Reliance Industries Relene F56003 Polyethylene

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded
Manufacturer Reliance Industries
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Reliance Industries Relene F56003 Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Relene F56003 is a High Density Polyethylene grade suitable for producing blown parts with excellent drawdown and paper like feel. It is recommended for making carrier bags and coextruded film structures. Information provided by Reliance Industries
Physical Properties Metric English Comments
Density 0.956 g/cc
0.0345 lb/in³
ASTM D1505
Melt Flow 0.30 g/10 min

@Load 2.16 kg
0.30 g/10 min

@Load 4.76 lb
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 35.0 MPa
5080 psi
ASTM D882
Film Tensile Strength at Yield, TD 37.0 MPa
5370 psi
ASTM D882
Film Elongation at Break, MD 700 %
700 %
ASTM D882
Film Elongation at Break, TD 900 %
900 %
ASTM D882
Elmendorf Tear Strength, MD 0.700 g/micron
17.8 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 10.0 g/micron
254 g/mil
ASTM D1922
Dart Drop 1.60 g/micron
40.6 g/mil
38mm Dart, 66mm height; ASTM D1709
Film Tensile Strength at Break, MD 55.0 MPa
7980 psi
ASTM D882
Film Tensile Strength at Break, TD 50.0 MPa
7250 psi
ASTM D882