- Polymer Property : Tensile Modulus = 1360 ksi
Polymer Property : Tensile Modulus = 1360 ksi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Modulus | 9.41 GPa | 1360 ksi | same value from ASTM and ISO test. |
| BASF Capron® HPN 9333G Impact Modified, 33% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron HPN 9333G is a 33% glass reinforced, impact modified polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with excellent surface a.. |
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | ISO 527-2 |
| Pasargad Polymer Peyvand Pasamid 3P-H1150B Nylon 6, 50% Glass Fiber Reinforced Form: PelletsProcessing Method: Injection MoldingUses: Automotive Application Furniture Appliance Components Electrical PartsFastenerHousingInformation provided by Pasargad Polymer Peyvand Co |
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | |
| Idemitsu Kosan Xarec® WA 212 SPS, 30% Glass Filled Crystalline Polymer, Glass Filled, Impact Modified. Used in Automotive and Industrial applications. |
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | |
| Idemitsu Kosan Xarec® WA 212LG SPS, 30% Glass Filled |
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | ISO 527 |
| Grupo Repol Dinalon® A1S25 G25 PA66 25% Glass Fiber Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol |
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | ISO 527-1/-2 |
| Lanxess Durethan® BKV 130 GIT 900116 Copolyamide, 30% Glass Fiber CoPA, injection molding grade, 30% glass fibers, elastomer-modified, suitable for GIT (gas assisted technology), good surface finishApplication Examples: Chain-saw handles, office chair armrests, of.. |
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | d.a.m.; ISO 527-1, -2; 1 mm/min |
| Lanxess Durethan® ECO BV 30 H2 900500 Nylon 6, 30% Glass Fiber PA 6, 30% glass fibers, injection molding, heat-ageing stabilized, contains 30% pre-consumer recycled materialInformation provided by LANXESS. |
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | |
| LATI Latishield 66-13A G/30 PA66, Steel/Glass Fiber Reinforced EMI shielding product based on Polyamide 66 (PA66). Steel fibers. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Ind.. |
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP IFL36L PA6.12 LNP* LUBRICOMP* IFL36L is a compound based on Nylon 6/12 containing 30% Glass Fiber, 15% PTFE. Added features of this grade include: Low Extractable, Wear Resistant. |
|||
| Tensile Modulus | 9.37 GPa | 1360 ksi | 1 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP RFL449 PA 66 LNP* LUBRICOMP* RFL449 is a compound based on Nylon 66 resin containing 20% Glass Fiber, 20% PTFE. Added features of this grade include: Wear Resistant, Flame Retardant. |
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | 1 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP RFP36XXZ PA 66 (Asia Pacific) LNP Lubricomp RFP36XXZ is a compound based on Nylon 66 resin containing Glass Fiber, PTFE, Silicone. Added features of this material include: internally lubricated. Also known as Lubricomp RFL-4536 .. |
|||
| Tensile Modulus | 9.36 GPa | 1360 ksi | 1 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP STAT-KON DE0021E PC LNP STAT-KON* DE0021E is a compound based on Polycarbonate resin containing 10% Carbon Fiber. Added features of this material include: Easy Molding, Flame Retardant, Electrically Conductive. |
|||
| Tensile Modulus | 9.38 GPa | 1360 ksi | 1 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP STAT-KON DX01303C PC LNP STAT-KON* DX01303C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive. |
|||
| Tensile Modulus | 9.37 GPa | 1360 ksi | 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP THERMOCOMP IX95700 PA 6/12 (Asia Pacific) LNP* Thermocomp* IX95700 is a compound based on Nylon 6/12 resin containing Glass Fiber. |
|||
| Tensile Modulus | 9.37 GPa | 1360 ksi | 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP THERMOCOMP IX95700 PA6.12 LNP* THERMOCOMP* IX95700 is a compound based on Nylon 6/12 resin containing Glass Fiber. |
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | 1 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Thermocomp RF0057E PA 66 (Asia Pacific) LNP* Thermocomp* RF0057E is a compound based on Nylon 66 resin containing Glass Fiber, Flame Retardant. Added features of this material include: Non-Brominated & Non-Chlorinated Flame Retardant.Thi.. |
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | 1 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Thermocomp RF0057E PA 66 (Europe-Africa-Middle East) LNP* Thermocomp* RF0057E is a compound based on Nylon 66 resin containing Glass Fiber, Flame Retardant. Added features of this material include: Non-Brominated & Non-Chlorinated Flame Retardant.Thi.. |
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | 1 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP RF006EXZ PA 66 LNP THERMOCOMP* RF006EXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: Easy Molding. |
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | 1 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP RF006ESZ PA 66 LNP THERMOCOMP* RF006ESZ is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized. |
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | ASTM D638 |
| Plenco 2311 Phenolic, Granular, Compression Molded PLENCO 02311 is a versatile general purpose organic filled phenolic molding compound offering excellent mold processability and optimized cure cycles. PLENCO 02311 is also granulated to provide impr.. |
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | ASTM D638 |
| Plenco 4349 Phenolic, Granular, Injection Molded PLENCO 04349 is a heat resistant, mineral filled phenolic molding compound offering optimized cure characteristics, and excellent heat resistant properties. PLENCO 04349 is also formulated to offer .. |
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | ASTM D638 |
| Plenco 4349 Phenolic, Granular, Transfer Molded PLENCO 04349 is a heat resistant, mineral filled phenolic molding compound offering optimized cure characteristics, and excellent heat resistant properties. PLENCO 04349 is also formulated to offer .. |
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | DAM; ISO 527-1/-2 |
| DuPont Performance Polymers Zytel® 73G30T BK261 Nylon 6
(Unverified Data**) 30% Glass Reinforced Toughened Polyamide 6 Zytel 73G30T BK261 is a 30% glass fiber reinforced toughened black polyamide 6 resin for injection molding.Information provided by DuPont Performance Polym.. |
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | 1 mm/min; ISO 527 |
| Eurostar Staramide AG6H PA66, 30% Glass Filled, Injection Molded AG6 is a Heat Stabilized, 30% Glass Fiber Reinforced Polyamide 66 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier. |
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | 1 mm/min; ISO 527 |
| Eurostar Staramide AG6K PA66, 30% Glass Filled, Injection Molded AG6 is a Heat and Hydrolytically Stabilized, 30% Glass Fiber Reinforced Polyamide 66 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive suppli.. |
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | 1 mm/min; ISO 527 |
| Eurostar Staramide RF006SXP PA66, 30% Glass Fiber Filled, Injection Molded Staramide RF006SXP is a 30% Glass Fiber Reinforced Polyamide 66 Injection Molding Resin (also known as RF1006HS)Information provided by Eurostar. |
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | 1 mm/min; ISO 527 |
| Eurostar Staramide RF006SXS PA66, 30% Glass Fiber Filled, Injection Molded Staramide RF006SXS is a 30% Glass Fiber Reinforced Polyamide 66 Injection Molding Resin (also known as RF1006HS)Information provided by Eurostar. |
|||
| Tensile Modulus | 9.40 GPa | 1360 ksi | |
| LATI Latilub 66-15ST G/30 PA66, 30% Glass Fiber Reinforced, Silicone/PTFE Filled Self-lubricating product based on Polyamide 66 (PA66). Silicone / PTFE. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by La.. |
|||
| Tensile Modulus | 9.40 GPa @Temperature 23.0 °C |
1360 ksi @Temperature 73.4 °F |
DAM; ISO 527 |
| DuPont Performance Polymers Zytel® 73G30TGI BK267 Nylon 6
(Unverified Data**) Zytel® 73G30TGI BK267 is a 30% glass fiber reinforced, toughened, black polyamide 6 optimized for gas injection molding process.Information provided by DuPont Performance Polymers |
|||