Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 74.0 MPa | 10700 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Cycolac® INP562 ABS+SAN SABIC INP562 provides compatibility with a wider range of ABS grades than many color concentrate bases; allows better dispersion than pellets; allows concentrate manufacturers to produce both pellet.. |
|||
Tensile Strength, Yield | 74.0 MPa | 10700 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® 505RU PC Lexan* 505RU is a glass reinforced,flame retardant(FR)grade with non brominated and non chlorinated FR systems and UV stablization packages. This product is intended for applications to meet WEEE/Ro.. |
|||
Tensile Strength, Yield | 74.0 MPa | 10700 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® 505RU PC (Asia Pacific) Lexan* 505RU is a glass reinforced,flame retardant(FR)grade with non brominated and non chlorinated FR systems and UV stablization packages. This product is intended for applications to meet WEEE/Ro.. |
|||
Tensile Strength, Yield | 74.0 MPa | 10700 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® FST9705 PC Copolymer High viscosity Proprietary Polycarbonate Ester, OSU 55/55 compliant, low smoke, flame retardant resin |
|||
Tensile Strength, Yield | 74.0 MPa | 10700 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® FST9705 PC Copolymer (Europe-Africa-Middle East) High viscosity PC Copolymer, OSU 55/55 compliant, low smoke, flame retardant resin |
|||
Tensile Strength, Yield | 74.0 MPa | 10700 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP DFL32 PC (Europe-Africa-Middle East) LNP* Lubricomp* DFL32 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. |
|||
Tensile Strength, Yield | 74.0 MPa @Temperature 23.0 °C |
10700 psi @Temperature 73.4 °F |
ISO 527 |
DuPont Performance Polymers Delrin® 311DP BK402 Acetal Homopolymer
(Unverified Data**) Delrin® 311DP BK402 is a medium high viscosity acetal homopolymer with improved thermal stability and modifications for more precise molding(reduced warpage, less shrinkage, fewer voids).Informatio.. |
|||
Tensile Strength, Yield | 74.0 MPa @Temperature 23.0 °C |
10700 psi @Temperature 73.4 °F |
ISO 527 |
DuPont Performance Polymers Delrin® 911DP BK402 Acetal Homopolymer
(Unverified Data**) Delrin® 911DP is a low viscosity acetal homopolymer with improved thermal stability and modifications for more precise molding (reduced warpage, less shrinkage, fewer voids).Information provided by.. |
|||
Tensile Strength, Yield | 74.0 - 74.0 MPa @Temperature 80.0 - 80.0 °C |
10700 - 10700 psi @Temperature 176 - 176 °F |
Average value: 74.0 MPa Grade Count:1 |
Overview of materials for Nylon 66, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 20% Glass Fiber Filled". Specific grades with glass content between 15% and 24% are included. .. |
|||
Tensile Strength, Yield | 74.0 MPa @Strain 0.200 %, Temperature 982 °C |
10700 psi @Strain 0.200 %, Temperature 1800 °F |
|
Haynes HR-160® alloy, hot rolled and solution annealed plate Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Tensile Strength, Yield | 74.0 MPa | 10700 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP LL004C PEEK LNP* LUBRICOMP* LL004C is a compound based on Polyetheretherketone resin containing 20% PTFE. Added features of this material include: Wear Resistant, Clean Compounding System. |
|||
Tensile Strength, Yield | 74.0 MPa | 10700 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP RAL22I PA 66 LNP* LUBRICOMP* RAL22I is a compound based on Nylon 66 resin containing 10% PTFE, 10% Aramid Fiber. Added features of this material include: Wear Resistant, High Impact. |
|||
Tensile Strength, Yield | 74.0 MPa | 10700 psi | ISO-DIS 527 |
Schwartz Technical Plastics LAMIGAMID® 510 Polyethylene Terephthalate Application: friction bearings, wear linersInformation provided by Schwartz Technical Plastics GmbH |
|||
Tensile Strength, Yield | 74.0 MPa | 10700 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP UAL22S PPA LNP* LUBRICOMP* UAL22S is a compound based on Polyphthalamide resin containing 10% PTFE, 10% Aramid. Added features of this material include: Wear Resistant, Heat Stabilized. |
|||
Tensile Strength, Yield | 74.0 MPa | 10700 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP AX04518 ABS LNP* THERMOCOMP* AX04518 is a compound based on ABS resin containing proprietary filler(s). |
|||
Tensile Strength, Yield | 74.0 MPa | 10700 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp DF002L PC LNP THERMOCOMP* DF002L is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Low Extractible.This data was supplied by SABIC-IP for the America.. |
|||
Tensile Strength, Yield | 74.0 MPa | 10700 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL N300X PPE+PS PPE+PS blend. Unfilled. Non-brominated, non-chlorinated FR system. UL94 V0. High heat. Dielectric strength. Dimensional stability. Suitable for E/E applications. |
|||
Tensile Strength, Yield | 74.0 MPa | 10700 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL N300X PPE+PS (Asia Pacific) PPE+PS blend. Unfilled. Non-brominated, non-chlorinated FR system. UL94 V0. High heat. Dielectric strength. Dimensional stability. Suitable for E/E applications. |
|||
Tensile Strength, Yield | 74.0 MPa | 10700 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp 9X04488 POLYPHENYLENESULFONE LNP* Thermocomp* 9X04488 is a compound based on POLYPHENYLENESULFONE resin containing Mineral.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength, Yield | 74.0 MPa | 10700 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP 9X11428J PPS LNP* THERMOCOMP* 9X11428J is a compound based on Polyphenylsulfone containing Proprietary Fillers. Added features of this material include: Healthcare, Low Extractable. |
|||
Tensile Strength, Yield | 74.0 MPa | 10700 psi | ISO 527-1/-2 |
Covestro Apec® 1895 Polycarbonate Easy flowingeasy to demoldsoftening temperature (VST/B 120)=183 °CPreprocessingMax. Water content |
|||
Tensile Strength, Yield | 74.0 MPa | 10700 psi | ISO 527-1/-2 |
DuPont Performance Polymers Delrin® 311DP BK402 Acetal (POM)
(Unverified Data**) Nucleated Medium-high Viscosity Acetal Homopolymer Delrin 311DP BK402 is a medium high viscosity acetal homopolymer with improved thermal stability and modifications for more precise molding(reduced.. |
|||
Tensile Strength, Yield | 74.0 MPa | 10700 psi | ISO 527-1/-2 |
DuPont Performance Polymers Delrin® 511DP BK402 Acetal (POM)
(Unverified Data**) Nucleated Medium Viscosity Acetal Homopolymer Delrin 511DP is a medium viscosity acetal homopolymer with improved thermal stability and modifications for more precise molding (reduced warpage less s.. |
|||
Tensile Strength, Yield | 74.0 MPa | 10700 psi | ISO 527-1/-2 |
DuPont Performance Polymers Delrin® 911DP BK402 Acetal (POM)
(Unverified Data**) Nucleated Low Viscosity Acetal Homopolymer Delrin 911DP is a low viscosity acetal homopolymer with improved thermal stability and modifications for more precise molding (reduced warpage less shrinka.. |
|||
Tensile Strength, Yield | 74.0 MPa | 10700 psi | 5 mm/min; ISO 527 |
Eurostar Starflam PX07037 PA6, Flame Retardant, Injection Molded Starflam PX07037 is an Unfilled, Halogen Free and Red Phosphorous Free, Flame Retardant, Polyamide 6 Injection Molding Resin (IR laser marking grade)Information provided by Eurostar. |
|||
Tensile Strength, Yield | 74.0 MPa | 10700 psi | conditioned 15 days, 23°C - 50 % R.H.; ISO 527 |
Arkema Group Rilsan® Clear G170 Polyamide Rilsan® Clear G170 is a high performance transparent polyamide with outstanding thermal resistance. This grade has been designed for extrusion and injection molding applications and for medical use.. |
|||
Tensile Strength, Yield | 74.0 MPa | 10700 psi | ISO 527 |
Azoty Tarnow™ TARNOFORM 300 GF2 GB2 POM 10% glass fiber/10% glass beads mix reinforced injection molding grade, suitable for applications where increased strength and stiffness is required with care of the surface quality.Information prov.. |
|||
Tensile Strength, Yield | 74.0 MPa | 10700 psi | 50mm/min; ISO 527-1/-2 |
BASF Ultrason® P 3010 MR SW 10101 PPSU Description: Unreinforced, higher viscosity injection molding grade, flame retardant and with improved chemical resistance. This grade is black colored and demolding optimized. Abbreviated designati.. |
|||
Tensile Strength, Yield | 74.0 MPa @Temperature 23.0 °C |
10700 psi @Temperature 73.4 °F |
ISO 527 |
DuPont Performance Polymers Delrin® 911DP NC010 Acetal Homopolymer
(Unverified Data**) Delrin® 911DP is a low viscosity acetal homopolymer with improved thermal stability and modifications for more precise molding (reduced warpage, less shrinkage, fewer voids).Information provided by.. |
|||
Tensile Strength, Yield | 74.0 MPa | 10700 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® SD9705 PC Copolymer (Europe-Africa-Middle East) High visocisty PC Copolymer, low smoke, flame retardant resinThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |