lead Free Various profiles, antishock UV resistant |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | 50mm/min; ASTM D638 |
Kingfa FW-650 Flame Retardant ABS Features:Weather resistanceSuper high impact resistanceApplications:Injection moldingSwitchSocketInformation Provided by Kingfa Sci. & Tech. Co., Ltd. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | 50 mm/min; ISO 527-1,-2 |
Ineos ABS Lustran® ABS 680 LNS503 High Performance Injection Molding Grade Lustran® ABS 680 LNS503 is an easy flow version. It is a high performance injection molding grade used for refrigerator and freezer door end caps. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | 50 mm/min; ISO 527-1,-2 |
Ineos ABS Lustran® Ultra 4105 ABS Pellets (Polycarbonate-modified), Medium High Heat Grade Lustran® Ultra 4105 is medium high heat grade with superior impact resistance. It is PC-modified and has low emission. It is used for the production of molded plastic articles. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP DZL24 PC (Asia Pacific) LNP* LUBRICOMP* DZL24 is a compound based on Polycarbonate resin containing PTFE, Milled Glass. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP KL005 Acetal Copolymer (Asia Pacific) LNP* LUBRICOMP* KL005 is a compound based on Acetal Copolymer resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP OL009 PPS - Linear (Asia Pacific) LNP* LUBRICOMP* OL009 is a compound based on PPS - Linear resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Xenoy® HX6600HP PBT+PC (Europe-Africa-Middle East) Xenoy HX6600HP is PBT based semi-crystalline blend with balanced flow and impact properties. Improved chemical resistance against lab disinfectants and chemicals for healthcare enclosure and housing.. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-LOY Cycoloy_CA6200 PC+ABS PRELIMINARY DATA. LNP* Stat-loy* Cycoloy_CA6200 compound is a Non-ECO flame retardant, anti-static PC+ABS for ESD management. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Stat-kon AD000Z ABS LNP* Stat-Kon AD000Z is a compound based on ABS resin with carbon powder. Grade characteristics: a statically conductive extrusion grade.This data was supplied by SABIC-IP for the Americas region... |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ISO 527 |
SABIC Innovative Plastics LNP Stat-loy W3000 PBT LNP STAT-LOY* W3000 is a compound based on Polybutylene Terephalate resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for the Americ.. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP DB0049F PC (Asia Pacific) LNP* Thermocomp* DB0049F is a compound based on Polycarbonate resin containing Glass Bead, Flame Retardant. Added features of this material include: Flame Retardant, Superior Molding. |
|||
Tensile Strength at Break | 37.0 MPa @Temperature 23.0 °C |
5370 psi @Temperature 73.4 °F |
ISO 527 |
DuPont Performance Polymers Crastin® CE2056 NC010 PBT Crastin® CE2056 NC010 is an unreinforced polybutylene terephthalate molding resin.Information provided by DuPont Performance Polymers |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | 50 mm/min; ISO 527 |
Chi Mei Polyrex® PG-33 Polystyrene Standard grade |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ASTM D1457 |
Asahi Glass Fluon® CD141 PTFE Coagulated Dispersion Powder Fluon®PTFE coagulated dispersion powders (fine powders) are used for paste extrusion to make tapes, tubes, rods and wire coatings.Information provided by Asahi Glass Company, Inc. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ASTM D1457 |
Asahi Glass Fluon® CD145 PTFE Coagulated Dispersion Powder Fluon®PTFE coagulated dispersion powders (fine powders) are used for paste extrusion to make tapes, tubes, rods and wire coatings.Information provided by Asahi Glass Company, Inc. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ISO 527 |
Total Finathene® SI 508 HDPE blow molding
(discontinued **) Finathene® SI 508 is part of a new generation of high density ethylene-hexene copolymers produced by the slurry loop low pressure polymerization process. Finathene® SI 508 is a high molecular weig.. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | 5 mm/min; ISO 527 |
Polimeri Europa Edistir N 1910 Polystyrene Very easy flow general purpose polystyrene. Used for injection of thin-wall, multi-cavity, very fast-cycle mouldings and for sheet extrusion in glossy capping of HIPS and in blend with HIPS or clear.. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HFD4471 PC (Asia Pacific) Lexan* HFD4471 is a 10% glass filled, medium flow, impact modified, injection moldable grade designed for high flow and superior surface appearance. HFD4417 has enhanced mold release, impact ductili.. |