Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ISO 527-3 |
Polimeri Europa Clearflex® FF D0 Very Low Density Polyethylene Clearflex FF D0 is a linear low density polyethylene, with antioxidants, suitable for blown film technology.Films made with Clearflex FF D0 are highly transparent, have excellent sealing properties,.. |
|||
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ISO 527-3 |
Polimeri Europa Clearflex® FG 106 Hexene Copolymer Linear Low Density Polyethylene Clearflex FG 106 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants, suitable for blown film extrusion.Films manufactured with Clearflex FG 106 are characterized by .. |
|||
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ISO 527-3 |
Polimeri Europa Clearflex® H&T FHH 508 Octene Copolymer Linear Medium Density Polyethylene Clearflex H&T FHH 508 is an octene copolymer linear medium density polyethylene (C8-LMDPE), with antioxidant, suitable for blown film extrusion.Films obtained from Clearflex H&T FHH 508 show good op.. |
|||
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ISO 527-3 |
Polimeri Europa Clearflex® H&T LFH 208 Octene Copolymer Linear Low Density Polyethylene Clearflex H&T LFH 208 is an octene copolymer linear low density polyethylene (C8-LLDPE), with antioxidants and processing aid, suitable for blown film extrusion.Films obtained from Clearflex H&T LFH.. |
|||
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ISO 527-3 |
Polimeri Europa Clearflex® H&T LFH 238 Octene Copolymer Linear Low Density Polyethylene Clearflex H&T LFH 238 is an octene copolymer linear low density polyethylene (C8-LLDPE), with antioxidants and processing aid, suitable for blown film extrusion. It contains slip and antiblocking a.. |
|||
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ISO 527-3 |
Polimeri Europa Eraclene® FB 506 Hexene Copolymer High Density Polyethylene - Blown Film Extrusion Eraclene FB 506 is a high density polyethylene resin (HDPE), hexene copolymer, with antioxidants, suitable for blown film extrusion.Its broad molecular weight distribution and density successfully c.. |
|||
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ISO 527-3 |
Polimeri Europa Clearflex® FF 106 Hexene Copolymer Linear Low Density Polyethylene Clearflex FF 106 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants, suitable for blown film extrusion.Films manufactured with Clearflex FF 106 are characterized by .. |
|||
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ISO 527-3 |
Polimeri Europa Clearflex® FF 508 Octene Copolymer Linear Medium Density Polyethylene Clearflex FF 508 is an octene copolymer linear medium density polyethylene (C8-LMDPE), with antioxidants and processing aid, suitable for blown film extrusion.Films manufactured with Clearflex FF 50.. |
|||
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ISO 527 |
Premix Thermoplastics PRE-ELEC® ESD 1100
(discontinued **) PRE-ELEC ESD 1100 is a static dissipative thermoplastic compound based on PETG. The dissipative property is permanent and built into the polymer chain. PRE-ELEC ESD 1100 has been developed for the e.. |
|||
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM D882 |
Chevron Phillips 7120ST LLDPE Blown Film Resin, Hexene Copolymer
(discontinued **) Resin Type: Hexene Copolymer, Cast/Blown Film ResinCharacteristics: Good Drawdown, Can be used in blown or cast applicationsApplications:Stretch Wrap, CoextrusionsProcessing Conditions: Extruder 6.3.. |
|||
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM D882 |
ExxonMobil Exceed™ 377D60 LDPE/Hexene Tough Premium Film Resin, 3 mil Film
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A hexene copolymer produced using Exxon Chemical's EXXPOL® technology. Films made from EXCEED 377D60 resin exhibit excellent impact strength and b.. |
|||
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM D882 |
Reliance Industries Relene E52009 Polyethylene Relene E52009 is a High Density Polyethylene grade with low gel content, excellent orientation characteristics and negligible water carry-over. This grade is recommended for making raffia tapes and.. |
|||
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM D882 |
Iran Petrochemical (PCC) 09X02 Linear Low Density Polyethylene 09X02 is a high performance LLDPE (HP-LLDPE) cast film grade combines ease of processing with low gels and good film strength. Its excellent stretchability makes this grade particularly suited for s.. |
|||
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ISO 1184 |
SIDPEC EGYPTENE® HD 3802 FA HDPE Film Applications:General purpose thin film, trash bags, merchant bagsBlending partnerFilm properties were measured on 15 micron film extruded at a blow up ratio of 5:1, 10D neck height.Information provi.. |
|||
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ISO 527-3 |
Borealis Bormed™ SC820CF Polypropylene Random Copolymer Bormed™ SC820CF is a very soft random heterophasic copolymer. Applications: Bormed™ SC820CF is recommended for packaging for medical devices. Bormed™ SC820CF contains no slip, antiblock, antist.. |
|||
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ISO 527-3 |
Borealis FS1560 High Density Polyethylene FS1560 is a high density polyethylene film grade which combine excellent extrusion behavior with superior mechanical properties. Films made of FS1560 have high impact and tensile strength, and bala.. |
|||
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ISO 527-3 |
Borealis Borstar® FB2310 LLDPE for Film Borstar BF2310 is a high molecular weight low density polyethylene film grade combining good and flexible extrusion behavior, excellent draw down and superior mechanical properties. Film made from .. |
|||
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ISO 527-3 |
Borealis Borstar® FB4230 LLDPE for Film Borstar FB4250T is a high molecular weight linear low density polyethylene grade combining good extrusion properties, excellent draw properties and good mechanical strength. Film made from Borstar .. |
|||
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ISO 527-3 |
Borealis FS1470 High Density Polyethylene FS1470 is a high density polyethylene film grade which combine excellent extrusion behavior with superior mechanical properties. Films made of FS1470 have high impact and tensile strength, and bala.. |
|||
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM D882 |
Eastman Cadence™ GS5 Clear (Unpigmented) Copolyester for film calendering Eastman Cadence™ copolyester, for calendered films, is a specialty plastic developed to meet the demand for an environmentally responsible material for the calendering industry. Available in diffe.. |
|||
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM D882 |
Braskem EB861 Blown Film Extrusion Low Density Polyethylene Medium-resistance films for general use; Mulching films; Shrink films; Coextrusion.Information provided by Braskem. |
|||
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM-D882 |
Braskem LL4800N PEBDL Cast Film Extrusion Polyethylene Copolymer LL4800N is a linear low-density polyethylene, copolymer of octene-1, produced by the solution process. It was developed for cast film extrusion. Films obtained with this product show a good processi.. |
|||
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM-D882 |
Braskem LL5800N LLDPE Blown Film Extrusion Polyethylene Copolymer LL5800N resin is a linear low-density polyethylene, copolymer of octene-1, produced by the solution process for blown film extrusion with excellent mechanical properties. It contains processing aid .. |
|||
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM-D882 |
Braskem LL5801N LLDPE Blown Film Extrusion Polyethylene Copolymer The LL5801N resin is a linear low-density polyethylene, copolymer of octene-1, produced by the solution process for blown film extrusion with excellent mechanical properties. It contains processing .. |
|||
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM-D882 |
Braskem Pluris 9300 LLDPE Blown Film Extrusion Polyethylene Quatropolymer Pluris 9300 is a Quatropolymer produced with Spherilene technology and is a LLDPE with unique properties, such as high stiffness associated with toughness. It is easier to process than conventional .. |
|||
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM-D882 |
Braskem Pluris 9310 LLDPE Blown Film Extrusion Polyethylene Quatropolymer Pluris 9310 is a Braskem Quatropolymer produced with Spherilene technology and is a LLDPE with unique properties, such as high stiffness associated with toughness. It is easier to process than conve.. |
|||
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM D882 |
Braskem Green PE SLH0820/30AF Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene Description: SLH0820/30AF is a LLDPE hexene copolymer produced by Braskem. It offers outstanding processability combined with excellent mechanical properties. Very low gel amount. The minimum biobas.. |
|||
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM D882 |
Huntsman Rexell® M3105 Blown Film Extrusion LLDPE
(discontinued **) Linear-low medium density copolymer, cast film extrusion, FDA compliantFeatures: Excellent combination of toughness, stiffness, and water vapor barrier with good temperature resistance.Applications:.. |
|||
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM D882 |
NOVA Chemicals Sclair® 13J7 Octene LMDPE Film Resin
(discontinued **) Film Properties. Features: Low gel, high clarity.Applications: Film.Data provided by the manufacturer. |
|||
Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM D882 |
Braskem LL 118 LLDPE Blown Film Extrusion Polyethylene Description: LL118 is a Linear Low Density Polyethylene, copolymer of butene-1, produced by Spherilene process. Developed for blown film extrusion in blends with polyethylenes. Films obtained with t.. |