Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 87.0 MPa @Temperature 23.0 °C |
12600 psi @Temperature 73.4 °F |
ISO 527 |
DuPont Performance Polymers Crastin® SK601 BK851 PBT
(Unverified Data**) Crastin® SK601 BK851 is a 10% glass fiber reinforced, lubricated, black polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers |
|||
Tensile Strength at Break | 87.0 MPa | 12600 psi | |
Plastcom SLOVASTER® B1 HML GF 10 PBT, 10% glass fibre FeaturesPBT for injection moulding, chemically reinforced with 10% glass fibre. Characterised by excellent properties also at minus temperatures like eg. modulus of elasticity in tension and bending.. |
|||
Tensile Strength at Break | 87.0 MPa | 12600 psi | ISO 527 |
Nilit FRIANYL A63 GV 5 Nylon 6.6 for injection molding, 5% glass fiber reinforced Nylon 6.6 for injection moldingInformation provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Tensile Strength at Break | 87.0 MPa | 12600 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® 3262R PC (Asia Pacific) Lexan* 3262R Polycarbonate (PC) resin is a 20% glass fiber filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant GF-PC has an UL-94 V2@1.5mm rating and is available .. |
|||
Tensile Strength at Break | 87.0 MPa | 12600 psi | ISO 527 |
Nilit FRIANYL A63 KV25 Nylon 6.6 for injection molding, 25% glass ball reinforced Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Tensile Strength at Break | 87.0 MPa | 12600 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP GFL36L PSU (Asia Pacific) LNP* Lubricomp* GFL36L is a compound based on Polysulfone resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible. |
|||
Tensile Strength at Break | 87.0 MPa | 12600 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP KCL34A Acetal Homopolymer LNP* LUBRICOMP* KCL34A is a compound based on Acetal Homopolymer resin containing 15% PTFE, 20% Carbon Fiber. Added features of this material include: Wear Resistant, Electrically Conductive. |
|||
Tensile Strength at Break | 87.0 MPa | 12600 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP KCL34A Acetal Homopolymer (Asia Pacific) LNP* Lubricomp* KCL34A is a compound based on Acetal Homopolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive. |
|||
Tensile Strength at Break | 87.0 MPa | 12600 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics SABIC PPCOMPOUND G3220A PP SABIC® PPcompound G3220A is a general purpose, 20% glass filled, chemically coupled, heat stabilized homopolymer polypropylene compound. The IMDS is 209767996. |
|||
Tensile Strength at Break | 87.0 MPa | 12600 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRILOY RF203H PA 66 LNP LUBRILOY* RF203H is a compound based on Nylon 66 resin containing 15% Glass Fiber, Proprietary Lubricant. Added features of this material include: Wear Resistant, Healthcare. |
|||
Tensile Strength at Break | 87.0 MPa | 12600 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON DX11411 PC LNP* STAT-KON* DX11411 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added feature of this grade is: Electrically Conductive. |
|||
Tensile Strength at Break | 87.0 MPa | 12600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON PFD04 PA 6 LNP* STAT-KON* PFD04 is a compound based on Nylon 6 containing 20% Glass Fiber. Added feature of this grade is: Ellectrically Conductive. |
|||
Tensile Strength at Break | 87.0 MPa | 12600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON PFD04S PA 6 (Europe-Africa-Middle East) LNP* Statkon* PFD04S is a compound based on PA 6 resin containing Glass Fiber, Carbon Powder. Added features include: Electrically Conductive, Heat Stabilized. |
|||
Tensile Strength at Break | 87.0 MPa | 12600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Thermocomp MF008S PP (Europe-Africa-Middle East) Heat Stabilized Polypropylene compound containing Glass Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Strength at Break | 87.0 MPa | 12600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP RF002SXS PA 66 LNP* THERMOCOMP* RF002SXS is a compound based on Nylon 66 resin contaning 10% Glass Fiber. Characteristcs of this grade are: Heat Stabilized. |
|||
Tensile Strength at Break | 87.0 MPa | 12600 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP RF002XXH PA 66 LNP THERMOCOMP* RF002XXH is a compound based on Nylon 66 resin containing 10% Glass Fiber. Added feature of this material includes: Healthcare. |
|||
Tensile Strength at Break | 87.0 MPa | 12600 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON DX03633C PC LNP STAT-KON* DX03633C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Clean Compounding System, Electrically Conductive. |
|||
Tensile Strength at Break | 87.0 MPa | 12600 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP MF00AS PP LNP THERMOCOMP* MF00AS is a compound based on Polypropylene resin containing 50% Glass Fiber. Added features of this material include: Chemically Coupled. |
|||
Tensile Strength at Break | 87.0 MPa | 12600 psi | ISO 527-1/-2 |
Unitika BV2120G15 PA66, 15% Glass Fiber Reinforced, Flame Retardant, Conditioned Information provided by Unitika Ltd. |
|||
Tensile Strength at Break | 87.0 MPa | 12600 psi | ASTM D638 |
Toyobo VYLOPET® CA5310 PC/PBT Polymer Alloy, High Rigidity, Impact Resistant Applications: Lamp partsHome electric appliance partsFeatures: Fine appearanceHigh rigidityImpact resistantInformation provided by Toyobo. |
|||
Tensile Strength at Break | 87.0 MPa | 12600 psi | DAM; ISO 527-1/-2 |
DuPont Performance Polymers Minlon® 11C140 BK086 Nylon 66
(Unverified Data**) 40% Mineral Reinforced Polyamide 66 Minlon 11C140 BK086 is a 40% mineral reinforced heat stabilized black polyamide 66 resin for injection molding. It has very low warpage.Information provided by Du.. |
|||
Tensile Strength at Break | 87.0 MPa | 12600 psi | 50%RH; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® 80G25HS BK117 Nylon 66
(Unverified Data**) 25% Glass Reinforced Toughened Heat Stabilized Polyamide 66 Zytel 80G25HS BK117 is a 25% glass fiber reinforced toughened heat stabilized black polyamide 66 resin for injection molding.Information p.. |
|||
Tensile Strength at Break | 87.0 MPa | 12600 psi | 5 mm/min; ISO 527 |
Eurostar Starpylen MF008S PP, 40% Glass Fiber Filled, Injection Molded Starpylen MF008S is a 40% Glass Fiber Reinforced Polypropylene Injection Molding ResinInformation provided by Eurostar. |
|||
Tensile Strength at Break | 87.0 MPa | 12600 psi | ISO 527-1/-2 |
DSM Akulon® K224-HG4 Nylon 6-20% Glass Reinforced (European Grade) (Cond) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
Tensile Strength at Break | 87.0 MPa | 12600 psi | ASTM D638 |
Unitika U-8000 U series resins are polymer alloys that are improved in resistance to oils and chemicals, the shortcoming of amorphous resins. They are transparent and have a greater moisture blocking property than.. |
|||
Tensile Strength at Break | 87.0 MPa | 12600 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® 3412ECR PC Lexan* 3412ECR Polycarbonate (PC) resin is a 20% glass fiber filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant GF-PC has an UL-94 V0 rating and is available in v.. |
|||
Tensile Strength at Break | 87.0 MPa | 12600 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® 3412ECR PC (Asia Pacific) Lexan* 3412ECR Polycarbonate (PC) resin is a 20% glass fiber filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant GF-PC has an UL-94 V0 rating and is available in v.. |
|||
Tensile Strength at Break | 87.0 MPa | 12600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP VERTON MV006BS PP LNP* VERTON* MV006BS is a compound based on Polypropylene resin containing 30% Long Glass Fiber. Added features of this grade include: Heat Stabilized, Burst Pressure, Structural, Chemically Coupl.. |
|||
Tensile Strength at Break | 87.0 MPa | 12600 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® VX4510 PBT (Europe-Africa-Middle East) VALOX VX4510 is a flame retarded, 10% glassfiber reinforced injection moulding PBT resin. |