Polymer Property : Film Tensile Strength at Break, TD = 6380 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, TD	44.0 MPa	6380 psi	ISO 527
Premix Thermoplastics PRE-ELEC® PC 1431 PRE-ELEC PC 1431 is a conductive thermoplastic compound based on polycarbonate. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELE..
Film Tensile Strength at Break, TD	44.0 MPa	6380 psi	ASTM D882
Westlake Mxsten CV CV77515-F Plastomer (discontinued **) Mxsten CV plastomer CV77515-X is a polyethylene plastomer designed for blown film extrusion that contains medium slip and no antiblock additives. Films produced with this resin exhibit a very low s..
Film Tensile Strength at Break, TD	44.0 MPa	6380 psi	ASTM D 882
NOVA Chemicals Surpass® FPs016-C Octene sLLDPE Film Resin FPs016-C complies with the U.S. FDA regulations for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food.NOVA Chem..
Film Tensile Strength at Break, TD	44.0 - 195 MPa	6380 - 28300 psi	Average value: 102 MPa Grade Count:7
Overview of materials for Ethylene Vinyl Alcohol (EVOH) This property data is a summary of similar materials in the MatWeb database for the category "Ethylene Vinyl Alcohol". Each property range of values reported is minimum and maximum values of appropr..
Film Tensile Strength at Break, TD	44.0 MPa	6380 psi	ASTM-D882
Westlake Mxsten CV77515 Polyethylene Plastomer Mxsten CV Plastomer CV77515 resin is a polyethylene plastomer designed for blown film extrusion and food packaging that contains 1,000 ppm slip and no antiblock additives. Films produced with this r..
Film Tensile Strength at Break, TD	44.0 MPa	6380 psi	ISO 527-3
Total PPR 6280 Random Copolymer Polypropylene, Cast Film Extrusion Grade Total Petrochemicals PPR 6280 is a random copolymer polypropylene with a melt flow index of 7 g/10 min suitable for the cast extrusion of films with outstanding optical properties and easy heat weld..
Film Tensile Strength at Break, TD	44.0 MPa	6380 psi	ASTM D882
Eastman Sahara Film Sahara Films are developed for use in applications where increased temperature resistance is desired.Applications/UsesHigh temperature printable films
Film Tensile Strength at Break, TD	44.0 MPa	6380 psi	ASTM D882
NOVA Chemicals Sclair® 13J7 Octene LMDPE Film Resin (discontinued **) Film Properties. Features: Low gel, high clarity.Applications: Film.Data provided by the manufacturer.
Film Tensile Strength at Break, TD	44.0 MPa	6380 psi	10%/min.; ASTM D638
EVALCA EVAL® EF-E Ethylene Vinyl Alcohol Copolymer Film (discontinued **) 44 mol % Ethylene. Non oriented type film; property values for 20 µm film.Data provided by EVALCA. Applications: EVOH is used in packaging applications because of its outstanding gas barrier pr..