NOVA Chemicals Sclair® 99K Homopolymer HDPE Film Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer NOVA Chemicals
Trade Name Sclair®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Sclair® 99K Homopolymer HDPE Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
99K complies with the U.S. FDA specifications for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food, without temperature or food-type restrictions, subject to technical suitability.NOVA Chemicals' polyethylene resins are chemically and biologically inert.Features: Excellent processability, Excellent Stretchability, High stiffness, Superior strength, Low gelAdditives: Process stabilizer, Process aidApplications: Industrial woven bags, TarpaulinsFilm properties are typical of blown film extruded on a 2.5" extruder with 4" die and a 35-mil die gap at a blowup ratio of 2.5:1, but are dependant on operating conditions.
Physical Properties Metric English Comments
Density 0.962 g/cc
0.0348 lb/in³
ASTM D 792
Thickness 38.0 microns
1.50 mil
Melt Flow 0.72 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.72 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Hardness, Shore D 69
69
ASTM D 2240
Film Tensile Strength at Yield, MD 27.0 MPa
3920 psi
ASTM D 882
Film Tensile Strength at Yield, TD 22.0 MPa
3190 psi
ASTM D 882
Film Tensile Strength at Break, MD 39.0 MPa
5660 psi
ASTM D 882
Film Tensile Strength at Break, TD 22.0 MPa
3190 psi
ASTM D 882
1% Secant Modulus, MD 830 MPa
120000 psi
ASTM D 882
1% Secant Modulus, TD 1330 MPa
193000 psi
ASTM D 882
Thermal Properties Metric English Comments
Vicat Softening Point 128 °C
262 °F
ASTM D 1525
Optical Properties Metric English Comments
Haze 78 %
78 %
ASTM D 1003
Gloss 5.0 %
5.0 %
at 45°; ASTM D 2457
Processing Properties Metric English Comments
Melt Temperature 200 - 230 °C
392 - 446 °F
Recommended
Blow-up Ratio (BUR) 2.5 - 4.0
2.5 - 4.0