Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	2.56 GPa	371 ksi	Type I, 5.1 mm/min; ASTM D638
PolyOne Geon™ Vinyl Rigid Extrusion 87358 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne
Tensile Modulus	2.56 GPa	371 ksi	Type I, 5.1 mm/min; ASTM D638
PolyOne Geon™ Vinyl Rigid Extrusion L9620 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne
Tensile Modulus	2.56 GPa	371 ksi	ISO 527-1/-2
Kuraray Genestarâ„¢ N1002A-M41 Nylon Low friction unreinforced injection grade. Main Features:Low friction coefficientLow wearExamples of applications are:Friction and wear applicationGear and wheel
Tensile Modulus	2.56 GPa	371 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRILOY K2000 Acetal LNP LUBRILOY* K2000 is a compound based on Acetal resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant.
Tensile Modulus	2.56 GPa	371 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRILOY K2000 Acetal (Asia Pacific) LNP LUBRILOY* K2000 is a compound based on Acetal resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Tensile Modulus	2.56 GPa	371 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRILOY K2000XXH Acetal LNP LUBRILOY* K2000XXH is a compound based on Acetal resin containing Proprietary Lubricant. Added features of this material are: Wear Resistant, Healthcare.
Tensile Modulus	2.56 GPa	371 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON DX04462C PC LNP STAT-KON* DX04462C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Clean Compounding System, Electrically Conductive.
Tensile Modulus	2.56 GPa	371 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON DX12411C PC LNP* STAT-KON* DX12411C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Clean Compounding System.
Tensile Modulus	2.56 GPa	371 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DX11354 PC (Asia Pacific) This is a PC compound with good plating, surface and mechanical performance, a good candidate for Laser Direct Structuring applications.
Tensile Modulus	2.56 GPa	371 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON DX02437 PC (Asia Pacific) LNP Stat-Kon DX02437 is a compound based on Polycarbonate resin containing conductive carbon powder, with good impact-resistance, flow and ESD performance, suitable for semi-con industry.
Tensile Modulus	2.56 GPa	371 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON DX04462C PC (Asia Pacific) LNP* STAT-KON* DX04462C is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Clean Compounding System.
Tensile Modulus	2.56 GPa	371 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL EXNL1117 PPE+HIPS high gloss Noryl
Tensile Modulus	2.56 GPa	371 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL FXN4020H PPE+HIPS high gloss Noryl
Tensile Modulus	2.56 GPa	371 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL FXN4020H PPE+HIPS (Asia Pacific) high gloss Noryl
Tensile Modulus	2.56 GPa	371 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL FXN4020H PPE+HIPS (Europe-Africa-Middle East) high gloss Noryl
Tensile Modulus	2.56 GPa	371 ksi	1 mm/min
Arkema Group Lucalor® PEY 333 CPVC, Pipe Grade LUCALOR PEY 333 is a chlorinated polyvinyl chloride compound (CPVC) developed for the extrusion of pipes for hot water supply and distribution system.ISO data provided by the manufacturer, Arkema.