Special Metals INCONEL® 706 Precipitation Hardening Alloy, Hot Finished Rod, 3 Part Heat Treatment, 8.0 inch (203 mm) Diameter

Category Metal , Nonferrous Metal , Nickel Alloy , Superalloy , Iron Base
Manufacturer Special Metals (includes the former Inco Alloys International Inc.)
Trade Name INCONEL®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Special Metals INCONEL® 706 Precipitation Hardening Alloy, Hot Finished Rod, 3 Part Heat Treatment, 8.0 inch (203 mm) Diameter.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Tensile strength (ultimate and yield), compressive strength, reduction of area, and elongation values reported here are typical for Hot Finished Rod, 3 Part Heat Treatment, 8.0 inch (203 mm) Diameter samples. Density and magnetic permeability are typical of precipitation hardened INCONEL® alloy 706. Other property values are typical of INCONEL® alloy 706.For optimum creep and rupture properties, the alloy receives a three part heat treatment as follows: Solution treat 1700-1850°F (925-1010°C) for a time commensurate with section size, then air cool. Stabilizing treatment 1550°F (845°C)/3 hr, air cool. Precipitation treatment 1325°F (720°C)/8 hr, furnace cool at 100°F (55°C)/hr to 1150°F (620°C)/8 hr, air cool.Data provided by the manufacturer, Special Metals.
Physical Properties Metric English Comments
Density 8.08 g/cc
0.292 lb/in³
Precipitation Hardened
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 1300 MPa
189000 psi
Tensile Strength, Yield 1010 MPa

@Strain 0.200 %
146000 psi

@Strain 0.200 %
Elongation at Break 18 %
18 %
Reduction of Area 28 %
28 %
Modulus of Elasticity 210 GPa
30500 ksi
Dynamic Method
Compressive Yield Strength 1102 MPa
159900 psi
(0.2% Offset) Thickness not reported for this value
Poissons Ratio 0.382
0.382
Calculated by mfr.
Shear Modulus 76.0 GPa
11000 ksi
Dynamic Method
Thermal Properties Metric English Comments
CTE, linear 13.46 µm/m-°C

@Temperature 24.0 - 100 °C
7.478 µin/in-°F

@Temperature 75.2 - 212 °F
Mean
15.08 µm/m-°C

@Temperature 24.0 - 300 °C
8.378 µin/in-°F

@Temperature 75.2 - 572 °F
Mean
15.59 µm/m-°C

@Temperature 24.0 - 500 °C
8.661 µin/in-°F

@Temperature 75.2 - 932 °F
Mean
16.42 µm/m-°C

@Temperature 21.0 - 700 °C
9.122 µin/in-°F

@Temperature 69.8 - 1290 °F
Mean
Specific Heat Capacity 0.444 J/g-°C
0.106 BTU/lb-°F
Thermal Conductivity 12.5 W/m-K
86.8 BTU-in/hr-ft²-°F
Melting Point 1334 - 1371 °C
2433 - 2500 °F
Solidus 1334 °C
2433 °F
Liquidus 1371 °C
2500 °F
Component Elements Properties Metric English Comments
Aluminum, Al <= 0.060 %
<= 0.060 %
Boron, B <= 0.0060 %
<= 0.0060 %
Carbon, C <= 0.30 %
<= 0.30 %
Chromium, Cr 14.5 - 17.5 %
14.5 - 17.5 %
Cobalt, Co <= 1.0 %
<= 1.0 %
Copper, Cu <= 0.35 %
<= 0.35 %
Iron, Fe 38 %
38 %
As remainder
Manganese, Mn <= 0.35 %
<= 0.35 %
Nickel, Ni 39 - 44 %
39 - 44 %
Including Cobalt
Niobium, Nb (Columbium, Cb) 2.5 - 3.3 %
2.5 - 3.3 %
Includes Ta
Phosphorous, P <= 0.020 %
<= 0.020 %
Silicon, Si <= 0.35 %
<= 0.35 %
Sulfur, S <= 0.015 %
<= 0.015 %
Titanium, Ti <= 0.40 %
<= 0.40 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000985 ohm-cm
0.0000985 ohm-cm
Magnetic Permeability 1.01
1.01
at 200 Oersted (15.9 kA/m);Annealed
Curie Temperature <= -78.0 °C
<= -108 °F