Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, MD | 15.0 - 31.0 MPa | 2180 - 4500 psi | Average value: 24.0 MPa Grade Count:12 |
Overview of materials for Ethylene Vinyl Acetate Copolymer (EVA), Extrusion/Coating Grade This property data is a summary of similar materials in the MatWeb database for the category "Ethylene Vinyl Acetate Copolymer (EVA), Extrusion/Coating Grade". Each property range of values reported.. |
|||
Film Tensile Strength at Break, MD | 15.0 - 40.0 MPa | 2180 - 5800 psi | Average value: 27.1 MPa Grade Count:145 |
Overview of materials for Ethylene Vinyl Acetate Copolymer (EVA), Film Grade This property data is a summary of similar materials in the MatWeb database for the category "Ethylene Vinyl Acetate Copolymer (EVA), Film Grade". Each property range of values reported is minimum a.. |
|||
Film Tensile Strength at Break, MD | 15.0 MPa | 2180 psi | ISO 527 |
Inno-Comp INNOPOL® CS 5-8250 W 50% Chalk-Filled High Density Polyethylene INNOPOL® CS 5-8250 W is a 50% chalk-filled compound based on high density polyethylene.INNOPOL® CS 5-8250 W is developed for packaging film production.All information provided by INNO-COMP. |
|||
Film Tensile Strength at Break, MD | 15.0 - 193 MPa | 2180 - 28000 psi | Average value: 121 MPa Grade Count:382 |
Overview of materials for Polypropylene, Film Grade This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Film Grade". Each property range of values reported is minimum and maximum values of appr.. |