Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ASTM D882 |
SABIC 218B Linear Low Density Polyethylene for Cast Film Product Description: 218B is a Linear Low Density Polyethylene grade designed to provide easy processability and specially formulated for optimum thermal stability at high processing temperatures u.. |
|||
Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ISO 527-3 |
Polimeri Europa Riblene® FF 20 Low Density Polyethylene - Blown Film Extrusion Riblene FF 20 is a high molecular weight low density polyethylene (LDPE) suitable for blown film extrusion. Riblene FF 20 is characterized by a good melt strength leading to a good bubble stability.. |
|||
Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ISO 527-3 |
Polimeri Europa Riblene® FF 22 Low Density Polyethylene - Blown Film Extrusion Riblene FF 22 is a high molecular weight low density polyethylene (LDPE), with added slip agent, suitable for blown film extrusion. Riblene FF 22 is characterized by a good melt strength leading to.. |
|||
Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ISO 527-3 |
Polimeri Europa Riblene® FH 20 Low Density Polyethylene - Blown Film Extrusion Riblene FH 20 is a low density polyethylene (LDPE) suitable for blown film extrusion. Riblene FH 20 is characterized by a good balance between processability and mechanical properties.Films manufac.. |
|||
Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ISO 527-3 |
Polimeri Europa Riblene® FL 30 Low Density Polyethylene - Blown Film Extrusion Riblene FL 30 is a low density polyethylene (LDPE) ideal for blown film extrusion. Riblene FL 30 is characterized by a good balance between processability, mechanical and optical properties.Films m.. |
|||
Film Tensile Strength at Break, TD | 22.0 MPa @Thickness 0.400 mm |
3190 psi @Thickness 0.0157 in |
ISO 527 |
Premix Thermoplastics PRE-ELEC® ABS 1415 Conductive Thermoplastic Compound PRE-ELEC® ABS 1415 is a conductive thermoplastic compound based on ABS. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® ABS.. |
|||
Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ISO 527 |
Premix Thermoplastics PRE-ELEC® PE 1271 PRE-ELEC PE 1271 is a conductive thermoplastic compound based on a blend of PE-LD/PE-LLD. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivi.. |
|||
Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ASTM D882 |
NOVA Chemicals Sclair® 19A Homopolymer HDPE Film Resin Film Properties.Data provided by the manufacturer. |
|||
Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ASTM D882 |
Petroquimica Triunfo Trithene® TS 4016 LDPE and LLDPE Blend - Film The Trithene® TS 4016 resin is a mixture of low-density polyethylene (LDPE) with linear low-density polyethylene (LLDPE) designed to meet the needs of the technical films segment for the use of aut.. |
|||
Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ASTM D882 |
Petroquimica Triunfo Tritheva® TN 2020 EVA Copolymer The Tritheva TN 2020 resin is a Ethylene-Vinyl Acetate copolymer (EVA) developed to mostly meet the needs of the multi-layer packaging segment produced by coextrusion and/or lamination processes. Th.. |
|||
Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ISO 527 |
Premix Thermoplastics PRE-ELEC® PE 1308
(discontinued **) PRE-ELEC PE 1308 is a conductive thermoplastic compound based on a blend of PE-LD/PE-LLD. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivi.. |
|||
Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ASTM D882 |
Eastman D4008-F Polyethylene
(discontinued **) Polyethylene D4008-F is a fractional melt formulation designed for film applications. It is suggested for applications requiring toughness and clarityList of Applications: Food packagingFood-contac.. |
|||
Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ASTM D882 |
Eastman E6838-969F Polyethylene
(discontinued **) E6838-969F is a low density formulation with no slip and medium antiblock. It is suggested for film applications that require toughness such as shrink/bundling film, disposable diapersand overwrap... |
|||
Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ASTM D882 |
ExxonMobil Escorene® CR-5810 EVA Resin, for High Cling Stretch Film
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A tackified Ethylene Vinyl Acetate resin for blown or cast stretch film.Applications: Packing films (cling). Data for film properties below based o.. |
|||
Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ASTM D882 |
ExxonMobil Escorene® LD-317 EVA Film Resin, FMI
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A fractional melt index, 5.5% vinyl acetate copolymer film resin. Film made from LD-317 offers excellent impact strength, tensile properties, and h.. |
|||
Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ASTM D 882 |
NOVA Chemicals Sclair® 99K Homopolymer HDPE Film Resin 99K complies with the U.S. FDA specifications for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food, without te.. |
|||
Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ASTM D882 |
Huntsman PE1753 EVA Film Extrusion
(discontinued **) 7.5% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Yields film with good clarity and excellent impact strength.Applications: Film extrusion: icebags, liquid packaging, lamination film, and .. |
|||
Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ASTM D882 |
Petroquimica Triunfo Trithene® TU 3001 LDPE - Agricultural Film The Trithene TU 3001 resin is a low-density polyethylene (LDPE) with high molecular weight, designed to satisfy those applications that require high mechanical properties, good processability and bu.. |
|||
Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ASTM D882 |
Petroquimica Triunfo Trithene® TU 8091 LDPE - Agricultural Film Trithene TU 8091 is a low-density polyethylene (LDPE) with high molecular weight, with excellent mechanical properties and good processability. These qualities ensure the production of very wide fil.. |
|||
Film Tensile Strength at Break, TD | 22.0 - 55.0 MPa | 3190 - 7980 psi | Average value: 41.2 MPa Grade Count:6 |
Overview of materials for Cyclo Olefin Polymer This property data is a summary of similar materials in the MatWeb database for the category "Cyclo Olefin Polymer". Each property range of values reported is minimum and maximum values of appropria.. |
|||
Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ASTM D882 |
Braskem PB 525/64 LDPE Blown Film Extrusion Polyethylene
(discontinued **) 38µm film gauge, obtained in 75mm extruder, die gap 1.0mm, output 1.75 kg/h-cm with 2:1 BUR. Applications: Automatic packaging of liquids products (FFS). Information provided by Braskem |
|||
Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ISO 527-3 |
Borealis FL5580 High Density Polyethylene FL5580 is a high density polyethylene with an excellent combination of extrusion properties and moisture barrier properties. Applications: FL5580 has been developed especially for applications like.. |
|||
Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ISO 527-3 |
Topas Advanced Polymers TOPAS® 9903D-10 Cyclic Olefin Copolymer (COC) TOPAS® 9903D-10 is a very low glass transition temperature (Tg=33°C) film extrusion grade. It is designed to deliver high shrinkage at low temperatures in shrink packaging applications. It is a mo.. |
|||
Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ASTM D882 |
ExxonMobil Escorene® LD-331 EVA Film Resin, Very High Clarity, Very High Impact
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A 5.8% vinyl acetate copolymer, high clarity film resin. Film made from this resin exhibits superior impact strength and heat sealability.Applicati.. |
|||
Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ASTM D882 |
Huntsman PE1403 EVA Film Extrusion
(discontinued **) 4% Vinyl Acetate EVA Copolymer, DMF listed and FDA compliantFeatures: High clarity film with good toughness and flexibility at low temperatures.Applications: Film extrusion: frozen food and general .. |
|||
Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ASTM D882 |
NOVA Chemicals Sclair® 11B4 Octene LLDPE Film Resin
(discontinued **) Film Properties. Features: Low gel, excellent seal characteristics, easy processability.Applications: Specialty lamination, co-extrusion.Data provided by the manufacturer. |
|||
Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ASTM D882 |
Eastman E6838-975F Polyethylene
(discontinued **) E6838-975F is a low density formulation with medium slip and medium antiblock. The formula is used in general purpose packaging where impact strength and processability are important. End-use film.. |