Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	860 - 1070 MPa	125000 - 155000 psi
Materion Beryllium Copper Alloy 165 Forgings & Extrusions; AT (TF00) Temper (UNS C17000) Treatment required for max strength: 3 hrs @ 330Â°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials In..
Tensile Strength, Yield	890 - 1070 MPa	129000 - 155000 psi
Materion Beryllium Copper Alloy 165 Plate & Rolled Bar; AT (TF00) Temper; All Thicknesses (UNS C17000) Treatment required for max strength: 3 hrs @ 330Â°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials In..
Tensile Strength, Yield	860 - 1070 MPa	125000 - 155000 psi
Materion Beryllium Copper Alloy 165 Plate & Rolled Bar; HT (TH04) Temper; over 51 to 76 mm Thickness (UNS C17000) Treatment required for max strength: 2 hrs @ 330Â°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials In..
Tensile Strength, Yield	860 - 1070 MPa	125000 - 155000 psi
Materion Beryllium Copper Alloy 165 Rod and Bar; AT (TF00) Temper; over 76 mm (UNS C17000) Treatment required for max strength: 3 hrs @ 315-330Â°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Material..
Tensile Strength, Yield	860 - 1070 MPa	125000 - 155000 psi
Materion Beryllium Copper Alloy 165 Rod and Bar; AT (TF00) Temper; up to 76 mm (UNS C17000) Treatment required for max strength: 3 hrs @ 315-330Â°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Material..
Tensile Strength, Yield	930 - 1070 MPa	135000 - 155000 psi
Materion BrushformÂ® 290 Beryllium Copper Alloy Strip; TM06 Temper (UNS C17200) Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100Â°C: 99%Stress Relaxation after 1000 hrs @ 200Â°C: 78%Formability Ratio, 90Â° Bend, R..
Tensile Strength, Yield	931 - 1070 MPa @Strain 0.200 %, Thickness <=25.4 mm	135000 - 155000 psi @Strain 0.200 %, Thickness <=1.00 in	Cold Drawn Bars
Schmolz + Bickenbach UGIMAÂ® 630 Stainless Steel Bar Description: 630 UGIMAÂ® is an improved machining martensitic precipitation hardenable grade produced only by Ugitech. It is identical in every way to standard type 630 (17-4), except with respect..