Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 70.0 MPa | 10200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Cycolac® MG47F ABS (Europe-Africa-Middle East) Multi-purpose, injection molding ABS providing a favorable balance of engineering properties. FDA compliant. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycolac® MG94 ABS Superior flow, injection molding ABS. Good impact. For thin-wall applications. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
Ovation Polymers Opnyl OP66UT105 Nylon 66 Ultra Tough - High Impact, Excellent retention of mechanical properties, High service temperature. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All.. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycolac® S701SU ABS (Europe-Africa-Middle East) CYCOLAC S701SU is an ABS with improved UV resistance, providing a superior balance of properties. Its wide processing window, excellent flow and good mechanical properties give this material an exce.. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Cycoloy® CP8320 PC+ABS Cycoloy Medium Heat Plating Grade for Automotive |
|||
Flexural Yield Strength | 70.3 - 230 MPa | 10200 - 33400 psi | Average value: 158 MPa Grade Count:95 |
Overview of materials for Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant". Each property range of values re.. |
|||
Flexural Yield Strength | 70.6 MPa @Thickness 3.20 mm |
10200 psi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
LG Chemical HF380U ABS, High Flow Feature: Injection Molding, High Flow, Good WeatherabilityApplication: Electric & Electronic Products, Miscellaneous Goods)CAS No. 9003-56-9Information provided by LG Chemical |
|||
Flexural Yield Strength | 70.6 MPa @Thickness 3.20 mm |
10200 psi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
LG Chemical LG709W ABS, Low Gloss, Heat Resistance Injection Molding, Low Gloss, Heat ResistanceApplication: Automobiles Interior Housing (Column Cover, Pilllars, Etc.)CAS No. 25120-20-1, 9003-56-9, 25747-74-7 and 9003-54-7Information provided by LG.. |
|||
Flexural Yield Strength | 70.6 MPa @Thickness 3.20 mm |
10200 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical LUMAX GN5006FC PBT+ABS, Heat Resistance Description: Injection Molding, PBT+ABS, Halogen Free Flame RetardantApplication: E&E (Connector)CAS: 9003-56-9, 9003-54-7 and 24968-12-5Information provided by LG Chemical |
|||
Flexural Yield Strength | 70.6 MPa @Thickness 6.40 mm |
10200 psi @Thickness 0.252 in |
10mm/min; ASTM D790 |
LG Chemical LUMID HI5003A PA6/PO, High Impact, High Flow, Good Paintablility Feature: Injection Molding, PA6/PO, High Impact, High Flow, Good PaintablilityApplication: Automotive Exterior PartsCAS No. 25038-54-4, 9010-79-1, 9003-07-0 and 14807-96-6Information provided by LG .. |
|||
Flexural Yield Strength | 70.6 MPa @Thickness 3.20 mm |
10200 psi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
LG Chemical MA210 ABS, Low Gloss Feature: Extrusion Molding, General Purpose, Low GlossApplication: Automotive Sheet, Semi-Conductor TrayCAS No. 9003-56-9Information provided by LG Chemical |
|||
Flexural Yield Strength | 70.6 MPa @Thickness 3.20 mm |
10200 psi @Thickness 0.126 in |
15 mm/min; ASTM D790 |
LG Chemical MP211 ABS, Low Gloss, Metal Plating Feature: Injection Molding, High Flow, Metal PlatingApplication: Decorative Parts (Home Appliance Door Handle Etc)CAS No. 9003-56-9 and 9003-54-7Information provided by LG Chemical |
|||
Flexural Yield Strength | 70.6 MPa @Thickness 6.40 mm |
10200 psi @Thickness 0.252 in |
30mm/min; ASTM D790 |
LG Chemical LUPOL HR2100D PP+GF17% Description: Injection Molding, PP+GF17%, General PurposeApplication: Electrical, Electronic and Automotive Parts CAS: 9003-07-0 and 165997-17-3Information provided by LG Chemical |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | at 5% strain; ASTM D790 |
Ineos ABS TRIAX® 1220 S ABS/Nylon Blend, Dry as Molded Extrusion and injection molding grade with good stress corrosion cracking resistance, good chemical resistance (fuel, cleaning agents), high impact and notched impact strength, good acoustical dampi.. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | ASTM D790 |
KYDEX® 6565 Acrylic/PVC Thermoplastic Sheet Low heat release aviation gradeApplications: Airducts, seat parts, bulkhead laminates, escape slide packboards, gallery parts, instrument panels, laboratory floorplans, sidewall panels, life vest sh.. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | ISO 178 |
Solvay Technyl® B 50H1 Nylon 66/6, Flame Retardant, EH50 Flame retardant copolyamide 66/6, unreinforced, heat stabilized, for injection molding.This phosphorus and halogen free flame retardant grade, UL 94 VO (0.4 mm), offers excellent filling qualities a.. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Xenoy® HX5600HP PBT+PC (Europe-Africa-Middle East) Xenoy HX5600HP is PBT based semi-crystalline blend with balanced flow and impact properties. Improved chemical resistance against lab disinfectants and chemicals for healthcare enclosure and housing.. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Xenoy® IQ1103 PBT+PC Xenoy iQ*1103 resin - Environmentally responsible and sustainable low carbon footprint resin. Xenoy iQ1103 is an unreinforced, impact modified alloy of PC (polycarbonate) + Valox iQ* PBT (polybuty.. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Xenoy® IQ1103 PBT+PC (Asia Pacific) Xenoy iQ*1103 resin - Environmentally responsible and sustainable low carbon footprint resin. Xenoy iQ1103 is an unreinforced, impact modified alloy of PC (polycarbonate) + Valox iQ* PBT (polybuty.. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL GTX GTX902E PPE+PA (Europe-Africa-Middle East) NORYL GTX902E is a low cost GTX grade especially developed for automotive (wheel)trims. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Noryl GTX LMX171 PPO/PBT (Europe-Africa-Middle East) Noryl LMX171 is a PPO/PBT blend including conductive agent with a balanced heat/impact property profile. Noryl LMX differentiate from Noryl GTX by a lower moisture uptake (0.15%).This data was suppl.. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Xenoy® X5600WX PC+POLYESTER (Europe-Africa-Middle East) Unreinforced, opaque Polyester+PC alloy. Chemical resistance, dimensional stability and mechanical performance. UV Stabilized. Mold ReleaseThis data was supplied by SABIC-IP for the Europe-Africa-Mi.. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Thermotuf PK005EI2 PA 6 (Europe-Africa-Middle East) LNP* THERMOTUF* PK005EI2 is a compound based on PA 6 resin containing Impact Modifier, Mineral. Added features include: High Impact.This data was supplied by SABIC-IP for the Europe-Africa-Middle Ea.. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Noryl EN130S PPE+HIPS (Europe-Africa-Middle East) Noryl EN130S is an extrusion grade with a Vicat B/120 temperature of 140 deg C, developed for profile extrusion and in compliance with Food contact regulations; color limited.This data was supplied .. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | ASTM D790 |
Tipco Tipcolite® TG 211 Phenolic Compound, Mineral & Wood Flour, Soft Flow & High Electrical Properties Soft Flow Phenolic Compound, Reinforced with Mineral & Wood FlourApplications: Electrical & ElectronicsProcessing: Compression MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.. |
|||
Flexural Yield Strength | 70.3 MPa @Thickness 3.17 mm |
10200 psi @Thickness 0.125 in |
|
TPI Porene® ABS-GA800 High Impact ABS Resin Information provided by US distributor Polymer Technology and Services, LLC (PTS). |
|||
Flexural Yield Strength | 70.3 MPa @Thickness 3.17 mm |
10200 psi @Thickness 0.125 in |
|
TPI Porene® ABS-GA850 High Impact ABS Resin Information provided by US distributor Polymer Technology and Services, LLC (PTS). |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | ASTM D790 |
E-Polymers TEKAMID® TB110HI , High Impact PA6, DAM High Impact resistance at low temperatureInformation provided by E-Polymers Co. Ltd. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL FN150 PPE+HIPS (Europe-Africa-Middle East) NORYL FN150 twin wall foam meets UL standard 94 V-0/5V ratings at 4 mm wall thickness. These unique flammability characteristics make FN150 the supreme choice for designing optimum wall thickness in.. |
|||
Flexural Yield Strength | 70.0 - 131 MPa | 10200 - 19000 psi | Average value: 105 MPa Grade Count:7 |
Overview of materials for Polybutylene Terephthalate (PBT), Aramid Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Aramid Fiber Filled". Each property range of values reported is minimu.. |