Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 61.0 MPa | 8850 psi | ISO.527 DIN.53455 |
Omnia Plastica Akulon® PA 66 - Akulon 66 - at 50% RH Polyamide obtained by the polymerisation of Hexamethylenediamine and Adipic acid. It is one of the oldest engineering plastics, having been created in the USA in 1930. Due to its origin it is widely.. |
|||
Tensile Strength at Break | 61.0 MPa | 8850 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® BY2710X PC (Asia Pacific) BY2710X is a modified Polycarbonate (PC) resin. It is a non-filled, injection moldable grade with UL-94 V0 rating and is available in various opaque color options. |
|||
Tensile Strength at Break | 61.0 MPa | 8850 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® EXL1330 PC Copolymer (Asia Pacific) Lexan* EXL1330 polycarbonate (PC) siloxane copolymer resin is a UV stabilized opaque injection molding (IM) and sheet extrusion grade. This resin offers extreme low temperature (-60 C) ductility in .. |
|||
Tensile Strength at Break | 61.0 MPa | 8850 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® EXL1330 PC Copolymer (Europe-Africa-Middle East) Lexan* EXL1330 polycarbonate (PC) siloxane copolymer resin is a UV stabilized opaque injection molding (IM) and sheet extrusion grade. This resin offers extreme low temperature (-60 C) ductility in .. |
|||
Tensile Strength at Break | 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® EXL1413T PC Copolymer (Europe-Africa-Middle East) Lexan* EXL1413T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers excellent low temperature (-30 °C) ductility in combination with medium f.. |
|||
Tensile Strength at Break | 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® EXL1443T PC Copolymer Lexan* EXL1443T polycarbonate (PC) siloxane copolymer resin is an injection molding grade with FDA and EU food contact compliance. This resin offers excellent low temperature (-30 C) ductility in co.. |
|||
Tensile Strength at Break | 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® EXL1463T PC Copolymer (Asia Pacific) Lexan* EXL1463T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers excellent low temperature (-30 C) ductility in combination with medium flow ch.. |
|||
Tensile Strength at Break | 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® EXL1463T PC Copolymer (Europe-Africa-Middle East) Lexan* EXL1463T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers excellent low temperature (-30 C) ductility in combination with medium flow ch.. |
|||
Tensile Strength at Break | 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® HPX4 PC Copolymer (Europe-Africa-Middle East) Medium flow specialty polycarbonate - improved processability & autoclavability. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP.. |
|||
Tensile Strength at Break | 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® HPX4R PC Copolymer Medium flow specialty polycarbonate with outstanding processability, ductility and autoclavability. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatib.. |
|||
Tensile Strength at Break | 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® HPX4R PC Copolymer (Asia Pacific) Medium flow specialty polycarbonate with outstanding processability, ductility and autoclavability. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatib.. |
|||
Tensile Strength at Break | 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® SD1278 PC Copolymer (Asia Pacific) Lexan* SD1278 polycarbonate (PC) siloxane copolymer resin is a transparent extrusion grade for food contact applications for sheet extrusion. This resin offers extreme low temperature (-40 °C) .. |
|||
Tensile Strength at Break | 61.0 MPa | 8850 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Faradex NS0029 PC+ABS (Europe-Africa-Middle East) LNP* Faradex* NS0029 is a compound based on PC+ABS Blend resin containing Flame Retardant, Stainless Steel Fiber. Added features of this material include: EMI/RFI Shielding, Flame Retardant.This da.. |
|||
Tensile Strength at Break | 61.0 MPa | 8850 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® EXL9330 PC Copolymer (Europe-Africa-Middle East) Opaque PC-Siloxane copolymer with excellent processability. Non-chlorinated, non-brominated flame retardant product in most colors. UV-stabilized. UL rated f1/V-0/5VA. |
|||
Tensile Strength at Break | 61.0 MPa | 8850 psi | ASTM D638 |
LG Chemical LUCEL MR-320 Low Warpage POM, 20% Mineral Filled LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
Tensile Strength at Break | 61.0 MPa | 8850 psi | ASTM D638 |
LG Chemical LUCEL N109-HR Heat Resistant POM, Unreinforced, Standard Viscosity LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
Tensile Strength at Break | 61.0 MPa | 8850 psi | ASTM D638 |
LG Chemical LUCEL N115 POM, Unreinforced, High Viscosity LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
Tensile Strength at Break | 61.0 MPa | 8850 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Noryl TN240 PPE+PS PPE+PS blend. Unfilled. Transparent. Good flow. Scratch resistant. Injection molding. Suitable for housewares, personal care and small appliance applications.This data was supplied by SABIC-IP for t.. |
|||
Tensile Strength at Break | 61.0 MPa | 8850 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP Lexan_WR6300 AES+PC+SAN (Asia Pacific) Wear resistant PC+SAN, with proprietary lubricant, for business equipment applications. |
|||
Tensile Strength at Break | 61.0 MPa | 8850 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP RP004 PA 66 LNP LUBRICOMP* RP004 is a compound based on Nylon 66 resin containing 20% PTFE/Silicone. Added features of this material include: Wear Resistant. |
|||
Tensile Strength at Break | 61.0 MPa | 8850 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON DD0009E PC LNP* STAT-KON* DD0009E is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive, Flame Retardant, Easy Molding. |
|||
Tensile Strength at Break | 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL N850 PPE+PS (Asia Pacific) ECO-FLO(tm). ECO conforming, nonhalogenated flame retardant PPE+PS. High flow. Electrical and Business Equipment applications. |
|||
Tensile Strength at Break | 61.0 MPa | 8850 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP RI001 PA 66 LNP* LUBRICOMP* RI001 is a compound based on Nylon 66 resin containing 2% Silicone. Added feature of this grade is: Wear Resistant. |
|||
Tensile Strength at Break | 61.0 MPa | 8850 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Xenoy® X5600WX PC+POLYESTER (Europe-Africa-Middle East) Unreinforced, opaque Polyester+PC alloy. Chemical resistance, dimensional stability and mechanical performance. UV Stabilized. Mold ReleaseThis data was supplied by SABIC-IP for the Europe-Africa-Mi.. |
|||
Tensile Strength at Break | 61.0 MPa | 8850 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL GTX GTX679 PPE+PA6 Noryl GTX* GTX679 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is mineral filled, conductive, and suitable for injection molding. The conductivity level is optimized to al.. |
|||
Tensile Strength at Break | 61.0 MPa | 8850 psi | ASTM D 638 |
Cossa Polimeri ESTABLEND PSA 7800 PC / ASA Blend Polycarbonate and acrylonitrile styrene acrylate blendGood light resistance, good impact resistance, high heat resistance, excellent processabilityInformation provided by Cossa Polimeri S.r.l. |
|||
Tensile Strength at Break | 61.0 MPa | 8850 psi | ISO 527 - 1 & - 2 |
Asahi Kasei Tenac®-C MT754 Copolymer Acetal Resin 20% Mineral filled, high stiffness, low warp gradeInformation provided by Asahi Kasei Corporation. |
|||
Tensile Strength at Break | 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® EXL1433T PC Copolymer Lexan* EXL1433T polycarbonate (PC) siloxane copolymer resin is a UV stabilized transparent injection molding grade. This resin offers excellent low temperature (-30 C) ductility in combination with .. |
|||
Tensile Strength at Break | 61.0 MPa | 8850 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Xenoy® X5600WX PC+POLYESTER (Asia Pacific) Unreinforced, opaque Polyester+PC alloy. Chemical resistance, dimensional stability and mechanical performance. UV Stabilized. Mold ReleaseThis data was supplied by SABIC-IP for the Asia Pacific reg.. |