Polymer Property : Tensile Strength, Yield = 70000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	483 MPa @Temperature 23.9 °C	70000 psi @Temperature 75.0 °F	0° Direction, Dry, Autoclave with Post-Cure; ASTM D638
Park Electrochemical Nelcote® E-746 Epoxy Prepreg, 581 Quartz Reinforced Nelcote® E-746 is a modified epoxy resin system designed to retain excellent mechanical properties after extended exposure to high temperature. E-746 has a proven history in many demanding aerospac..
Tensile Strength, Yield	483 MPa @Temperature 23.9 °C	70000 psi @Temperature 75.0 °F	0° Direction, Dry; ASTM D638 Type 1
Park Electrochemical Nelcote® P-670I Polyester Prepreg, 7781 E-Glass Reinforced Nelcote® P-670I is a versatile, non-styrenated/low VOC polyester resin. P670I is used in a wide variety of applications including radomes, tooling and aircraft structures.Key Features and Benefits:..
Tensile Strength, Yield	483 MPa @Temperature 82.2 °C	70000 psi @Temperature 180 °F	0° Direction, Wet; ASTM D638
Park Electrochemical Nelcote® V-376 Cyanate Ester Epoxy Prepregs, 581 Quartz Reinforced Nelcote® V-376 is a Cyanate Ester matrix providing excellent electrical and mechanical properties for harsh aircraft, shipboard, and undersea applications for Radomes, Antenna, and Reflectors. Simp..
Tensile Strength, Yield	>= 483 MPa @Strain 0.200 %, Thickness 12.7 - 25.4 mm	>= 70000 psi @Strain 0.200 %, Thickness 0.500 - 1.00 in	ASTM E-8
H.C. Starck 3203 Pure Molybdenum APL, Arc-Cast, Low Carbon Plate Arc-Cast Plate 3203 Low CarbonDescription of Product: This specification covers rolled plate of carbon-deoxidized molybdenum produced from ingots consolidated by the H.C. Starck consumable electrod..
Tensile Strength, Yield	>= 483 MPa @Diameter 22.2 - 28.57 mm, Strain 0.200 %	>= 70000 psi @Diameter 0.875 - 1.125 in, Strain 0.200 %	ASTM E-8
H.C. Starck Pure Molybdenum AB, Arc-Cast Bar Arc-Cast BarDescription of Product: This specification covers carbon-deoxidized molybdenum wrought bar produced from ingots consolidated by the H.C. Stark consumable electrode vacuum-arc-casting pr..
Tensile Strength, Yield	>= 483 MPa @Diameter 22.2 - 28.57 mm, Strain 0.200 %	>= 70000 psi @Diameter 0.875 - 1.125 in, Strain 0.200 %	ASTM E-8
H.C. Starck Pure Molybdenum ABL, Arc-Cast, Low Carbon Bar Description of Product: This specification covers carbon-deoxidized, low-carbon molybdenum wrought bar produced from ingots consolidated by the H.C. Starck consumable electrode vacuum-arc-casting p..
Tensile Strength, Yield	483 - 621 MPa @Strain 0.200 %, Thickness <=25.4 mm	70000 - 90000 psi @Strain 0.200 %, Thickness <=1.00 in	Cold Drawn Bars
Schmolz + Bickenbach UGIMAÂ® 304 Cu Stainless Steel Bar Description: 304Cu UGIMAÂ® is an enhanced machining grade produced only by Ugitech, providing the ultimate level of machinability available in an non-resulfurized austenitic stainless steel. 304Cu..
Tensile Strength, Yield	>= 483 MPa @Thickness 3.17 mm	>= 70000 psi @Thickness 0.125 in	Longitudinal Direction
Alcoa 2090-T83 Aluminum Aluminum-lithium alloy developed for high strength aerospace applications. The Al-Cu-Li alloy offers an 8 per cent density savings when compared with other aerospace alloys. Alloy 2090-T83 also has ..