Polymer Property : Tensile Strength, Yield = 3450 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	23.8 MPa	3450 psi	2 in per min; ASTM D638
Network Polymers NPP 25-0803 Description: Copolymer PolypropyleneInformation provided by Network Polymers Inc.
Tensile Strength, Yield	23.8 MPa	3450 psi	5.1 mm/min; ASTM D638
PolyOne Geon™ L4605 Red 7640 Polyvinyl Chloride, Semi-Rigid (PVC, Semi-Rigid) Information provided by PolyOne
Tensile Strength, Yield	23.8 MPa	3450 psi	aged in air at 100ºC for 4 days
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with Plasticizer SC MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	23.8 MPa	3450 psi	(2 in/min); ASTM D638
Phillips 66 COPYLENE® CM015 Polypropylene Impact Copolymer COPYLENE™ CM015 is low melt flow impact copolymer with a barefoot additive package and is designed for excellent processing in injection molding and extrusion applications.Applications: Injection M..
Tensile Strength, Yield	23.8 MPa	3450 psi	(2 in/min); ASTM D638
Phillips 66 COPYLENE® CM200LN-02 Polypropylene Impact Copolymer COPYLENE™ CM200LN-02 is specially designed for injection molding applications where an excellent balance of stiffness/impact and good cycle times are required.Applications: Injection molding applic..
Tensile Strength, Yield	23.8 MPa	3450 psi
TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 40 PHR N330 (HAF) Filler MILLATHANE HT is a polyester millable polyurethane which has the ability to withstand elevated temperatures. Polyurethanes have been known for their excellent resistance to abrasion, impact, tear st..
Tensile Strength, Yield	23.8 MPa	3450 psi	2 in/min (50 mm/min); ASTM D638
Ineos K44-11-128 HDPE Ineos K44-11-128 is a high molecular weight, high density polyethylene copolymer intended for large part blow molding where the finished product demands good physical performance and low color. Thi..
Tensile Strength, Yield	23.8 MPa	3450 psi	ASTM D 638
Styrolution PS 6220 HIPS Excellent toughnessHigh glossDesigned for deep draw thermoformingInformation provided by Styrolution
Tensile Strength, Yield	23.8 MPa	3450 psi	ASTM D638
Washington Penn Medium Impact Copolymer 40% Talc Filled Talc-filled polypropylene compounds have been tailored specifically to meet the requirements of each of the major automobile producers. Grades are available to meet FDA food and drug packaging requi..
Tensile Strength, Yield	23.8 MPa	3450 psi	ASTM D638
Washington Penn Medium Impact Copolymer 50% Talc Filled Talc-filled polypropylene compounds have been tailored specifically to meet the requirements of each of the major automobile producers. Grades are available to meet FDA food and drug packaging requi..
Tensile Strength, Yield	23.8 MPa	3450 psi	aged in air at 100ºC for 4 days
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with Plasticizer SC MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	23.8 MPa	3450 psi	(2 in/min); ASTM D638
Phillips 66 COPYLENE® CM015G Polypropylene Impact Copolymer COPYLENE® CM015G is low melt flow impact copolymer with a barefoot additive package and is designed for excellent processing in injection molding and extrusion applications.Applications:Injection M..
Tensile Strength, Yield	23.8 MPa	3450 psi
TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 40 PHR N330 (HAF) Filler MILLATHANE HT is a polyester millable polyurethane which has the ability to withstand elevated temperatures. Polyurethanes have been known for their excellent resistance to abrasion, impact, tear st..