Polymer Property : Film Tensile Strength at Break, TD = 50.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, TD	50.0 MPa	7250 psi	ISO 527-3
Polimeri Europa Eraclene® FB 506 Hexene Copolymer High Density Polyethylene - Blown Film Extrusion Eraclene FB 506 is a high density polyethylene resin (HDPE), hexene copolymer, with antioxidants, suitable for blown film extrusion.Its broad molecular weight distribution and density successfully c..
Film Tensile Strength at Break, TD	50.0 MPa	7250 psi
Premix Thermoplastics PREFLEX E12.5 Polyphenylene Ether (PPO/PPE) PREFLEX films combine outstanding dielectric properties, good heat stability, low water absorption and chemical resistance in a way not available before. Also rigid boards made of the same material ..
Film Tensile Strength at Break, TD	50.0 MPa	7250 psi
Premix Thermoplastics PREFLEX E50 Polyphenylene Ether (PPO/PPE) PREFLEX films combine outstanding dielectric properties, good heat stability, low water absorption and chemical resistance in a way not available before. Also rigid boards made of the same material ..
Film Tensile Strength at Break, TD	50.0 MPa	7250 psi	ASTM D882
Chevron Phillips 7120ST LLDPE Blown Film Resin, Hexene Copolymer (discontinued **) Resin Type: Hexene Copolymer, Cast/Blown Film ResinCharacteristics: Good Drawdown, Can be used in blown or cast applicationsApplications:Stretch Wrap, CoextrusionsProcessing Conditions: Extruder 6.3..
Film Tensile Strength at Break, TD	50.0 MPa	7250 psi	ASTM D882
Lotte Chemical Titan TITANCEED® mL2764 Linear low density polyethylene resin (discontinued **) Titanceed® mL2764 is a pelleted metallocene linear low density polyethylene resin formulated with antioxidant. Films made from Titanceed® mL2764 have outstanding tensile properties, impact streng..
Film Tensile Strength at Break, TD	50.0 MPa	7250 psi	ASTM D882
Reliance Industries Relene F46003 Polyethylene Relene F46003 is a High Density Polyethylene grade suitable for producing blown parts with superior stiffness and barrier properties. It is recommended for making liners and coextruded film structu..
Film Tensile Strength at Break, TD	50.0 MPa	7250 psi	ASTM D882
Reliance Industries Relene F56003 Polyethylene Relene F56003 is a High Density Polyethylene grade suitable for producing blown parts with excellent drawdown and paper like feel. It is recommended for making carrier bags and coextruded film stru..
Film Tensile Strength at Break, TD	50.0 MPa	7250 psi	ASTM D882
Solvay Specialty Polymers Ajediumâ„¢ Films -- HalarÂ® 500LC Ethylene Chlorotrifluoroethylene Copolymer (ECTFE) HalarÂ® ECTFE is a semi-crystalline fluoropolymer with a chemical structure of a 1:1 alternating copolymer of ethylene and chlorotrifluoroethylene.HalarÂ® film is a strong, hard, tough, abrasion..
Film Tensile Strength at Break, TD	50.0 MPa	7250 psi	ISO 527-3
Borealis Bormed™ SC820CF Polypropylene Random Copolymer Bormed™ SC820CF is a very soft random heterophasic copolymer. Applications: Bormed™ SC820CF is recommended for packaging for medical devices. Bormed™ SC820CF contains no slip, antiblock, antist..
Film Tensile Strength at Break, TD	50.0 MPa	7250 psi	ISO 527-3
Topas Advanced Polymers TOPAS® 8007F-04 Cyclic Olefin Copolymer (COC) TOPAS® 8007F-04 is a general purpose film extrusion grade. It is a high clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and..
Film Tensile Strength at Break, TD	50.0 MPa	7250 psi	ISO 527-3
Topas Advanced Polymers TOPAS® 8007F-400 Cyclic Olefin Copolymer (COC) TOPAS® 8007F-400 is a robust film extrusion grade designed for blending with polyethylene (PE). It is a moderate clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, ..
Film Tensile Strength at Break, TD	50.0 MPa	7250 psi	ASTM D882
Eastman Embrace LV Copolyester for Extruded/Cast Film Applications:Beverage packagingDairy packagingFood packagingJuice packagingPharmaceutical packagingSoft drink packagingKey Attributes:Customizable shrink curveEye-catching 360° graphic capabilityLo..
Film Tensile Strength at Break, TD	50.0 MPa	7250 psi	ASTM D882
Chevron Phillips MarFlex® D163 Metallocene Linear Low Density Polyethylene, Blown Film This mLLDPE is tailored for applications that require:Excellent clarityExcellent glossExcellent toughnessExcellent heat sealTypical blown film applications include:Seal layer in coextrusionsHeavy du..
Film Tensile Strength at Break, TD	50.0 MPa	7250 psi	Calculated from mfr's report of 66 N/cm per ASTM D828 and the typical thickness
DuPont™ Nomex® 410 Paper, 5 mil Nominal Thickness Nomex® Type 410 is a calendared insulation paper which offers high inherent dielectric strength, mechanical toughness, flexibility, and resilience. It is the original form of Nomex® paper and is ..
Film Tensile Strength at Break, TD	50.0 MPa	7250 psi	ASTM-D882
Braskem GM9450F HDPE Blown Film Extrusion Polyethylene HDPE GM9450F is a high-density polyethylene developed for the high molecular weight film extrusion segment produced with bimodal technology. The film produced from this resin has high tenacity and e..
Film Tensile Strength at Break, TD	50.0 MPa	7250 psi	ISO 527-3
Polimeri Europa Eraclene® FA 506 Hexene Copolymer High Density Polyethylene - Blown Film Extrusion Eraclene FA 506 is a high density polyethylene resin (HDPE), hexene copolymer, with antioxidants, suitable for blown film extrusion.Its broad molecular weight distribution and density successfully c..