Polymer Property : Tensile Strength, Yield = 11600 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	80.0 MPa	11600 psi	Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Lexan® DMX2415 PC (Asia Pacific) Lexan* DMX2415 is a polycarbonate resin with improved scratch resistance. Lexan* DMX2415 is available in transparent, translucent, and opaque colors.This data was supplied by SABIC-IP for the Asia P..
Tensile Strength, Yield	80.0 MPa	11600 psi	Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Lexan® DMX9455 PC Copolymer (Europe-Africa-Middle East) Lexan* DMX9455 is a standard flow, flame retardant, V0/1.5mm, opaque polycarbonate copolymer resin with improved scratch resistance.This data was supplied by SABIC-IP for the Europe-Africa-Middle Ea..
Tensile Strength, Yield	80.0 MPa	11600 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® DMX9455 PC Copolymer (Europe-Africa-Middle East) Lexan* DMX9455 is a standard flow, flame retardant, V0/1.5mm, opaque polycarbonate copolymer resin with improved scratch resistance.This data was supplied by SABIC-IP for the Europe-Africa-Middle Ea..
Tensile Strength, Yield	80.0 MPa	11600 psi	Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Lexan® DMX9455A PC Copolymer Lexan* DMX9455A is a standard flow, flame retardant, transparent polycarbonate copolymer resin with improved scratch resistance.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength, Yield	80.0 MPa	11600 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® DMX1435 PC Copolymer (Asia Pacific) This product will be phased out per January 2015 -- Lexan* DMX1435 is a UV stabilized standard flow polycarbonate copolymer resin with improved scratch resistance.
Tensile Strength, Yield	80.0 MPa	11600 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® DMX9455A PC Copolymer (Asia Pacific) This product will be phased out per January 2015 -- Lexan* DMX9455A is a standard flow, flame retardant, transparent polycarbonate copolymer resin with improved scratch resistance.
Tensile Strength, Yield	80.0 MPa	11600 psi	ASTM D 638
SABIC Innovative Plastics LNP Lubricomp DFI12E PC LNP* Lubricomp* DFI12E is a compound based on Polycarbonate resin containing Glass Fiber, Silicone. Added features of this material include: Internally Lubricated, Easy Molding.This data was suppli..
Tensile Strength, Yield	80.0 MPa	11600 psi	2 in/min; ASTM D638
BASF Capron® B73QP Nylon 6 (DAM) (discontinued **) Information provided by BASF Corporation.Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line.
Tensile Strength, Yield	80.0 MPa	11600 psi	ISO 527-1/-2
Kuraray Genestarâ„¢ N1002A-M41 Nylon Low friction unreinforced injection grade. Main Features:Low friction coefficientLow wearExamples of applications are:Friction and wear applicationGear and wheel
Tensile Strength, Yield	80.0 MPa	11600 psi	ISO 527-1/-2
Lanxess DurethanÂ® AC 30 000000 Nylon 66 PA 66, injection molding-grade, non-reinforced, higher notched impact strength than A 30 / A 31 in the dry and conditioned stateApplication Examples: plug connectors, cable binders, cable clips, par..
Tensile Strength, Yield	80.0 MPa	11600 psi	ISO 527-1/-2
Lanxess DurethanÂ® BM 25 FN20 700350 Nylon 6, 25% Mineral PA 6, injection molding grade, 25% mineral, UL94V-2 off 0.75 mm, max. temp. glow wire test:960Â°C off 0.8 mm, free from halogen
Tensile Strength, Yield	80.0 MPa	11600 psi	ISO 527-1/-2
Lanxess DurethanÂ® CI 31 F 000000 Copolyamide PA6/6I Copolyamide PA6/6I, low melt point (188-191Â°C), low viscosity, no additives, very high transparency, in compliance with FDA as far as the PA-layer is separated from the food by a 50 Âµm PE film..
Tensile Strength, Yield	80.0 MPa	11600 psi	ISO 527 type 1 A
Solvay TECHNYLÂ® B 50 H1 PA66/6, DRY Description: TECHNYLÂ® B 50H1 is an unreinforced melamine cyanurate flame retarded copolyamide 66/6. This product has been heat stabilized and is suitable for injection molding. This product is av..
Tensile Strength, Yield	80.0 MPa	11600 psi	ISO-DIS 527
Schwartz Technical Plastics LAMIGAMIDÂ® 317 Cast Polyamide 6, Heat Stabilized, Dry Application: coupling parts, sealing rings, bearingsInformation provided by Schwartz Technical Plastics GmbH
Tensile Strength, Yield	80.0 MPa	11600 psi	5 mm/min; ISO 527
SABIC Innovative Plastics NORYL IGN5531 PPE+PS (Europe-Africa-Middle East) Noryl* IGN5531 is an 20% glass fiber reinforced, injection moldable grade. This modified polyphenylene ether resin is designed to deliver a balance of heat, strength and electrical properties. Nor..
Tensile Strength, Yield	80.0 MPa	11600 psi	ISO-DIS 527
Schwartz Technical Plastics OPTAMIDÂ® Cast Polyamide 6, Dry Application: deflection rope sheaves for elevatorsInformation provided by Schwartz Technical Plastics GmbH
Tensile Strength, Yield	80.0 MPa	11600 psi	ASTM D638
PlastxWorld Veroplas PB5300 Nylon 66 general purpose, 30% mineral filled injection molding gradeInformation provided by PlastxWorld Inc.
Tensile Strength, Yield	80.0 MPa	11600 psi	ISO 527-2
Tisan TISLAMID® 66 Flame Retardant (V0). Heat Stabilized Nylon 66 TISLAMID has a wide area of application in electric/electronic, automotive, durable goods and telecommunications industries. It demonstrates characteristics such as Excellent chemical resistanceElec..
Tensile Strength, Yield	80.0 MPa	11600 psi
Hexcel® HexPly® F155 Epoxy Resin HexPly® F155 is an advanced modified epoxy formulation designed for autoclave curing to offer very high laminate strengths, coupled with increased fracture toughness and adhesive properties. HexPly..
Tensile Strength, Yield	80.0 MPa	11600 psi	ISO 527
Polyram Polytron P20B03 Polypropylene, 20% Long Glass Fiber A chemically coupled 20% long glass fibers reinforced black polypropylene, heat stabilized for injection molding applications.Information provided by Polyram.
Tensile Strength, Yield	80.0 MPa	11600 psi	ASTM D638
Covestro Makrolon® 9415(Z) Polycarbonate Medium viscosity, flame retardant extrusion and injection molding grade with 10% standard glass fibers and easy mold release agent.Information provided by Bayer.As of 1 September 2015, Bayer Materia..
Tensile Strength, Yield	80.0 MPa	11600 psi	dry; ISO 527-1/-2
DSM Novamid® 1011CH5KR PA6 Heat Stabilized, Easy Molding Grade
Tensile Strength, Yield	80.0 MPa	11600 psi	ASTM D638
Cresset Powers Cress-Alon™ A3000 3.0 r.v. Film or Extrusion Grade Nylon 6, Dry As Molded Neat resin, for film or extrusion.Information provided by Cresset Powers Ltd.
Tensile Strength, Yield	80.0 MPa	11600 psi	ISO 527
Eurotec® Tecomid® NA40 NL XA70 PA6.6, unfilled, flame retardant - halogen free (RoHS compliant), heat stabilized, natural Information provided by Eurotec®
Tensile Strength, Yield	80.0 MPa	11600 psi	v = 50 mm/min; ISO 527-2
CENTROPLAST CENTRO HPM Polysulfone This plastic has good hydrolysis, chemical and radiation resistance, and can operate at high temperatures. It is used in food processing industry, pumps and valves, and medical equipment.Informatio..
Tensile Strength, Yield	80.0 MPa	11600 psi	dry; ISO 527
Azoty Tarnow™ Tarnamid® T-27 MCS Polyamide 6 - Colored Medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.For colored parts produced by injection molding.Tarnamid® has the following ..
Tensile Strength, Yield	80.0 MPa	11600 psi	ISO 527
Eurotec® Tecomid® NB40 NL RM PA 6 low friction and wear Excellent stiffness/toughness balanceHigh mechanical strengthVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance and low frictionVery good..
Tensile Strength, Yield	80.0 MPa	11600 psi	ISO 527-2
Ascend Performance Materials Vydyne® 75HF Nylon 66/6, Heat Stabilized, DAM Vydyne® 75HF is a medium-high-viscosity, heat-stabilized PA66/6 copolymer resin designed for extrusion applications. It is available in natural color only. Vydyne 75HF resin offers a well-balanced ..
Tensile Strength, Yield	80.0 MPa	11600 psi	ISO 527
BASF Nypel® 2314 HS BK6 PA6 (Dry) Description: Nypel® 2314 HS BK6 is a black pigmented, low viscosity, heat stabilized, semi crystalline, injection molding compound based on recycled PA6 feedstocks. It also offers the following: go..
Tensile Strength, Yield	80.0 MPa	11600 psi	DAM; ISO 527 Type 1 A
Solvay Technyl® A 402 H1 Nylon 66 Unreinforced, very high viscosity, heat stabilized, for extrusion and injection molding. TECHNYL® A 402 H1 offers three main advantages: high impact resistance at low humidity levels, good rigidit..