Material Notes:
Description of Product: This specification covers carbon-deoxidized, low-carbon molybdenum wrought bar produced from ingots consolidated by the H.C. Starck consumable electrode vacuum-arc-casting process.Structure: Bar will be supplied in a stress-relieved condition. Material can also be supplied in the recrystallized condition.Information provided by H.C. Starck.
Mechanical Properties Metric English Comments
Hardness, Vickers <= 200

@Load 10.0 kg
<= 200

@Load 22.0 lb
mid-radius, recrystallized bar, all sizes; DPH (10 kg)
205 - 240

@Load 10.0 kg,
Diameter 73.03 - 88.9 mm
205 - 240

@Load 22.0 lb,
Diameter 2.875 - 3.50 in
mid-radius; DPH (10 kg)
210 - 250

@Load 10.0 kg,
Diameter 47.63 - 73.03 mm
210 - 250

@Load 22.0 lb,
Diameter 1.875 - 2.875 in
mid-radius; DPH (10 kg)
215 - 260

@Load 10.0 kg,
Diameter 28.57 - 47.63 mm
215 - 260

@Load 22.0 lb,
Diameter 1.125 - 1.875 in
mid-radius; DPH (10 kg)
225 - 270

@Load 10.0 kg,
Diameter 22.2 - 28.57 mm
225 - 270

@Load 22.0 lb,
Diameter 0.875 - 1.125 in
mid-radius; DPH (10 kg)
230 - 280

@Load 10.0 kg,
Diameter 3.17 - 22.2 mm
230 - 280

@Load 22.0 lb,
Diameter 0.125 - 0.875 in
mid-radius; DPH (10 kg)
Tensile Strength >= 448 MPa

@Diameter 73.03 - 88.9 mm
>= 65000 psi

@Diameter 2.875 - 3.50 in
ASTM E-8
>= 483 MPa

@Diameter 47.63 - 73.03 mm
>= 70000 psi

@Diameter 1.875 - 2.875 in
ASTM E-8
>= 517 MPa

@Diameter 3.17 - 10.319 mm
>= 75000 psi

@Diameter 0.125 - 0.40625 in
ASTM E-8
>= 517 MPa

@Diameter 28.57 - 47.63 mm
>= 75000 psi

@Diameter 1.125 - 1.875 in
ASTM E-8
>= 586 MPa

@Diameter 22.2 - 28.57 mm
>= 85000 psi

@Diameter 0.875 - 1.125 in
ASTM E-8
>= 621 MPa

@Diameter 10.319 - 22.2 mm
>= 90000 psi

@Diameter 0.40625 - 0.875 in
ASTM E-8
Tensile Strength, Yield >= 379 MPa

@Diameter 3.17 - 10.319 mm,
Strain 0.200 %
>= 55000 psi

@Diameter 0.125 - 0.40625 in,
Strain 0.200 %
ASTM E-8
>= 379 MPa

@Diameter 73.03 - 88.9 mm,
Strain 0.200 %
>= 55000 psi

@Diameter 2.875 - 3.50 in,
Strain 0.200 %
ASTM E-8
>= 414 MPa

@Diameter 47.63 - 73.03 mm,
Strain 0.200 %
>= 60000 psi

@Diameter 1.875 - 2.875 in,
Strain 0.200 %
ASTM E-8
>= 448 MPa

@Diameter 28.57 - 47.63 mm,
Strain 0.200 %
>= 65000 psi

@Diameter 1.125 - 1.875 in,
Strain 0.200 %
ASTM E-8
>= 483 MPa

@Diameter 22.2 - 28.57 mm,
Strain 0.200 %
>= 70000 psi

@Diameter 0.875 - 1.125 in,
Strain 0.200 %
ASTM E-8
>= 517 MPa

@Diameter 10.319 - 22.2 mm,
Strain 0.200 %
>= 75000 psi

@Diameter 0.40625 - 0.875 in,
Strain 0.200 %
ASTM E-8
Elongation at Break >= 10 %

@Diameter 28.57 - 47.63 mm
>= 10 %

@Diameter 1.125 - 1.875 in
ASTM E-8
>= 10 %

@Diameter 47.63 - 73.03 mm
>= 10 %

@Diameter 1.875 - 2.875 in
ASTM E-8
>= 10 %

@Diameter 73.03 - 88.9 mm
>= 10 %

@Diameter 2.875 - 3.50 in
ASTM E-8
>= 15 %

@Diameter 3.17 - 10.319 mm
>= 15 %

@Diameter 0.125 - 0.40625 in
ASTM E-8
>= 15 %

@Diameter 10.319 - 22.2 mm
>= 15 %

@Diameter 0.40625 - 0.875 in
ASTM E-8
>= 15 %

@Diameter 22.2 - 28.57 mm
>= 15 %

@Diameter 0.875 - 1.125 in
ASTM E-8
Component Elements Properties Metric English Comments
Carbon, C <= 0.010 %
<= 0.010 %
Iron, Fe <= 0.010 %
<= 0.010 %
Molybdenum, Mo >= 99.97 %
>= 99.97 %
by difference
Nickel, Ni <= 0.0020 %
<= 0.0020 %
Nitrogen, N <= 0.0020 %
<= 0.0020 %
Oxygen, O <= 0.0015 %
<= 0.0015 %
Silicon, Si <= 0.010 %
<= 0.010 %