Polymer Property : Tensile Strength, Yield = 112000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	772 MPa	112000 psi
Meehanite K-325 Austempered Ductile Iron Type K-325 is used for applications such as gears requiring high contact rolling and tooth bending fatigue properties. Type K-325 also possess high fracture toughness impact strength. Excellent fo..
Tensile Strength, Yield	770 MPa	112000 psi	Typical, 1/2 t
Industeel SUPERELSOÂ® 690CR Quenched and Tempered High Strength Steel for Leg Components of Jack-up Rigs SuperelsoÂ® 690 CR (SE 690 CR) is a 690MPa (100ksi) yield strength quenched and tempered steel adapted for jack-up rig legs of offshore drilling platforms. SuperelsoÂ® 690 CR is manufactured via..
Tensile Strength, Yield	770 MPa @Strain 0.200 %, Temperature 650 Â°C	112000 psi @Strain 0.200 %, Temperature 1200 Â°F
Haynes Waspaloyâ„¢ alloy, sheet Age-hardenable superalloy with very good strength at temperatures up 980Â°C (1800Â°F), can be cold-formed in the annealed condition, may also be hot formed at 1040Â°C (1900Â°F) and above, go..
Tensile Strength, Yield	770 MPa @Strain 0.200 %, Temperature 760 Â°C	112000 psi @Strain 0.200 %, Temperature 1400 Â°F
Haynes Waspaloyâ„¢ alloy, sheet Age-hardenable superalloy with very good strength at temperatures up 980Â°C (1800Â°F), can be cold-formed in the annealed condition, may also be hot formed at 1040Â°C (1900Â°F) and above, go..
Tensile Strength, Yield	770 MPa @Strain 0.200 %	112000 psi @Strain 0.200 %	Precipitation Hardened. Value at room temperature
Special Metals NIMONICÂ® Alloy 105 A precipitation-hardenable nickel-cobalt-chromium alloy with an addition of molybdenum for solid-solution strengthening. The relatively high aluminum content enhances both strength (through greater..
Tensile Strength, Yield	774 MPa @Temperature 175 °C	112000 psi @Temperature 347 °F	Material as cured
Hexcel® HexPly® 922-1/35%/G926 180°C Curing Epoxy Matrix 5H satin/370g/m2 carbon fabric: FVC=60%Information provided by HexCel
Tensile Strength, Yield	775 MPa	112000 psi
Elgiloy® Co-Cr-Ni Alloy, Strip, 20% Cold Reduction The strength, elongation, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, fati..
Tensile Strength, Yield	773 MPa @Strain 0.200 %, Temperature 649 °C	112000 psi @Strain 0.200 %, Temperature 1200 °F
Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Double Aged 732°C/8hr/FC to 621°C/8hr/AC Data provided by Carpenter Technology Corporation.Custom Age 625 PLUS® alloy is a precipitation hardenable, nickel-base alloy which, in many environments, displays corrosion resistance similar to t..