Polymer Property : Tensile Modulus = 278 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	1.92 GPa	278 ksi	Type I, 5.1 mm/min; ASTM D638
PolyOne Geon™ HTX Ultra LA436G Black 2880 Polyvinyl Chloride Alloy (PVC Alloy) Higher gloss, wider processing window version of Geon HTX Ultra LA426G.Recommend drying material for a minimum of 2 hours at 160 degrees Farenheit. Physical properties measured on LA436G Black 2880...
Tensile Modulus	1.92 GPa	278 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP ML004LS PP LNP* LUBRICOMP* ML004LS is a compound based on Polypropylene resin containing 20% PTFE. Added features of this matLNP* Lubricomp* ML004LS is a compound based on Polypropylene resin containing PTFE...
Tensile Modulus	1.92 GPa	278 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics SABIC PPCOMPOUND 9710 PP SABICÂ® PPcompound 9710 is a mineral filled, impact modified polypropylene TPO. This material combines high impact resistance, scratch resistance, and heat stability with interior automotive UV st..
Tensile Modulus	1.92 GPa	278 ksi	ASTM Test
Styrolution TerluxÂ® 2812 TR MABS Terlux 2812 TR is a transparent grade of MABS for injection molding with high flowability.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.
Tensile Modulus	1.92 GPa	278 ksi	ISO 527-2
Styron MAGNUMâ„¢ 3325 SLG Acrylonitrile Butadiene Styrene (ABS) Resin Overview: Super Low Gloss, Medium Heat, Medium Impact ABS resin for injection molded automotive interior trim applications Magnum 3325 SLG can achieve 60Â° Gardner gloss levels below 2.0 with low ..
Tensile Modulus	1.92 GPa	278 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics ValoxÂ® IQ357M PBT+PC (Europe-Africa-Middle East) Valox* Resin IQ357M: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified, easy flow product with mold release.
Tensile Modulus	1.92 GPa	278 ksi	1 mm/min
Arkema Group Appryl® CZN 0525 Polypropylene, 25% Talc Filled Compound of a PP copolymer modified with EPR and 25% talc. This grade has been specially developed for interior trim applications, that required an excellent impact test associated with a high modul..
Tensile Modulus	1.92 GPa	278 ksi	1 mm/min
Arkema Group Rilsan® MB 3000 Nylon 11, Sheathing Grade (Conditioned) Designation ISO 1874-PA11,MF,12-010Polyvalent rigid grade for injection molding and sheathing of cables. Available color: natural. Flame retardant agent, halogen free. Fire-resistant. Easy to be pro..
Tensile Modulus	1.92 GPa	278 ksi	1 mm/min
Arkema Group Appryl® CZU 0525 Polypropylene, 25% Talc Filled Compound of a PP copolymer modified with EPR and 25% talc. This grade has been specially developed for exterior trim automotive applications, that required an excellent impact test associated with a..