Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Modulus | 1.40 GPa | 203 ksi | ISO 6721-2 |
Styrolution Polystyrol 158 K GR 2 PS Description: Polystyrol 158 K is a heat resistant, rapid freezing general purpose grade. It is suitable for expanded sheet and film; for blend s with high impact Polystyrol in heat contact applicati.. |
|||
Shear Modulus | 1.40 GPa | 203 ksi | ISO 6721-2 |
Styrolution Polystyrol 158 K GR 21 PS Description: Polystyrol 158 K is a heat resistant, rapid freezing general purpose grade. It is suitable for expanded sheet and film; for blend s with high impact Polystyrol in heat contact applicati.. |
|||
Shear Modulus | 1.40 GPa | 203 ksi | ISO 6721-2 |
Styrolution Polystyrol 165 H GR 2 PS Description: Polystyrol 165 H is a high molecular weight, good flowing grade, often blended with high impact extrusion grades.Applications: In blends with high impact Polystyrene or Styrolux; thermo.. |
|||
Shear Modulus | 1.40 GPa | 203 ksi | ISO 6721-2 |
Styrolution Polystyrol 165 H GR 21 PS Description: Polystyrol 165 H is a high molecular weight, good flowing grade, often blended with high impact extrusion grades.Applications: In blends with high impact Polystyrene or Styrolux; thermo.. |
|||
Shear Modulus | 1.40 GPa | 203 ksi | ISO R527 type 1 |
Hexcel® HexPly® 914 175°C Curing Epoxy Matrix HexPly® 914 is a highly successful modified epoxy matrix which is used extensively in high temperature resistant primary aircraft structures. The controlled melt viscosity and excellent matrix rheo.. |
|||
Shear Modulus | 1.40 GPa | 203 ksi | calculated |
BASF Capron® 5202CQ Blend HS Blend Nylon 66 (Dry)
(discontinued **) Capron 5202CQ HS Blend is a heat stabilized, blended polyamide 6,6 injection molding homopolymer developed for fast molding cycles. It is also available in pigmented versions.Capron 5202CQ HS Blend.. |
|||
Shear Modulus | 1.40 GPa | 203 ksi | calculated |
BASF Capron® 8202C HS Nylon 6 (Dry)
(discontinued **) Capron 8202C HS is a heat stabilized, low viscosity, polyamide 6 injection molding homopolymer possessing a modified crystalline structure for increased property performance and faster cycles. It i.. |