Polymer Property : Tensile Strength, Yield = 2100 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	14.5 MPa	2100 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Wire & Cable 1725-xx13FRD Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne
Tensile Strength, Yield	14.5 MPa	2100 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Wire & Cable JAB40L Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications. Provisional Product Information - Physical and Mechanical properties based on initial production.Information provide..
Tensile Strength, Yield	14.5 MPa	2100 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Wire & Cable WEJB400L Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne
Tensile Strength, Yield	14.5 MPa	2100 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Wire & Cable WJAX204L Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications. Provisional Product Information - Physical and Mechanical properties based on initial production.Information provide..
Tensile Strength, Yield	14.5 MPa	2100 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Wire & Cable WJAX204V Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne
Tensile Strength, Yield	14.5 - 59.0 MPa	2100 - 8560 psi	Average value: 33.1 MPa Grade Count:48
Overview of materials for Polystyrene, Molded, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene". Each property range of values reported is minimum and maximum values of appropriate MatWeb..
Tensile Strength, Yield	14.5 MPa	2100 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 120 PHR N990 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	14.5 MPa	2100 psi	20"/min; ASTM D638
LyondellBasell PetrotheneÂ® GA574189 Linear Low Density Polyethylene, Injection Molding Grade PETROTHENE GA574189 exhibits excellent flow and impact with good stiffness. Typical applications include lids, closures, containers, housewares and medical items.Regulatory Status: GA574189 meets th..
Tensile Strength, Yield	14.5 MPa	2100 psi	ASTM D638
I. Stern 550 High Impact Polystyrene Features:Good process propertiesExcellent toughness and environmental stress crackingApplicationsStructural foamDisplaysSmall appliancesAgency RatingsFDA Title 21 CFR 177.1640UL File E220962Informat..
Tensile Strength, Yield	14.5 MPa	2100 psi	Molded; ASTM D638
LyondellBasell PetrotheneÂ® NA940094 Low Density Polyethylene (Film Grade) ApplicationsPETROTHENE NA 940 is a series of resins designed for heavy duty film applications. Superior puncture resistance combined with excellent impact properties make NA 940 an ideal choice for..
Tensile Strength, Yield	14.5 MPa	2100 psi
Spartech E65070 General Purpose PVC First choice for compounds meeting the stringent requirements of Spiral Hose, Automotive, Housewares, Farm Equipment, Coated Fencing and numerous other applications including Lawn & Garden Wheels. B..
Tensile Strength, Yield	14.5 MPa	2100 psi	ASTM D412
Teknor Apex APEXÂ® 3211-85 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMUses-Automotive Applications, Non-specific Food Applications, General Purpose, Medical Applications, Modeling..
Tensile Strength, Yield	14.5 MPa	2100 psi	100%; ASTM D412
Teknor Apex APEXÂ® 3301-90 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTM Uses-Automotive Applications, Food Service Applications, General Purpose, Medical Applications, Profiles, To..
Tensile Strength, Yield	14.5 MPa	2100 psi	ASTM D412-92
Saint-Gobain TransflowÂ® M-34-R Raw Milk Tubing Formulation Description: TransflowÂ M-34-R: TransflowÂ Raw Milk tubing is specially formulated to reduce the risks that can occur with the use of rubber tubings. Many regulatory sanitarians throughout the w..
Tensile Strength, Yield	14.5 MPa	2100 psi
Trelleborg R480 Commercial Natural Rubber Polyisoprene All information provided by Trelleborg
Tensile Strength, Yield	14.5 MPa	2100 psi	heat aged 70 hours at 300ºF
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 60 PHR N330 (HAF) Black MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c..
Tensile Strength, Yield	14.5 MPa	2100 psi	ASTM D638
Borealis Low Sulfur™ LE0594 Crosslinkable Semiconductive Compound for Shielding of Power Cables Low Sulphur LE0594 is designed for use as a conductor and bonded insulation shield for medium and high voltage cables. LE0594 is a peroxide crosslinkable compound and is specifically intended to me..
Tensile Strength, Yield	14.5 MPa	2100 psi	2"/min; ASTM D638
A. Schulman POLYAXIS® LPA815 LPA 815EVA DescriptionPolyaxis LPA 815 is an EVA which is soft an pliable, even at low temperatures.NOTE: Physical properties are based on rotationally molded samples from unpigmented resin. Density and ESCR ..
Tensile Strength, Yield	14.5 MPa	2100 psi	ASTM D638
ExxonMobil LLDPE LL 5001.09 Linear Low Density Polyethylene Resin Product Description: LL 5100.09 is a linear low density polyethylene resin designed to provide good processability and ease of blending. The granular from of LL 5100.09 makes for efficient blending ..
Tensile Strength, Yield	14.5 MPa	2100 psi	ASTM D-638
Axiall 59770 Wire & Cable Flexible PVC Non-lead stabilized, 105°C rated vinyl elastomer compound suitable for SJEOW insulation and jacket applications per UL 62. UL, QMTT2 recognized for 720 hour sunlight resistance applications.Inform..
Tensile Strength, Yield	14.5 MPa	2100 psi	ASTM D-638
Axiall 8702 Moldings & Extrusions Flexible PVC General purpose, elastomeric vinyl compound well suited for co-extrusion with rigid PVC.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.
Tensile Strength, Yield	14.5 MPa	2100 psi	ASTM D-638
Axiall 10852 Wire & Cable Flexible PVC General purpose non-lead stabilized jacket compound recommended for UL 75°C applications or 80C automotive applications.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in..
Tensile Strength, Yield	14.5 MPa	2100 psi	ASTM D-638
Axiall 19810 Wire & Cable Flexible PVC Primary insulation also recommended for 105°C molding applications.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.
Tensile Strength, Yield	14.5 MPa	2100 psi	heat aged 70 hours at 300ºF
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 60 PHR N330 (HAF) Black MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c..
Tensile Strength, Yield	14.5 MPa	2100 psi	ASTM D412
Teknor Apex APEX® 3202-65 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMUses-Caps, Closure, Connectors, Food Service Applications, Safety Equipment, Valves/Valve Parts Appearance-Cl..
Tensile Strength, Yield	14.5 MPa	2100 psi
Trelleborg R406 Commercial Natural Rubber Polyisoprene All information provided by Trelleborg
Tensile Strength, Yield	14.5 MPa	2100 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 120 PHR N990 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	14.5 MPa	2100 psi	ASTM D 638
LyondellBasell Hifax™ CA207A Thermoplastic Polyolefin Elastomer Description: Hifax™ CA207A thermoplastic olefin resin is designed to reduce shrinkage and improve paint adhesion of PP compound. It is based on proprietary Basell process technology. All ingredien..
Tensile Strength, Yield	14.5 MPa	2100 psi	ASTM D412
Teknor Apex APEX® 3302-65 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTM Uses- Medical Applications, Tubing, Appearance-ClearForms-PelletsProcessing-ExtrusionInformation provided by..
Tensile Strength, Yield	14.5 MPa	2100 psi	Method A (Dumbbell & Section), 20 in/min, Break; ASTM D412
PolyOne Synprene® RT-5145D Thermoplastic Elastomer - SBC (discontinued **) Description/Features:High Performance Thermoplastic ElastomerNaturalIgnition ResistantApplications:Multi-PurposeMarket:Building and ConstructionConsumer GoodsIndustrialProcessing Method:Injection Mo..