Polymer Property : Tensile Strength, Yield = 172 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	55.8 - 172 MPa	8100 - 24900 psi	Average value: 79.1 MPa Grade Count:46
Overview of materials for Polycarbonate, Glass Fiber Filled, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Glass Fiber Filled, Flame Retardant". Each property range of values reported is minimum a..
Tensile Strength, Yield	89.6 - 172 MPa	13000 - 25000 psi	0.2% offset
Eagle Brass 706 Copper Nickel 10%, Annealed 706 exhibits excellent corrosion resistance, especially in marine applications. It has a relatively high strength and has resistance at elevated temperatures. The cost is relatively high compared to..
Tensile Strength, Yield	124 - 172 MPa	18000 - 25000 psi	0.2% offset
Eagle Brass 725 Copper Nickel Tin, Annealed Alloy C725 is a moderate strength, low conductivity alloy with excellent bare solderability and corrosion resistance. Applications include electronic parts, springs, connectors and wire wrap termina..
Tensile Strength, Yield	103 - 172 MPa	15000 - 25000 psi
Chicago Extruded Metals UNS C33500 Copper-Zinc-Lead Alloy Copper-Zinc-Lead Alloy (Leaded Brass)Finished product available in bars.Chicago Extruded Metal temper codes: H01, H02Information provided by Chicago Extruded Metals
Tensile Strength, Yield	103 - 172 MPa	15000 - 25000 psi
Chicago Extruded Metals UNS C34000 Copper-Zinc-Lead Alloy Copper-Zinc-Lead Alloy (Leaded Brass)Finished product available as bar or rod.Chicago Extruded Metal temper codes: H01, H02Information provided by Chicago Extruded Metals
Tensile Strength, Yield	103 - 172 MPa	15000 - 25000 psi
Chicago Extruded Metals UNS C35000 Copper-Zinc-Lead Alloy Copper-Zinc-Lead Alloy (Leaded Brass)Finished product available as bar or rod.Chicago Extruded Metal temper codes: H01, H02, H04Information provided by Chicago Extruded Metals
Tensile Strength, Yield	103 - 172 MPa	15000 - 25000 psi
Chicago Extruded Metals UNS C35300 Copper-Zinc-Lead Alloy Copper-Zinc-Lead Alloy (Leaded Brass)Finished product available as bar or rod.Chicago Extruded Metal temper codes: H01, H02, H04Information provided by Chicago Extruded Metals
Tensile Strength, Yield	124 - 172 MPa @Strain 0.200 %	18000 - 25000 psi @Strain 0.200 %	Annealed Sheet
ATI Wah Chang Vanadium Vanadium is widely dispersed in the earths crust occurring in many types of deposits. Most vanadium is currently obtained as a by-product or co product from titanomagnetites, petroleum, uranium ores..