Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 79.0 MPa | 11500 psi | ASTM D638 |
Nylene® 400 Nylon 6, Extrusion Grade Film Grade. Extrusion grade. Nylene 400 is a very low viscosity, extrusion grade nylon 6 resin suitable for specialty fibers. Also, the low viscosity allows for ease of mixing in compounding appli.. |
|||
Tensile Strength, Yield | 79.3 MPa | 11500 psi | ASTM D638 |
PTS PPE/Nylon Alloy 10% Glass Filled Information provided by PTS LLC. |
|||
Tensile Strength, Yield | 79.3 MPa | 11500 psi | ASTM D638 |
Ravago Manufacturing Americas Hylex® P1025G10 HB Polycarbonate, 10% Glass Reinforced Information provided by Ravago. |
|||
Tensile Strength, Yield | 79.3 MPa | 11500 psi | ASTM D638 |
Ravago Manufacturing Americas Hylon® N2000HL Nylon 6 (DAM) Information provided by Ravago. |
|||
Tensile Strength, Yield | 79.0 MPa | 11500 psi | 2 in/min; ASTM D638 |
BASF Capron® 8202 NL Nylon 6 (DAM)
(discontinued **) Information provided by BASF Corporation.Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line. |
|||
Tensile Strength, Yield | 79.4 MPa @Thickness 3.20 mm |
11500 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
LG Chemical LUMID GP1100A(W) PA6, Low Viscosity Feature: Injection Molding, PA6, Low ViscosityApplication: Industrial Material, Sport PartsCAS No. 25038-54-4Information provided by LG Chemical |
|||
Tensile Strength, Yield | 79.4 MPa @Thickness 3.20 mm |
11500 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
LG Chemical LUMID GP3200B(W) PA66+MF20%, General Purpose Feature: Injection Molding, PA6+MF20%, General PurposeApplication: E&E (Rice Cooker Housing)Information provided by LG Chemical |
|||
Tensile Strength, Yield | 79.3 MPa | 11500 psi | ASTM D638 |
Lord Adhesives Thermosetâ„¢ EP-809 Ignition Coil Impregnating and Encapsulation Epoxy Lord EP-809 is a long working life, heat curing, two component epoxy formulation. It was designed especially for potting high voltage automotive ignition coils. The combination of low viscosity, exc.. |
|||
Tensile Strength, Yield | 79.3 MPa | 11500 psi | 2.0 in/min; ASTM D638 |
LTL Color Compounds ColorFast® PCGF120 Polycarbonate, 20% Glass-Filled 20% glass-filled grade, good balance of impact and mechanical propertiesAll information provided by LTL Color Compounders, Inc. |
|||
Tensile Strength, Yield | 79.0 MPa | 11500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RX05487 PA 66 LNP* LUBRICOMP* RX05487 is a compound based on Nylon 66 containing 10% Aramid Fiber, 10% Lubricant. Added features of this material are: Low Warpage, Wear Resistant. |
|||
Tensile Strength, Yield | 79.3 MPa | 11500 psi | ASTM D638 |
Techmer ES Electrablend® PA6/6 C BK Availability: North AmericaForms: PelletsFiller/Reinforcement: Unspecified Filler/Reinfor.Features: ConductiveAppearance: BlackInformation provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 79.3 MPa | 11500 psi | ASTM D638 |
Techmer ES Electrablend® PA6/PC Availability: North AmericaForms: PelletsFiller/Reinforcement: Unspecified Filler/Reinfor.Features: Conductive Appearance: BlackInformation provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 79.3 MPa | 11500 psi | ASTM D638 |
Techmer ES HiFill® PA6 E U Availability: North AmericaForms: PelletsFeatures: General PurposeProcessing Method: ExtrusionTPCI# 9777102Information provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 79.3 MPa | 11500 psi | ASTM D638 |
Techmer ES HiFill® PA6/6 GF10 TL10 BK 10% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 10% Filler by Weight Additive: Heat Stabilizer and PTFE Lubricant(10%)Features: Lubricated and Heat Stabiliz.. |
|||
Tensile Strength, Yield | 79.0 MPa | 11500 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL NH5020 PPE+PS Noryl* NH5020 Resin is an unreinforced blend of Polyphenylene Ether(PPE) + Polystyrenre resin. The material offers a good balance of heat, flow, hydrolytic stability, and non-halogenated flame reta.. |
|||
Tensile Strength, Yield | 79.0 MPa | 11500 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL NH5020 PPE+PS (Asia Pacific) Noryl* NH5020 Resin is an unreinforced blend of Polyphenylene Ether(PPE) + Polystyrenre resin. The material offers a good balance of heat, flow, hydrolytic stability, and non-halogenated flame reta.. |
|||
Tensile Strength, Yield | 79.0 MPa | 11500 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL NH5020 PPE+PS (Europe-Africa-Middle East) Noryl* NH5020 Resin is an unreinforced blend of Polyphenylene Ether(PPE) + Polystyrenre resin. The material offers a good balance of heat, flow, hydrolytic stability, and non-halogenated flame reta.. |
|||
Tensile Strength, Yield | 79.3 MPa | 11500 psi | ASTM D638 |
Techmer ES Electrablend® PA6 C BK Availability: North AmericaForms: PelletsFiller/Reinforcement: Unspecified Filler/Reinfor.Features: ConductiveAppearance: BlackInformation provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 79.0 MPa | 11500 psi | Nominal Stress, yld, Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL GTX EXNX0080 PPE+PPS Noryl APS* EXNX0080 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can.. |
|||
Tensile Strength, Yield | 79.0 MPa | 11500 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL N1250 PPE+HIPS (Asia Pacific) Noryl* N1250 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and good flow , this resin also uses non-chlorinated, non-brominated FR ad.. |
|||
Tensile Strength, Yield | 79.0 MPa | 11500 psi | 2 in/min; ASTM Test |
BASF Ultramid® 8202 PA6 (Dry) Ultramid 8202 is a low viscosity, general purpose polyamide 6 injection molding homopolymer exhibiting excellent melt fluidity for filling thin sections. It is also available in heat stabilized (Ult.. |
|||
Tensile Strength, Yield | 79.0 MPa | 11500 psi | 50mm/min; ISO 527 |
BASF Ultramid® B3S Q661 PA6 (Dry) Ultramid B3S Q661 is a general purpose, PA6 resin for injection molding. |
|||
Tensile Strength, Yield | 79.0 MPa | 11500 psi | 2 in/min; ASTM Test |
BASF Ultramid® B3S Q661 PA6 (Dry) Ultramid B3S Q661 is a general purpose, PA6 resin for injection molding. |
|||
Tensile Strength, Yield | 79.0 MPa | 11500 psi | Dry; ASTM D638 |
Asahi Kasei Leona® 1300S Nylon 66 General purpose grade. Good balance of flowability and mechanical properties.Applications:Connectors, washers, cable ties. Information provided by Asahi Kasei |
|||
Tensile Strength, Yield | 79.0 MPa | 11500 psi | ASTM D638 |
Ashley Polymers Ashlene® 833 Nylon 6 Basic Nylon 6 medium viscosity, with high residual monomer. Highly flexible and high strength, particularly suited for monofilament extrusion.Data provided by the manufacturer |
|||
Tensile Strength, Yield | 79.0 MPa | 11500 psi | ASTM D638 |
Ashley Polymers Ashlene® 835 Nylon 6 Basic Nylon 6 high viscosity, for coating and laminating applications, FDA approved.Data provided by the manufacturer |
|||
Tensile Strength, Yield | 79.3 MPa | 11500 psi | ASTM D638 |
LNP Konduit® ITF-212-11 Polyamide 6/12 Copolymer
(discontinued **) Features: Thermally ConductiveForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades ar.. |
|||
Tensile Strength, Yield | 79.3 MPa | 11500 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
PolyOne Edgetek® AT-25GF-10MN/000 BLASCK Acetal-Copolymer, Glass/Mineral Filled
(discontinued **) Description/Features:Glass/Mineral ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
Tensile Strength, Yield | 79.3 MPa | 11500 psi | 2.0 in/min; ASTM D638 |
LTL Color Compounds ColorFast® NY1 Nylon 6 Injection molding nylon 6, with or without lubeAll information provided by LTL Color Compounders, Inc. |