Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 1.92 GPa | 278 ksi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Geon™ HTX Ultra LA436G Black 2880 Polyvinyl Chloride Alloy (PVC Alloy) Higher gloss, wider processing window version of Geon HTX Ultra LA426G.Recommend drying material for a minimum of 2 hours at 160 degrees Farenheit. Physical properties measured on LA436G Black 2880... |
|||
Tensile Modulus | 1.92 GPa | 278 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP ML004LS PP LNP* LUBRICOMP* ML004LS is a compound based on Polypropylene resin containing 20% PTFE. Added features of this matLNP* Lubricomp* ML004LS is a compound based on Polypropylene resin containing PTFE... |
|||
Tensile Modulus | 1.92 GPa | 278 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics SABIC PPCOMPOUND 9710 PP SABIC® PPcompound 9710 is a mineral filled, impact modified polypropylene TPO. This material combines high impact resistance, scratch resistance, and heat stability with interior automotive UV st.. |
|||
Tensile Modulus | 1.92 GPa | 279 ksi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® WX-9700 ASA, Unreinforced Extrusion Grade Information provided by Samsung Cheil Industries. |
|||
Tensile Modulus | 1.92 GPa | 278 ksi | ASTM Test |
Styrolution Terlux® 2812 TR MABS Terlux 2812 TR is a transparent grade of MABS for injection molding with high flowability.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS. |
|||
Tensile Modulus | 1.92 GPa | 279 ksi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® WX-9700 ASA, Unreinforced Extrusion Grade Information provided by Samsung Cheil Industries. |
|||
Tensile Modulus | 1.92 GPa | 278 ksi | ISO 527-2 |
Styron MAGNUM™ 3325 SLG Acrylonitrile Butadiene Styrene (ABS) Resin Overview: Super Low Gloss, Medium Heat, Medium Impact ABS resin for injection molded automotive interior trim applications Magnum 3325 SLG can achieve 60° Gardner gloss levels below 2.0 with low .. |
|||
Tensile Modulus | 1.92 GPa | 278 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® IQ357M PBT+PC (Europe-Africa-Middle East) Valox* Resin IQ357M: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified, easy flow product with mold release. |
|||
Tensile Modulus | 1.92 GPa | 278 ksi | 1 mm/min |
Arkema Group Appryl® CZN 0525 Polypropylene, 25% Talc Filled Compound of a PP copolymer modified with EPR and 25% talc. This grade has been specially developed for interior trim applications, that required an excellent impact test associated with a high modul.. |
|||
Tensile Modulus | 1.92 GPa | 278 ksi | 1 mm/min |
Arkema Group Rilsan® MB 3000 Nylon 11, Sheathing Grade (Conditioned) Designation ISO 1874-PA11,MF,12-010Polyvalent rigid grade for injection molding and sheathing of cables. Available color: natural. Flame retardant agent, halogen free. Fire-resistant. Easy to be pro.. |
|||
Tensile Modulus | 1.92 GPa | 278 ksi | 1 mm/min |
Arkema Group Appryl® CZU 0525 Polypropylene, 25% Talc Filled Compound of a PP copolymer modified with EPR and 25% talc. This grade has been specially developed for exterior trim automotive applications, that required an excellent impact test associated with a.. |