Polymer Property : Tensile Modulus = 1620 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	11.17 GPa	1620 ksi	same value from ASTM and ISO test.
BASF Capron® HPN 9233G 33% Glass-Filled Nylon 6 (Dry) (discontinued **) Capron HPN 9233G is a 33% glass reinforced polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with excellent surface aesthetics. It is..
Tensile Modulus	11.2 GPa	1620 ksi	ISO 527-2
Solvay Specialty Polymers Amodel® A-1130 FW Polyphthalamide (PPA) (Unverified Data**) Amodel A-1130 FW is a 30% glass-fiber reinforced polyphthalamide (PPA) grade containing a solid lubricant. This resin was designed for moderate-pressure, low-velocity friction and wear applications...
Tensile Modulus	11.2 GPa	1620 ksi	ISO 527-2
Solvay Specialty Polymers Amodel® A-1133 DW Polyphthalamide (PPA) (discontinued **) Amodel A-1133 DW is a 33% glass-fiber reinforced polyphthalamide (PPA) grade approved for use with potable water in the United States, the United Kingdom and France. - Natural: A-1133 NT DW - Black:..
Tensile Modulus	11.2 GPa @Temperature 100 °C	1620 ksi @Temperature 212 °F	ISO 527-2
Solvay Specialty Polymers Amodel® A-1145 HS Polyphthalamide (PPA) (Unverified Data**) Amodel A-1145 HS is a 45% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, very high flexural modulus and very high tensile strength. Excellent creep ..
Tensile Modulus	11.2 GPa	1620 ksi	ISO 527-2/1A/1
Solvay Specialty Polymers KetaSpire® KT-880 GF30 Polyetheretherketone (PEEK) (Unverified Data**) KetaSpire KT-880 GF30 is the high-flow, 30% glass-fiber reinforced grade of polyetheretherketone (PEEK). This resin offers higher strength and stiffness properties relative to unreinforced KetaSpire..
Tensile Modulus	11.2 GPa	1620 ksi	ASTM Data
Dow Questra® WA206 High Heat Syndiotactic Polystyrene, 40% Glass Filled (discontinued **) QUESTRA® Crystalline Polymers are semi-crystalline engineering thermoplastic resins produced from styrene monomer using a proprietary metallocene catalyst system. These syndiotactic polymers are ve..
Tensile Modulus	11.2 GPa	1620 ksi	ASTM Data
Dow Questra® WA551 High Heat Syndiotactic Polystyrene, 40% Glass Filled (discontinued **) QUESTRA® Crystalline Polymers are semi-crystalline engineering thermoplastic resins produced from styrene monomer using a proprietary metallocene catalyst system. These syndiotactic polymers are ve..
Tensile Modulus	11.2 GPa	1620 ksi	ISO 527
Nilit FRIANYL A63 H-GV35 Nylon 6.6 for injection molding, 35% glass fiber reinforced Nylon 6.6 for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Modulus	11.2 GPa	1620 ksi	d.a.m.; ISO 527-1, -2; 1 mm/min
Lanxess DurethanÂ® AKV 35 H2.0 SR1 901510 Nylon 66, Glass Fiber Reinforced PA 66, 35% glass fibers, injection molding, heat-aging stabilized, improved surface finishInformation provided by LANXESS.
Tensile Modulus	11.2 GPa	1620 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP WFL369 PBT LNP* Lubricomp* WFL369 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Ret..
Tensile Modulus	11.2 GPa	1620 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP WFL369 PBT (Asia Pacific) LNP* Lubricomp* WFL369 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Ret..
Tensile Modulus	11.2 GPa	1620 ksi	ISO 527-2
Solvay Specialty Polymers AmodelÂ® A-1130 FW Polyphthalamide (PPA), 30% Glass Fiber AmodelÂ® A-1130 FW is a 30% glass-fiber reinforced polyphthalamide (PPA) grade containing a solid lubricant. This resin was designed for moderate-pressure, low-velocity friction and wear applicati..
Tensile Modulus	11.2 GPa @Temperature 100 Â°C	1620 ksi @Temperature 212 Â°F	4; ISO 527-2
Solvay Specialty Polymers AmodelÂ® A-1145 HS Polyphthalamide (PPA), 45% Glass Fiber (Dry) AmodelÂ® A-1145 HS is a 45% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, very high flexural modulus and very high tensile strength. Excellent cr..
Tensile Modulus	11.2 GPa	1620 ksi	ISO 527-2
Solvay Specialty Polymers AmodelÂ® HFZ A-1133 L Polyphthalamide (PPA), 33% Glass Fiber AmodelÂ® HFZ A-1133 L is a high-flow, 33% glass fiber reinforced polyphthalamide (PPA) grade.Features: Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; Good Stiffness; ..
Tensile Modulus	11.17 GPa	1620 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DF008ER PC LNP THERMOCOMP* DF008ER is a compound based on Polycarbonate resin containing 40% Glass Fiber. Added features include: Easy Molding, Mold Release.
Tensile Modulus	11.17 GPa	1620 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP RF007H PA 66 LNP* Thermocomp* RF007H is a compound based on Nylon 66 containing glass fiber. Added feature includes: Healthcare.
Tensile Modulus	11.17 GPa	1620 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP RF007SXP PA 66 LNP* THERMOCOMP* RF007SXP is a compound based on Nylon 66 containing 35% Glass Fiber. Added feature of this material includes: Heat Stabilized.
Tensile Modulus	11.2 GPa	1620 ksi	1 mm/min; ISO 527-1
Sax Polymers SAXAMID 126F6RY01 Nylon 6, 30% Glass Fiber SAXAMID 126F6RY01 is a polyamide 6 injection-molding-grade reinforced with 30% glass fibers. It has a halogen-free flame retardant.Information provided by SAX Polymers
Tensile Modulus	11.2 GPa	1620 ksi	ISO 527-2
Solvay Specialty Polymers KetaSpireÂ® KT-880 GF30 Polyetheretherketone (PEEK), 30% Glass Fiber KetaSpireÂ® KT-880 GF30 is the high-flow, 30% glass-fiber reinforced grade of polyetheretherketone (PEEK). This resin offers higher strength and stiffness properties relative to unreinforced KetaS..
Tensile Modulus	11.17 GPa	1620 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DF008ERH PC LNP THERMOCOMP* DF008ERH is a compound based on Polycarbonate resin containing 40% Glass Fiber. Added features of this material include: Easy Molding, Mold Release, Healthcare.
Tensile Modulus	11.2 GPa	1620 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP LF006E PEEK (Europe-Africa-Middle East) LNP* THERMOCOMP* LF006E is a compound based on Polyetheretherketone resin containing Glass Fiber. Added features include: Easy Molding.
Tensile Modulus	11.17 GPa	1620 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP MC002 PP LNP* THERMOCOMP* MC002 is a compound based on Polypropylene resin containing 10% Carbon Fiber. Added feature of this material is: Electrically Conductive.
Tensile Modulus	11.2 GPa	1620 ksi	ISO 527-1/-2
Unitika B2040G50 PA66, 50% Glass Fiber Reinforced, Conditioned Information provided by Unitika Ltd.
Tensile Modulus	11.2 GPa	1620 ksi	ISO 527-1/-2
DuPont Performance Polymers Crastin® SK645FR NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)&l 30% Glass Reinforced Flame Retardant Polybutylene Terephthalate Crastin SK645FR is a flame retardant 30% glass reinforced polybutylene terephthalate molding resin. It is recognized as UL94V-0 at 0.7..
Tensile Modulus	11.2 GPa	1620 ksi	ISO 527
Azoty Tarnow™ Tarnamid® T-27 GF40 I Polyamide 6 - Glass Fiber Reinforced 40% Glass fiber reinforced, impact modified, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following mai..
Tensile Modulus	11.2 GPa	1620 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP VERTON RVL36SXS PA 66 (Europe-Africa-Middle East) LNP* VERTON* RVL36SXS is a compound based on PA 66 resin containing Long Glass Fiber, PTFE. Added features include; Internally Lubricated.
Tensile Modulus	11.2 GPa	1620 ksi	ISO 527-2
Solvay Specialty Polymers Amodel® HFZ A-1133 L Polyphthalamide (PPA) (Unverified Data**) Amodel® HFZ A-1133 L is a high-flow, 33% glass fiber reinforced polyphthalamide (PPA) grade. Natural: HFZ A-1133 L NT Black: HFZ A-1133 L BK 937Information provided by Solvay Specialty Polymers.