PolyOne Geon™ HTX Ultra LA436G Black 2880 Polyvinyl Chloride Alloy (PVC Alloy)

Category Polymer , Thermoplastic , Vinyl (PVC)
Manufacturer PolyOne Corporation
Trade Name Geon™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Geon™ HTX Ultra LA436G Black 2880 Polyvinyl Chloride Alloy (PVC Alloy).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Higher gloss, wider processing window version of Geon HTX Ultra LA426G.Recommend drying material for a minimum of 2 hours at 160 degrees Farenheit. Physical properties measured on LA436G Black 2880. This version produces the highest gloss, higher impact and can be run at lower extruder temperatures than standard LA426G product.Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.21 g/cc
1.21 g/cc
ASTM D792
Mechanical Properties Metric English Comments
Hardness, Shore D 74
74
15 sec; ASTM D2240
Tensile Strength, Yield 36.0 MPa
5220 psi
Type I, 5.1 mm/min; ASTM D638
Tensile Modulus 1.92 GPa
278 ksi
Type I, 5.1 mm/min; ASTM D638
Flexural Strength 58.7 MPa
8510 psi
ASTM D790
Flexural Modulus 2.04 GPa
296 ksi
ASTM D790
Izod Impact, Notched 4.90 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
9.18 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Compression Molded; ASTM D256A
Dart Drop Total Energy 52.0 J/cm

@Temperature 23.0 °C
0.0974 ft-lb/mil

@Temperature 73.4 °F
Procedure A, C.125; ASTM D4226
111 J/cm

@Temperature 23.0 °C
0.208 ft-lb/mil

@Temperature 73.4 °F
Procedure B, C.125; ASTM D4226
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 83.0 µm/m-°C
46.1 µin/in-°F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 87.8 °C

@Thickness 3.18 mm
190 °F

@Thickness 0.125 in
Annealed; ASTM D648
88.3 °C

@Thickness 3.18 mm
191 °F

@Thickness 0.125 in
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 81.1 °C

@Thickness 3.18 mm
178 °F

@Thickness 0.125 in
Unannealed; ASTM D648
85.0 °C

@Thickness 3.18 mm
185 °F

@Thickness 0.125 in
Annealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 174 - 193 °C
345 - 379 °F
Descriptive Properties Value Comments
Ease of Sizing Acceptable
Features Good Processability
High Gloss
High Impact Resistance
Forms Cube
Pellets
Generic Material PVC Alloy
Generic Name Polyvinyl Chloride Alloy (PVC Alloy)
Processing Method Extrusion
PVC Cell Classification 14215
ASTM D1784
441311640000
ASTM D4216
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Uses Capstock
Outdoor Applications
Profiles