Polymer Property : Tensile Strength, Yield = 135000 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 930 - 1140 MPa | 135000 - 165000 psi | |
| Materion Beryllium Copper Alloy 165 Plate & Rolled Bar; HT (TH04) Temper; over 9.5 to 25 mm Thickness (UNS C17000) Treatment required for max strength: 2 hrs @ 330°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials In.. |
|||
| Tensile Strength, Yield | 930 - 1140 MPa | 135000 - 165000 psi | |
| Materion Beryllium Copper Alloy 165 Plate & Rolled Bar; HT (TH04) Temper; up to 9.5 mm Thickness (UNS C17000) Treatment required for max strength: 2 hrs @ 330°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials In.. |
|||
| Tensile Strength, Yield | 930 - 1210 MPa | 135000 - 175000 psi | |
| Materion Beryllium Copper Alloy 165 Rod and Bar; HT (TH04) Temper; over 25.4 to 76 mm (UNS C17000) Treatment required for max strength: 2-3 hrs @ 315-330°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materi.. |
|||
| Tensile Strength, Yield | 930 - 1180 MPa | 135000 - 171000 psi | |
| Materion Beryllium Copper Alloy 190 Strip; XHM (TM06) Temper (UNS C17200) Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100°C: 98%Stress Relaxation after 1000 hrs @ 200°C: 69%Formability Ratio, 90° Bend, R.. |
|||
| Tensile Strength, Yield | 931 - 1000 MPa @Strain 0.200 % |
135000 - 145000 psi @Strain 0.200 % |
|
| Materion BrushCAST® 165CT Fine Grain Casting Alloy (Solution Annealed & Aged) Pouring Temperature: 1010-1120°CHeat treatment required for max strength (Annealing): 760-790°C/water quenchHeat treatment required for max strength (Hardening): 760-790°C/water quenchDescr.. |
|||
| Tensile Strength, Yield | 930 - 1070 MPa | 135000 - 155000 psi | |
| Materion Brushform® 290 Beryllium Copper Alloy Strip; TM06 Temper (UNS C17200) Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100°C: 99%Stress Relaxation after 1000 hrs @ 200°C: 78%Formability Ratio, 90° Bend, R.. |
|||
| Tensile Strength, Yield | 931 MPa | 135000 psi | 621°C Temper Temperature |
| Latrobe Lescalloy® 16NCD13 VAC-ARC High Strength Alloy Steel 16NCD13 VAC-ARC is a premium quality low alloy, carburizing casehardenable vacuum arc remelted steel which takes its name from the French industry designation. In the carburized condition, its high .. |
|||
| Tensile Strength, Yield | 931 MPa @Strain 0.200 % |
135000 psi @Strain 0.200 % |
496°C Temper Temperature |
| Latrobe Lescalloy® 16NCD13 VAC-ARC High Strength Alloy Steel 16NCD13 VAC-ARC is a premium quality low alloy, carburizing casehardenable vacuum arc remelted steel which takes its name from the French industry designation. In the carburized condition, its high .. |
|||
| Tensile Strength, Yield | 931 - 1050 MPa | 135000 - 153000 psi | |
| Materion Alloy 390 Beryllium Nickel Strip Alloy 390 was specifically designed for high power applications, providing a unique combination of high strength and high conductivity. Increasing power requirements are driving the need for lower c.. |
|||
| Tensile Strength, Yield | 931 - 1000 MPa @Strain 0.200 % |
135000 - 145000 psi @Strain 0.200 % |
|
| Materion BrushCAST® 165C High Strength Casting Alloy (Solution Annealed & Aged) Pouring Temperature: 1010-1120°CHeat treatment required for max strength (Annealing): 760-790°C/water quenchHeat treatment required for max strength (Hardening): 760-790°C/water quenchDescr.. |
|||
| Tensile Strength, Yield | 930 MPa @Strain 0.200 % |
135000 psi @Strain 0.200 % |
|
| Haynes 242® alloy, cold rolled sheet, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Tensile Strength, Yield | 931 - 1070 MPa @Strain 0.200 %, Thickness <=25.4 mm |
135000 - 155000 psi @Strain 0.200 %, Thickness <=1.00 in |
Cold Drawn Bars |
| Schmolz + Bickenbach UGIMA® 630 Stainless Steel Bar Description: 630 UGIMA® is an improved machining martensitic precipitation hardenable grade produced only by Ugitech. It is identical in every way to standard type 630 (17-4), except with respect.. |
|||
| Tensile Strength, Yield | 930 MPa @Strain 0.200 % |
135000 psi @Strain 0.200 % |
Typical |
| TIMET 8-1-1 Titanium Alloy (Ti-8Al-1Mo-1V); Annealed Sheet Industry Specifications: USA Aerospace: AMS 4915,4916. France: T-A8DV. Features: Designed for creep resistance up to 450°C, used primarily in engine applications such as forged compressor blades.. |
|||
| Tensile Strength, Yield | 930 MPa @Strain 0.200 % |
135000 psi @Strain 0.200 % |
Typical |
| TIMET TIMETAL® 834 (Ti-5.8Al-4Sn-3.5Zr-0.7Nb-0.5Mo-0.35Si-0.06C) Titanium Alloy High-Strength, High Temperature, Creep Resistant AlloyIndustry Specifications: France: T-A6EZ r4Nb.Features: TIMETAL 834 is a near alpha titanium alloy offering increased tensile strength and creep.. |
|||
| Tensile Strength, Yield | 931 MPa | 135000 psi | |
| Wingate Alloys Winco Heat Treated, High Tensile Alloy Steel for Maintenance and Machine Repair Electric furnace grade alloy steel in small heats for superior quality control.Winco is a well balanced machinable alloy made to strict specifications for maximum efficiency under extremely hard usa.. |
|||
| Tensile Strength, Yield | 931 MPa | 135000 psi | |
| Wingate Alloys Winco TGP Turned, Ground and Polished Heat-Treated High Tensile Alloy Steel Advantages:Turned, ground and polished to precision sizes so it is extremely accurate as to straightness and finish – almost ready for immediate installation.Will withstand shock and vibration to p.. |
|||
| Tensile Strength, Yield | >= 931 MPa | >= 135000 psi | 0.2% Offset |
| Eagle Brass 301 Austenitic Stainless Steel, 3/4 Hardened Type 301 is a chromium-nickel stainless steel that provides high strength and good ductility with chromium and nickel contents lowered to increase the work hardening range. This permits higher tens.. |
|||
| Tensile Strength, Yield | >= 931 MPa | >= 135000 psi | 0.2% Offset |
| Eagle Brass 302 Austenitic Stainless Steel, 3/4 Hardened Types 302 is a widely used variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled.Information provided by Eagle Brass Compa.. |
|||
| Tensile Strength, Yield | >= 931 MPa | >= 135000 psi | 0.2% Offset |
| Eagle Brass 304L Austenitic Stainless Steel, 3/4 Hardened Type 304L is a very common variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled. Lower carbon 304L minimizes chromium ca.. |
|||
| Tensile Strength, Yield | >= 931 MPa | >= 135000 psi | 0.2% Offset |
| Eagle Brass 316 Austenitic Stainless Steel, 3/4 Hardened The Mo addition increases general corrosion resistance to pitting from chloride ion solutions, and provides increased strength at elevated temperatures. Properties are similar to those of Type 304 .. |
|||
| Tensile Strength, Yield | >= 931 MPa | >= 135000 psi | 0.2% Offset |
| Eagle Brass 316L Austenitic Stainless Steel, 3/4 Hardened Type 316L is an extra-low carbon version of Type 316 that minimizes carbide precipitation. Typical uses include exhaust manifolds, furnace parts, heat exchangers, jet engine parts, pharmaceutical a.. |
|||
| Tensile Strength, Yield | >= 931 MPa | >= 135000 psi | 0.2% Offset |
| Eagle Brass 304 Austenitic Stainless Steel, 3/4 Hardened Types 304 is a widely used variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled.Information provided by Eagle Brass Compa.. |
|||
| Tensile Strength, Yield | 930 MPa @Strain 0.200 % |
135000 psi @Strain 0.200 % |
|
| Carpenter BioDur™ CCM® Medical Implant Alloy, Warm Worked Data provided by Carpenter Technology Corporation.Medical Implant Alloy. Non-magnetic Co-Cr-Mo alloy exhibiting high strength, corrosion resistance, and wear resistance. BioDur Carpenter CCM alloy.. |
|||
| Tensile Strength, Yield | 931 MPa @Strain 0.200 % |
135000 psi @Strain 0.200 % |
|
| ATI Allegheny Ludlum AL 13-8™ H 1100 Precipitation Hardening Alloy Characteristics: excellent strength, high hardness, superior toughness, good corrosion resistance, good transverse toughness properties, strength and ductility can be tailored by varying the aging t.. |
|||
| Tensile Strength, Yield | 931 MPa | 135000 psi | |
| ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 302, 40% Cold Rolled (UNS S30200) This alloy is one of the most familiar and most frequently used alloy in the stainless steel family. It may be best used in applications where the following properties are important: resistance to .. |
|||
| Tensile Strength, Yield | 931 MPa | 135000 psi | |
| ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 304L, 40% Cold Rolled (UNS S30403) This alloy is one of the most familiar and most frequently used alloy in the stainless steel family. It may be best used in applications where the following properties are important: resistance to .. |
|||
| Tensile Strength, Yield | 931 MPa | 135000 psi | |
| ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 305, 50% Cold Rolled (UNS S30500) This alloy is one of the most familiar and most frequently used alloy in the stainless steel family. It may be best used in applications where the following properties are important: resistance to .. |
|||
| Tensile Strength, Yield | >= 931 MPa @Strain 0.200 % |
>= 135000 psi @Strain 0.200 % |
|
| ATI Allegheny Ludlum Stainless Steel Type 301, 3/4 Hard (UNS S30100) Allegheny Ludlum Type 301 is a high strength grade of steel available in six conditions or tempers, its resistance to atmosphere corrosion and its bright, attractive surface make it an excellent cho.. |
|||
| Tensile Strength, Yield | 931 MPa | 135000 psi | |
| ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 304, 40% Cold Rolled (UNS S30400) This alloy is one of the most familiar and most frequently used alloy in the stainless steel family. It may be best used in applications where the following properties are important: resistance to .. |
|||
| Tensile Strength, Yield | 930 MPa @Strain 0.200 % |
135000 psi @Strain 0.200 % |
|
| Carpenter BioDur™ CCM Plus™ Medical Implant Alloy, Hot Worked Data provided by Carpenter Technology Corporation.Medical Implant Alloy. Non-magnetic Co-Cr-Mo alloy exhibiting high strength, corrosion resistance, and wear resistance. BioDur CCM Plus alloy is a.. |
|||