Polymer Property : Tensile Strength, Yield = 116000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	800 - 1050 MPa	116000 - 152000 psi	Swaged after Sintering
MarkeTech 96-3-1 Tungsten Alloy, AMS-T-21014 Class 3 Used to fabricate parts to near net size and several processes to produce high quality tungsten based materials.Tungsten heavy alloys have very high melting point and have a density twice that of st..
Tensile Strength, Yield	799 MPa @Strain 0.200 %	116000 psi @Strain 0.200 %
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079Â°C, water quenched, 30 minutes at 1066Â°C, air cooled, aged 16 hours at 760Â°C (1400Â°F) Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Tensile Strength, Yield	800 MPa @Strain 0.200 %, Temperature 371 Â°C	116000 psi @Strain 0.200 %, Temperature 700 Â°F	13"x11"
Latrobe LescalloyÂ® 6305 VAC-ARC ; High Strength Alloy Steel LESCALLOY 6305 VAC-ARC steel is a modified 4140 steel with higher molybdenum and a vanadium addition. The alloy steel is generally used in the 160/180,000 psi tensile strength range obtained with a..
Tensile Strength, Yield	800 MPa @Strain 0.200 %, Temperature 550 Â°C	116000 psi @Strain 0.200 %, Temperature 1020 Â°F	Precipitation Hardened prior to test
Special Metals NIMONICÂ® Alloy 901 A nickel-iron-chromium alloy containing titanium and aluminum for precipitation hardening and molybdenum for solid-solution strengthening. The alloy has high yield strength and creep resistance at ..
Tensile Strength, Yield	800 MPa	116000 psi	ISO 527
Styrolution AbsolanÂ® 2500 SAN Absolac 2500 is a heat and chemical resistant gradeInformation provided by Styrolution
Tensile Strength, Yield	>= 800 MPa @Strain 0.200 %	>= 116000 psi @Strain 0.200 %
TIMET TIMETAL® 367 (Ti-6Al-7Nb) Titanium Alloy Medium-Strength Surgical Implant AlloyFeatures: TIMETAL 367 is a dedicated, medium strength, titanium alloy for surgical implants. The alloy was developed specifically for the manufacture of femora..
Tensile Strength, Yield	800 MPa @Strain 0.200 %, Temperature 20.0 °C	116000 psi @Strain 0.200 %, Temperature 68.0 °F	Longitudinal Tests from 3" rolled plate at 293 HB
EDRO P1FM #31 Free Machining Holder Steel EDRO #31 P1-FM is a free machining low alloy steel supplied prehardened to 262-321 HB.P1-FM is characterized by excellent machinability, uniform and consistent hardness in all dimensions, good resis..
Tensile Strength, Yield	>= 800 MPa @Strain 0.200 %	>= 116000 psi @Strain 0.200 %
CLAL-MSX NICLAFOR® 1000 TDX Quenched/Cold Rolled, Drawn Copper Alloy Finished parts can be produced with: reduction in sections, high mechanical properties even at high temperature, high spring properties, high conductivity, good resistance to corrosion, low permeabi..
Tensile Strength, Yield	>= 800 MPa @Strain 0.200 %	>= 116000 psi @Strain 0.200 %
CLAL-MSX NICLAFOR® 1000 TH2 Quenched/Precipitation Heat Treated, Drawn Copper Alloy Finished parts can be produced with: reduction in sections, high mechanical properties even at high temperature, high spring properties, high conductivity, good resistance to corrosion, low permeabi..
Tensile Strength, Yield	>= 800 MPa @Strain 0.200 %	>= 116000 psi @Strain 0.200 %
CLAL-MSX NICLAFOR® 1000 TH3 Quenched/Cold Rolled/Precipitation Heat Treated, Rolled Copper Alloy Finished parts can be produced with: reduction in sections, high mechanical properties even at high temperature, high spring properties, high conductivity, good resistance to corrosion, low permeabi..
Tensile Strength, Yield	800 MPa @Strain 0.200 %	116000 psi @Strain 0.200 %	68°F (hardened to 310 HB)
Bohler-Uddeholm HOLDER Pre-hardened Holder Tool Steel Chromium-molybdenum alloyed steelA pre-hardened steel with very good machinability supplied at ~300 HB for clamping and holding plates and blocks.Holder is characterized by: Excellent machinability..
Tensile Strength, Yield	800 MPa @Strain 0.200 %, Temperature 232 °C	116000 psi @Strain 0.200 %, Temperature 450 °F
Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Double Aged 732°C/8hr/FC to 621°C/8hr/AC Data provided by Carpenter Technology Corporation.Custom Age 625 PLUS® alloy is a precipitation hardenable, nickel-base alloy which, in many environments, displays corrosion resistance similar to t..
Tensile Strength, Yield	800 - 950 MPa	116000 - 138000 psi
ArcelorMittal Complex Phase Steel 1000 Very high strength steel, Hot Rolled Steel Available in the following: Extragal®/Galvannealed (HCT950C+Z)Description: The Complex Phase family of steels supplements ArcelorMittal's VHSS (very high strength steel) product range. These steels..
Tensile Strength, Yield	800 - 950 MPa	116000 - 138000 psi
ArcelorMittal Complex Phase Steel 1000 Y800 Very high strength steel, Cold Rolled Steel Description: The Complex Phase family of steels supplements ArcelorMittal's VHSS (very high strength steel) product range. These steels are cold formed to make lightweight structural elements. A num..
Tensile Strength, Yield	798 MPa @Treatment Temp. 649 °C, Time 360000 sec	116000 psi @Treatment Temp. 1200 °F, Time 100 hour	0.2%. Room temp test after thermal exposure
Haynes 282® Nickel Alloy Plate, Solution Annealed and Age-Hardened, after long term high temperature exposure Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and land-b..