Reliance Industries Relene E52009 Polyethylene

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded
Manufacturer Reliance Industries
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Reliance Industries Relene E52009 Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Relene E52009 is a High Density Polyethylene grade with low gel content, excellent orientation characteristics and negligible water carry-over. This grade is recommended for making raffia tapes and monofilaments with an excellent balance of high tenacity and good elongation. Information provided by Reliance Industries
Physical Properties Metric English Comments
Density 0.952 g/cc
0.0344 lb/in³
ASTM D1505
Melt Flow 0.85 g/10 min

@Load 2.16 kg
0.85 g/10 min

@Load 4.76 lb
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 34.5 MPa
5000 psi
ASTM D882
Film Tensile Strength at Yield, TD 37.5 MPa
5440 psi
ASTM D882
Film Elongation at Break, MD 900 %
900 %
ASTM D882
Film Elongation at Break, TD 950 %
950 %
ASTM D882
Elmendorf Tear Strength, MD 0.600 g/micron
15.2 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 1.70 g/micron
43.2 g/mil
ASTM D1922
Dart Drop 1.50 g/micron
38.1 g/mil
38mm Dart, 66mm height; ASTM D1709
Film Tensile Strength at Break, MD 50.0 MPa
7250 psi
ASTM D882
Film Tensile Strength at Break, TD 45.0 MPa
6530 psi
ASTM D882