Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, MD | 131 MPa | 19000 psi | ASTM D882 |
DuPont™ Clysar® EHC Polyolefin Shrink Packaging Film, 50 Gauge
(discontinued **) Data provided by DuPont Packaging Polymers.A biaxially oriented, heat-shrinkable copolymer film. It is a polypropylene and polyethylene-based film that is predominantly polypropylene. Used when exc.. |
|||
Film Tensile Strength at Break, MD | 131 MPa | 19000 psi | ASTM D882 |
DuPont™ Clysar® EHC Polyolefin Shrink Packaging Film, 60 Gauge
(discontinued **) Data provided by DuPont Packaging Polymers.A biaxially oriented, heat-shrinkable copolymer film. It is a polypropylene and polyethylene-based film that is predominantly polypropylene. Used when exc.. |
|||
Film Tensile Strength at Break, MD | 131 MPa | 19000 psi | ASTM D882 |
DuPont™ Clysar® EHC Polyolefin Shrink Packaging Film, 75 Gauge
(discontinued **) Data provided by DuPont Packaging Polymers.A biaxially oriented, heat-shrinkable copolymer film. It is a polypropylene and polyethylene-based film that is predominantly polypropylene. Used when exc.. |
|||
Film Tensile Strength at Break, MD | 131 MPa | 19000 psi | ASTM D882 |
DuPont™ Clysar® EHC Polyolefin Shrink Packaging Film, 100 Gauge
(discontinued **) Data provided by DuPont Packaging Polymers.A biaxially oriented, heat-shrinkable copolymer film. It is a polypropylene and polyethylene-based film that is predominantly polypropylene. Used when exc.. |
|||
Film Tensile Strength at Break, MD | 131 MPa | 19000 psi | ASTM D882 |
DuPont™ Clysar® EHC Polyolefin Shrink Packaging Film, 150 Gauge
(discontinued **) Data provided by DuPont Packaging Polymers.A biaxially oriented, heat-shrinkable copolymer film. It is a polypropylene and polyethylene-based film that is predominantly polypropylene. Used when exc.. |
|||
Film Tensile Strength at Break, MD | 131 MPa | 19000 psi | ASTM D882 |
Total PPH 3371 Polypropylene, Oriented Film Extrusion Grade Homopolymer film gradeLow Residuals - Fina 3371 utilizes the new Fina proprietary process technology to provide extremely low residuals for improved color stability and clarity.Slip/Antiblock - Fina.. |
|||
Film Tensile Strength at Break, MD | 131 MPa | 19000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
ExxonMobil Bicor® 50 LBW OPP Film Product Description: Bicor LBW is a two-sided treated, slip modified, non-heat sealable OPP film designed for use as the outside web of a lamination. The print surface is treated and can be printed .. |
|||
Film Tensile Strength at Break, MD | 131 MPa | 19000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
ExxonMobil Bicor™ 120 XRG-2 OPP Film Product Description: Bicor 120 XRG-2 is a one-side sealable OPP film that can be used as the inside web of a lamination where exceptional seal performance is required. The high-energy surface is int.. |
|||
Film Tensile Strength at Break, MD | 131 MPa | 19000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
ExxonMobil Bicor™ 70 XRG-2 OPP Film Product Description: Bicor 70 XRG-2 is one-side treated, one-side sealable OPP film that can be used as the inside web of a lamination where exceptional seal performance is required. The high-energy.. |
|||
Film Tensile Strength at Break, MD | 131 MPa | 19000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
ExxonMobil Metallyte® 50 TSPM OPP Film Product Description: A high barrier, non-sealable OPP film with one-side metalized a one-side treated. TSP< is designed for use as the inner web of a cold seal lamination or as the center web of a t.. |
|||
Film Tensile Strength at Break, MD | 131 MPa | 19000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
ExxonMobil Metallyte™ 12MM281 OPP Film Product Description: A high barrier, non-sealable OPP film with one-side metalized and one-side treated. 12MM281 is designed for use as the center web of a triplex adhesive lamination. The treated s.. |
|||
Film Tensile Strength at Break, MD | 131 MPa | 19000 psi | ASTM D882A |
DuPont Teijin Films Melinex® ST329 Polyester Film, 1000 Gauge MELINEX® ST329 has good handling properties and a unique pearlescent appearance with no pre-treatments. It is heat stabilized for applications in high temperature processes where film registration .. |
|||
Film Tensile Strength at Break, MD | 131 MPa | 19000 psi | ASTM D882A |
DuPont Teijin Films Mylar® EB11 Polyester Film, 200 Gauge Mylar® EB11 is a low gloss polyester film with a matte surface. It is typically used as a carrier film. It is commercially available in nominal 48 - 300 gauge. General Product Info: Mylar® EB11 is.. |
|||
Film Tensile Strength at Break, MD | 131 MPa | 19000 psi | ASTM D882A |
DuPont Teijin Films Mylar® EB11 Polyester Film, 300 Gauge Mylar® EB11 is a low gloss polyester film with a matte surface. It is typically used as a carrier film. It is commercially available in nominal 48 - 300 gauge. General Product Info: Mylar® EB11 is.. |
|||
Film Tensile Strength at Break, MD | 131 MPa | 19000 psi | ASTM D882A |
DuPont Teijin Films Mylar® EB11 Polyester Film, 92 Gauge Mylar® EB11 is a low gloss polyester film with a matte surface. It is typically used as a carrier film. It is commercially available in nominal 48 - 300 gauge. General Product Info: Mylar® EB11 is.. |
|||
Film Tensile Strength at Break, MD | 131 MPa | 19000 psi | ASTM D882A |
DuPont Teijin Films Mylar® EB11 Polyester Film, 48 Gauge Mylar® EB11 is a low gloss polyester film with a matte surface. It is typically used as a carrier film. It is commercially available in nominal 48 - 300 gauge. General Product Info: Mylar® EB11 is.. |