Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | <= 42.0 MPa | <= 6090 psi | ISO/R527 |
Polykemi AB POLYabs XX0 ABS, Extrusion Grade Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 42.0 MPa | <= 6090 psi | ISO/R527 |
Polykemi AB POLYabs F00 GF15 ABS, Glass Fiber-Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 42.0 MPa | <= 6090 psi | ISO/R527 |
Polykemi AB POLYabs F00L ABS Information provided by Polykemi AB |
|||
Tensile Strength at Break | 42.0 MPa | 6090 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® FL900S PC (Europe-Africa-Middle East) Foamable Lexan* FL900S polycarbonate resin is an ideal choice for structural components where load bearing capability at elevated temperature is a key requirement. It exhibits outstanding inpact str.. |
|||
Tensile Strength at Break | 42.0 MPa | 6090 psi | ASTM D638 |
3M Dyneon™ PVDF 1010/0001 Polyvinylidene Fluoride
(discontinued **) Polyvinylidene Fluoride (PVDF) is ideal for multiple applications across a wide array of industries. Widely used in the chemical process industry, wire and cable industry, semiconductor industry, an.. |
|||
Tensile Strength at Break | 42.0 MPa | 6090 psi | ISO 37 |
Huntsman AVALON® 60 DE Thermoplastic Polyurethane Introduction: AVALON 60 DE is a high performance polyester based thermoplastic polyurethane for injection molding. AVALON 60 DE is part of the AVALON Perform Range and offers a premium soling materi.. |
|||
Tensile Strength at Break | 42.0 MPa | 6090 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP DL003P PC LNP LUBRICOMP* DL003P is a compound based on Polycarbonate resin containing 15% PTFE. Added features of this material include: Exceptional Processing, Internally Lubricated. |
|||
Tensile Strength at Break | 42.0 MPa | 6090 psi | ISO 527 Type 1A |
Solvay TECHNYL® C 536XT PA6, Conditioned Description: TECHNYL® C 536XT is an unreinforced polyamide 6, high viscosity, for extrusion blow molding. This product is available in natural color.Benefits: The product offers a good processing.. |
|||
Tensile Strength at Break | 42.0 MPa | 6090 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP WL003 PBT (Europe-Africa-Middle East) LNP* Lubricomp* WL003 is a compound based on Polybutylene Terephalate resin containing PTFE. |
|||
Tensile Strength at Break | 42.0 MPa | 6090 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP WL0049 PBT LNP* LUBRICOMP* WL0049 is a compound based on PBT containing 20% PTFE. Added features include: Wear Resistant, Flame Retardant. |
|||
Tensile Strength at Break | 42.0 MPa | 6090 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP ZP001XXP PPE+PS (Asia Pacific) LNP* Lubricomp* ZP001XXP is a compound based on PPE+PS Blend resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 42.0 MPa | 6090 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® 357 PBT+PC PC/PBT, Unreinforced, impact modified, UL94V-0 rated. Applications like bobbins, switches and enclosures. |
|||
Tensile Strength at Break | 42.0 MPa | 6090 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® ENH3500 PBT (Asia Pacific) Unfilled PBT, Non-Brominated & Non-Chlorinated Flame Retardant |
|||
Tensile Strength at Break | 42.0 MPa | 6090 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-LOY AF3009 ABS (Asia Pacific) LNP* Stat-loy* AF3009 is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber, Flame Retardant. Added features of this material include: Antistat, Flame Retardant. |
|||
Tensile Strength at Break | 42.0 MPa | 6090 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP NX07354 PC+ABS (Asia Pacific) This is a PC/ABS compound, a good candidate for Laser Direct Structuring applications. |
|||
Tensile Strength at Break | 42.0 MPa | 6090 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL PVX516 PPE PREVEX* PVX516 resin is a high flow, non FR grade, 110 C HDT |
|||
Tensile Strength at Break | 42.0 MPa | 6090 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL PVX516 PPE PREVEX* PVX516 resin is a high flow, non FR grade, 110 C HDT |
|||
Tensile Strength at Break | 42.0 MPa | 6090 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Xenoy® X3108UV PBT+PC (Asia Pacific) Unreinforced, UV-stabilized, flame retardant, impact modified PBT+PC with V0 at 0.8mm thickness. For interior and exterior applications like wall switches and electrical enclosures.This data was sup.. |
|||
Tensile Strength at Break | 42.0 MPa | 6090 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Xenoy® XL1562 PBT+PC (Europe-Africa-Middle East) XENOY XL1562 is an impact modified PBT+PC blend with outstanding chemical resistance, good UV stability and flow properties.This data was supplied by SABIC-IP for the Europe-Africa-Middle East regio.. |
|||
Tensile Strength at Break | 42.0 MPa | 6090 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP DB008ERP PC LNP* THERMOCOMP* DB008ERP is a compound based on Polycarbonate resin containing 40% Glass Bead. Added features of this material include: Easy Molding, Mold Release. |
|||
Tensile Strength at Break | 42.0 MPa | 6090 psi | ISO R 527 |
Stir SpA RH I P (PVC) Application: Spiral extrusion - various profilesInformation provided by STIR SpA |
|||
Tensile Strength at Break | 42.0 MPa | 6090 psi | 83% Ret. |
UBE UBESTA® 3030U Nylon 12 (After Formic Acid (10%) for 1000 hours) Description: UBESTA has a strong resistance to chemicals. Under normal conditions, it is not significantly affected by alkalis, alcohols, ethers, ketones, hydrocarbons, lubricating oils, gasoline, c.. |
|||
Tensile Strength at Break | 42.0 MPa | 6090 psi | ISO 527-2 |
Total PSC 1810/1811 Polystyrene 1811 is a very easy flowing crystal polystyrene designed, principally, for the injection molding industry. The excellent processing characteristics of this grade allows for the production of articl.. |
|||
Tensile Strength at Break | 42.0 MPa | 6090 psi | 50mm/min; ASTM D638 |
Denka TP-801 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a.. |
|||
Tensile Strength at Break | 42.0 MPa | 6090 psi | Conditioned 15 days at 23°C - 50% RH; ASTM D638 |
Arkema Group Pebax® MX 1205 SA 01 Polyether Block Amide (PEBA) Polyether block amide PEBAX® MX 1205 SA 01 is a thermoplastic elastomer made of flexible polyether and rigid polyamide. This SA grade is specially designed to food uses.Information provided by Arke.. |
|||
Tensile Strength at Break | 42.0 MPa | 6090 psi | ASTM-D638 |
Braskem GV0350 HDPE Blow Molding Polyethylene Copolymer HDPE GV0350 is a high-density polyethylene copolymer that has great molar mass, excellent chemical resistance, and high impact resistance and stiffness. It was developed for the blow-molding of larg.. |
|||
Tensile Strength at Break | 42.0 MPa | 6090 psi | ASTM D638 |
Braskem HB 0155 HDPE Blow Molding Polyethylene Applications: Large containers from 60 to 200 litersInformation provided by Braskem |
|||
Tensile Strength at Break | 42.0 MPa | 6090 psi | ASTM D638 |
Braskem Green PE SGM7746C Blow Molding and Monofilament High Density Polyethylene Lower greenhouse gas emissions100% made from renewable raw materialsPerformance and Competitiveness: Green Polyethylene has the same characteristics as petrochemical polyethyleneApplications: Mono.. |
|||
Tensile Strength at Break | 42.0 MPa | 6090 psi | ISO 527 |
Ascend Performance Materials Vydyne® 49 Nylon 66, Conditioned Vydyne® 49 is a general-purpose, impact-modified PA66 resin. Available in natural, it is recognized for all the processing and property advantages inherent to PA66 with the addition of improved imp.. |
|||
Tensile Strength at Break | 42.0 MPa | 6090 psi | Conditioned 15 days at 23°C - 50% RH; ASTM D638 |
Arkema Group Pebax® MX 1205 SP 01 Polyether Block Amide (PEBA) Polyether block amide PEBAX® MX 1205 SP 01 is a thermoplastic elastomer made of flexible polyether and rigid polyamide. This SP grade has been developed to be heat and UV resistant.Information prov.. |