SABIC Innovative Plastics LNP STAT-KON DX02437 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DX02437 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP Stat-Kon DX02437 is a compound based on Polycarbonate resin containing conductive carbon powder, with good impact-resistance, flow and ESD performance, suitable for semi-con industry.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.236 g/cc | 0.04465 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0064 cm/cm @Thickness 1.50 - 3.20 mm |
0.0064 in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0068 cm/cm @Thickness 1.50 - 3.20 mm |
0.0068 in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
| Melt Index of Compound | 16 g/10 min @Load 5.00 kg, Temperature 300 °C |
16 g/10 min @Load 11.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 47.0 MPa | 6820 psi | Type I, 5 mm/min; ASTM D638 |
| 47.0 MPa | 6820 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 58.0 MPa | 8410 psi | Type I, 5 mm/min; ASTM D638 |
| 58.0 MPa | 8410 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 7.8 % | 7.8 % | Flexural Strain, break, 2 mm/min; ISO 178 |
| 16.5 % | 16.5 % | 5 mm/min; ISO 527 | |
| 19.3 % | 19.3 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.55 GPa | 370 ksi | 1 mm/min; ISO 527 |
| 2.56 GPa | 371 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 92.0 MPa | 13300 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.55 GPa | 370 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched | 3.59 J/cm | 6.73 ft-lb/in | ASTM D256 |
| 2.94 J/cm @Temperature 0.000 °C |
5.51 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 21.4 J/cm | 40.1 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 24.0 kJ/m² | 11.4 ft-lb/in² | 80*10*4; ISO 180/1A |
| 20.0 kJ/m² @Temperature 0.000 °C |
9.52 ft-lb/in² @Temperature 32.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 130 kJ/m² | 61.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Charpy Impact Unnotched | 9.50 J/cm² | 45.2 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| Charpy Impact, Notched | 2.60 J/cm² | 12.4 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 27.0 J | 19.9 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| 39.0 J @Temperature 23.0 °C |
28.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 | |
| Impact Test | 63.0 J | 46.5 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C | 259 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 111 °C @Thickness 3.20 mm |
232 °F @Thickness 0.126 in |
ASTM D648 | |
| Vicat Softening Point | 144 °C | 291 °F | Rate A/50; ASTM D1525 |
| 144 °C | 291 °F | Rate A/50; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.41e+7 ohm-cm | 1.41e+7 ohm-cm | ASTM D257 |
| Surface Resistance | 4.80e+7 ohm | 4.80e+7 ohm | ASTM D257 |