Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | <= 32.0 MPa | <= 4640 psi | ISO/R527 |
Polykemi AB POLYfill PPH T4020 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Geloy XTWE270M ASA+SAN (Asia Pacific) Excellent weatherability, good flow/aesthetics and good impact.Profile co-extrusion grade over ABS, PVC or other compatible polymers. XTWE270M is available in various colours.This data was supplied.. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP AL003 ABS LNP LUBRICOMP* AL003 is a compound based on Acrylonitrile Butadiene Styrene resin containing 15% PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP AL003 ABS (Europe-Africa-Middle East) LNP LUBRICOMP* AL003 is a compound based on Acrylonitrile Butadiene Styrene resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP AL002 ABS LNP LUBRICOMP* AL002 is a compound based on Acrylonitrile Butadiene Styrene resin containing 10% PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP AL002 ABS (Europe-Africa-Middle East) LNP* LUBRICOMP* AL002 is a compound based on Acrylonitrile Butadiene Styrene resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Noryl RF1132 PPE+PP PPE+PP blend for high frequency applications. Good heat resistance and low DK.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | 50 mm/min, 1A; ISO 527 |
SABIC Innovative Plastics SABIC PPCOMPOUND 19T1020 PP SABIC® PPcompound 19T1020 is a general purpose, talc filled, heat stabilized homopolymer polypropylene compound. This compound exhibits high flow and is suitable for injection molding application.. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON FD000 PE LNP* STAT-KON* FD000 is an unfilled Polyethylene. Added feature of this grade is: Electrically Conductive. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON FX98501 PE LNP* STAT-KON* FX98501 is a compound based on Polyethylene resin containing Proprietary Fillers. Added feature of this material is: Electrically Conductive. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Xenoy® 6620U PBT+PC PBT+PC, Unfilled, Impact Modified, UV stabilized. Outstanding low temperature impact performance and chemical resistance. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-LOY K3000Z Acetal LNP* STAT-LOY* K3000Z is a compound based on unfilled Acetal resin. Added feature of this material is: Antistat. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | ISO 527-2 |
Tisan TISOPLEN® 10% Talc Filled Heat Stabilized Homopolymer Polypropylene TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow mois.. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | ISO 527 |
Total 3802 Blue MDPE pipe, injection molding FINATHENE® 3802 Blue is a polyethylene copolymer based on C6 hexene as co-monomer and is produced by a continuous low pressure slurry polymerization process. FINATHENE® 3802 Blue is a blue polyeth.. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D 638 |
Cossa Polimeri ESTABLEND CR Polycarbonate ABS Blend Polycarbonate and Acrylonitrile Butadiene Styrene blend for chromium plating, painting and metallizationGood impact resistance, good thermal resistanceInformation provided by Cossa Polimeri S.r.l. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | 50 mm/min; ISO 527 |
Chi Mei Polylac® PA-746 ABS - High Flow High flow, medium impact |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | 50mm/min; ASTM D638 |
Denka TE-30 Transparent Resin Polymer (MABS resin) ABS "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a.. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D882 |
3M 25X187 Protective UV Tape 3M™ Protective UV Tape 25X187 is a black and white co-extruded polyethylene tape featuring limited UV resistance.Information provided by 3M |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | Conditioned 15 days at 23°C - 50% RH; ASTM D638 |
Arkema Group Pebax® 2533 SA 01 MED Polyether Block Amide (PEBA) Polyether block amide PEBAX® 2533 SA 01 MED is a thermoplastic elastomer made of flexible polyether and rigid polyamide. This grade offers the highest quality and it is specially designed to meet t.. |
|||
Tensile Strength at Break | 32.0 - 34.0 MPa | 4640 - 4930 psi | ASTM D4745-97 |
Adamas Adalon® 509 PTFE, 3% MoS2 Information provided by Adamas, HPM |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | Conditioned; ISO R 527 |
Addiplast Addilene H 490 M20S Flame Retardant Polypropylene, 20% Mineral Filled Flame retardant, mineral filled, with halogensInformation provided by Addiplast. |
|||
Tensile Strength at Break | 32.0 - 34.0 MPa | 4640 - 4930 psi | ASTM D4745-97 |
Adamas Adalon® 508 PTFE, 1% MoS2 Information provided by Adamas, HPM |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
Asahi Glass Fluon® P-63P PFA Perfluoropolymer Fluon® PFA is a copolymer of tetrafluoroethylene (C2F4) and perfluoroalkoxyethylene, which has excellent chemical, electrical, mechanical and surface properties. PFA retains many inherent character.. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | |
AorTech Biomaterials ECSil™ 75A Biomedical Carbonate Silicone Pellets Elast-Eon™ Carbonate Silicone (ECSil™) is a family of next generation biomedical polymers. ECSil™ is finding strong interest in cardiac pacing leads, orthopaedics, spinal discs, and generally an.. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | DIN EN ISO 527-3 |
3M Dyneon™ TF 2053Z PTFE Fine Powder Dyneon™ TF 2053 Z PTFE is an ideal grade for extrusion of tubing and cables requiring only moderately high reduction ratio.Product Features:Processable by standard paste extrusion methods Good over.. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | |
Plastcom SLOVALEN PH 82 T 20 PP, 20% mineral filling FeaturesModified homopolymer PP for injection moulding with the content of 20% mineral filling. Increased rigidity, strength and thermal use up to 130°C depending on the talc conte nt. Decreased sh.. |
|||
Tensile Strength at Break | <= 32.0 MPa | <= 4640 psi | ISO/R527 |
Polykemi AB POLYfill PPH TS15010 H VTUV1 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | ISO R 527 |
Fainplast Compounds RE 224 Rigid PVC, Extrusion Various profiles |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM-D638 |
Braskem HB0454HR HDPE Blow Molding Polyethylene Copolymer HB0454HR is a high-density polyethylene copolymer resin with average molecular weight produced by the Unipol® process. A bottle made with HB0454HR shows excellent processability, color, and superfi.. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | ISO R 527 |
Fainplast Compounds RE 230/D Rigid PVC, Extrusion Electric channels |