Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Modulus | 76.0 GPa | 11000 ksi | |
Special Metals DURANICKEL® 301 (UNS N03301) Annealed and Aged Strip Tensile strength (ultimate), hardness, and elongation values reported here are typical for Annealed and Aged Strip specifically. Other property values are typical of aged DURANICKEL® alloy 301 or.. |
|||
Shear Modulus | 76.0 GPa | 11000 ksi | |
Special Metals DURANICKEL® 301 (UNS N03301) Annealed and Aged Wire Tensile strength (ultimate) and elongation values reported here are typical for Annealed and Aged Wire specifically. Other property values are typical of aged DURANICKEL® alloy 301 or the alloy i.. |
|||
Shear Modulus | 76.0 GPa | 11000 ksi | |
Special Metals DURANICKEL® 301 (UNS N03301) Annealed Rod and Bar Tensile strength (ultimate and yield), compressive strength, hardness, and elongation values reported here are typical for Annealed Rod and Bar specifically. Other property values are typical of ann.. |
|||
Shear Modulus | 76.0 GPa | 11000 ksi | |
Special Metals DURANICKEL® 301 (UNS N03301) Annealed Strip Tensile strength (ultimate and yield), hardness, and elongation values reported here are typical for Annealed Strip specifically. Other property values are typical of annealed DURANICKEL® alloy 3.. |
|||
Shear Modulus | 76.0 GPa | 11000 ksi | |
Special Metals DURANICKEL® 301 (UNS N03301) Annealed Wire Tensile strength (ultimate) and elongation values reported here are typical for Annealed Wire specifically. Other property values are typical of annealed DURANICKEL® alloy 301 or the alloy in gen.. |
|||
Shear Modulus | 76.0 GPa | 11000 ksi | |
Special Metals DURANICKEL® 301 (UNS N03301) Cold-Drawn and Aged Rod and Bar Tensile strength (ultimate and yield), compressive strength, hardness, and elongation values reported here are typical for Cold-Drawn and Aged Rod and Bar specifically. Other property values are typ.. |
|||
Shear Modulus | 76.0 GPa | 11000 ksi | |
Special Metals DURANICKEL® 301 (UNS N03301) Cold-Drawn Rod and Bar Tensile strength (ultimate and yield), hardness, and elongation values reported here are typical for Cold-Drawn Rod and Bar specifically. Other property values are typical of annealed DURANICKEL®.. |
|||
Shear Modulus | 76.0 GPa | 11000 ksi | |
Special Metals DURANICKEL® 301 (UNS N03301) Half-Hard Strip Tensile strength (ultimate), hardness, and elongation values reported here are typical for Half-Hard Strip specifically. Other property values are typical of annealed DURANICKEL® alloy 301 or the.. |
|||
Shear Modulus | 76.0 GPa | 11000 ksi | |
Special Metals DURANICKEL® 301 (UNS N03301) Hot-Finished and Aged Rod and Bar Tensile strength (ultimate and yield), hardness, and elongation values reported here are typical for Hot-Finished and Aged Rod and Bar specifically. Other property values are typical of aged DURANIC.. |
|||
Shear Modulus | 76.0 GPa | 11000 ksi | |
Special Metals DURANICKEL® 301 (UNS N03301) Hot-Finished Rod and Bar Tensile strength (ultimate and yield), hardness, and elongation values reported here are typical for Hot-Finished Rod and Bar specifically. Other property values are typical of annealed DURANICKELÂ.. |
|||
Shear Modulus | 76.0 GPa | 11000 ksi | |
Special Metals DURANICKEL® 301 (UNS N03301) Spring Strip Tensile strength (ultimate), hardness, and elongation values reported here are typical for Spring Strip specifically. Other property values are typical of annealed DURANICKEL® alloy 301 or the al.. |
|||
Shear Modulus | 76.0 GPa | 11000 ksi | |
Special Metals DURANICKEL® 301 (UNS N03301) Spring Strip, Aged Tensile strength (ultimate), hardness, and elongation values reported here are typical for Spring Strip, Aged specifically. Other property values are typical of aged DURANICKEL® alloy 301 or the .. |
|||
Shear Modulus | 76.0 GPa | 11000 ksi | |
Special Metals DURANICKEL® 301 (UNS N03301) Spring Wire Tensile strength (ultimate) and elongation values reported here are typical for Spring Wire specifically. Other property values are typical of annealed DURANICKEL® alloy 301 or the alloy in gener.. |
|||
Shear Modulus | 76.0 GPa | 11000 ksi | |
Special Metals DURANICKEL® 301 (UNS N03301) Spring Wire, Aged Tensile strength (ultimate) and elongation values reported here are typical for Spring Wire, Aged specifically. Other property values are typical of aged DURANICKEL® alloy 301 or the alloy in gen.. |
|||
Shear Modulus | 76.0 GPa | 11000 ksi | Dynamic Method |
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Cold Rolled Sheet, 2 Part Heat Treatment, 0.040 inch (1.02 mm) Thickness Tensile strength (ultimate and yield), shear strength, and elongation values reported here are typical for Cold Rolled Sheet, 2 Part Heat Treatment, 0.040 inch (1.02 mm) Thickness samples. Density a.. |
|||
Shear Modulus | 76.0 GPa | 11000 ksi | Dynamic Method |
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Cold Rolled Sheet, 3 Part Heat Treatment, 0.040 inch (1.02 mm) Thickness Tensile strength (ultimate and yield), shear strength, and elongation values reported here are typical for Cold Rolled Sheet, 3 Part Heat Treatment, 0.040 inch (1.02 mm) Thickness samples. Density a.. |
|||
Shear Modulus | 76.0 GPa | 11000 ksi | Dynamic Method |
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Cold Rolled Sheet, 3 Part Heat Treatment, 0.062 inch (1.57 mm) Thickness Tensile and bearing strengths (ultimate and yield) and elongation values reported here are typical for Cold Rolled Sheet, 3 Part Heat Treatment, 0.062 inch (1.57 mm) Thickness samples. Density and m.. |
|||
Shear Modulus | 76.0 GPa | 11000 ksi | Precipitation Hardened, Dynamic Method |
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Cold Rolled Sheet, Solution Treated Tensile strength (ultimate and yield), and elongation values reported here are typical for Cold Rolled Sheet, Solution Treated samples. Density and magnetic permeability are typical of annealed INCO.. |
|||
Shear Modulus | 76.0 GPa | 11000 ksi | Dynamic Method |
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Forged Disc, 2 Part Heat Treatment Tensile strength (ultimate and yield), reduction of area, and elongation values reported here are typical for Forged Disc, 2 Part Heat Treatment samples. Density and magnetic permeability are typica.. |
|||
Shear Modulus | 76.0 GPa | 11000 ksi | Dynamic Method |
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Forged Disc, 3 Part Heat Treatment Tensile strength (ultimate and yield), reduction of area, and elongation values reported here are typical for Forged Disc, 3 Part Heat Treatment samples. Density and magnetic permeability are typica.. |
|||
Shear Modulus | 76.0 GPa | 11000 ksi | Precipitation Hardened, Dynamic Method |
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Forged Disc, Solution Treated Tensile strength (ultimate and yield), reduction of area, and elongation values reported here are typical for Forged Disc, Solution Treated samples. Density and magnetic permeability are typical of .. |
|||
Shear Modulus | 76.0 GPa | 11000 ksi | Dynamic Method |
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Hot Finished Flat, 2 Part Heat Treatment, 1.250 inch (31.8 mm) Thickness Tensile strength (ultimate and yield), shear strength, compressive strength, reduction of area, and elongation values reported here are typical for Hot Finished Flat, 2 Part Heat Treatment, 1.250 in.. |
|||
Shear Modulus | 76.0 GPa | 11000 ksi | Dynamic Method |
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Hot Finished Rod, 3 Part Heat Treatment, 0.562 inch (14.3 mm) Diameter Tensile strength (ultimate and yield), shear strength, reduction of area, and elongation values reported here are typical for Hot Finished Rod, 3 Part Heat Treatment, 0.562 inch (14.3 mm) Diameter s.. |
|||
Shear Modulus | 76.0 GPa | 11000 ksi | Dynamic Method |
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Hot Finished Rod, 3 Part Heat Treatment, 8.0 inch (203 mm) Diameter Tensile strength (ultimate and yield), compressive strength, reduction of area, and elongation values reported here are typical for Hot Finished Rod, 3 Part Heat Treatment, 8.0 inch (203 mm) Diamete.. |
|||
Shear Modulus | 76.0 GPa | 11000 ksi | Calculated |
Sapco Partially Stabilized TZP Zirconia (YSZ) Information provided by Sapco. |
|||
Shear Modulus | 76.0 GPa | 11000 ksi | |
Elgiloy® Co-Cr-Ni Alloy, Wire, 10% Cold Reduction The strength, shear modulus, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, f.. |
|||
Shear Modulus | 76.0 GPa | 11000 ksi | |
Elgiloy® Co-Cr-Ni Alloy, Wire, 10% Cold Reduction, Heat Treated Heat Treatment 5 hours at 527°C. The strength, shear modulus, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: Hi.. |
|||
Shear Modulus | 76.0 GPa | 11000 ksi | |
ATI Allegheny Ludlum AL 600™ Nickel-Base Alloy, UNS N06600 Allegheny Ludlum is a nickel-chromium alloy designed for use from cryogenic to elevated temperatures in the range of 1093 degrees Celsius. AL 600 alloy is non-magnetic and readily weldable. The al.. |
|||
Shear Modulus | 76.0 GPa | 11000 ksi | Dynamic Method |
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Cold Rolled Sheet, 2 Part Heat Treatment, 0.062 inch (1.57 mm) Thickness Tensile and bearing strengths (ultimate and yield) and elongation values reported here are typical for Cold Rolled Sheet, 2 Part Heat Treatment, 0.062 inch (1.57 mm) Thickness samples. Density and m.. |
|||
Shear Modulus | 76.0 GPa | 11000 ksi | Dynamic Method |
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Hot Finished Rod, 2 Part Heat Treatment, 0.562 inch (14.3 mm) Diameter Tensile strength (ultimate and yield), shear strength, reduction of area, and elongation values reported here are typical for Hot Finished Rod, 2 Part Heat Treatment, 0.562 inch (14.3 mm) Diameter s.. |