SABIC Innovative Plastics Lexan® 505RU PC (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® 505RU PC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Lexan* 505RU is a glass reinforced,flame retardant(FR)grade with non brominated and non chlorinated FR systems and UV stablization packages. This product is intended for applications to meet WEEE/RoHS regulations as well as various voluntary environmental labels.
Physical Properties Metric English Comments
Specific Gravity 1.26 g/cc
1.26 g/cc
ASTM D792
Density 1.26 g/cc
0.0455 lb/in³
ISO 1183
Moisture Absorption 0.150 %
0.150 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.30 %
0.30 %
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0060 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 8.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
8.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Melt Index of Compound 7.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
7.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
8700 psi
5 mm/min; ISO 527
62.0 MPa
8990 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 72.0 MPa
10400 psi
5 mm/min; ISO 527
74.0 MPa
10700 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 6.0 %
6.0 %
Type I, 5 mm/min; ASTM D638
6.0 %
6.0 %
5 mm/min; ISO 527
Elongation at Yield 3.0 %
3.0 %
5 mm/min; ISO 527
4.0 %
4.0 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 3.50 GPa
508 ksi
1 mm/min; ISO 527
3.60 GPa
522 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 114 MPa
16500 psi
1.3 mm/min, 50 mm span; ASTM D790
122 MPa
17700 psi
2 mm/min; ISO 178
Flexural Modulus 3.20 GPa
464 ksi
1.3 mm/min, 50 mm span; ASTM D790
3.50 GPa
508 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.900 J/cm
1.69 ft-lb/in
ASTM D256
0.700 J/cm

@Temperature -30.0 °C
1.31 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Unnotched 12.0 J/cm
22.5 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
80*10*3; ISO 180/1A
8.00 kJ/m²

@Temperature -30.0 °C
3.81 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
NB75; 80*10*3; ISO 180/1U
73.0 kJ/m²

@Temperature -30.0 °C
34.7 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1U
Charpy Impact Unnotched NB
NB
NB87; Edgew 80*10*3 sp=62mm; ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
NB85; Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
0.700 J/cm²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 25.0 J

@Temperature 23.0 °C
18.4 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 50.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
27.8 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
50.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
27.8 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 74.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.1 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
85.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
47.2 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 136 °C
277 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
137 °C

@Thickness 3.20 mm
279 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 147 °C
297 °F
Rate B/50; ISO 306
149 °C
300 °F
Rate B/120; ISO 306
149 °C
300 °F
Rate B/50; ASTM D1525
Flammability, UL94 V-2

@Thickness 0.750 mm
V-2

@Thickness 0.0295 in
UL 94 by SABIC-IP
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94 by SABIC-IP
5VB

@Thickness 3.00 mm
5VB

@Thickness 0.118 in
UL 94 by SABIC-IP
5VA

@Thickness 3.00 mm
5VA

@Thickness 0.118 in
UL 94 by SABIC-IP
Glow Wire Test 850 °C
1560 °F
IEC 60695-2-13
875 °C
1610 °F
IEC 60695-2-13
960 °C

@Thickness 0.750 mm
1760 °F

@Thickness 0.0295 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Comparative Tracking Index 175 V
175 V
IEC 60112
175 - 250 V
175 - 250 V
UL 746A
Hot Wire Ignition, HWI 15 - 30 sec
15 - 30 sec
UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
UL 746A
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C Pass
IEC 60695-10-2
UV-light, water exposure/immersion F1
UL 746C