Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycolac® MG38U ABS High impact ABS. UL 746C f1 listed. Toughness/rigidity. Good fatigue resistance. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycolac® MG47 ABS (Europe-Africa-Middle East) Multi-purpose, injection molding ABS providing a favorable balance of engineering properties. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycolac® S701S ABS (Europe-Africa-Middle East) CYCOLAC S701S is a new developed ABS providing a superior balance of properties. Its wide processing window, excellent flow and good mechanical properties give this material an excellent fit in appl.. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | ASTM D790 |
Eastman Eastar GN002 Copolyester, Natural
(discontinued **) Eastar GN002 Copolyester is a glycol modified polyethylene terephthalate (PET) with an added mold release. Eastar GN002 copolyester will not crystallize and thus offers wider processing latitude tha.. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | ISO 178, ASTM D790 |
Nilit Nilamid A3 H ZC High Impact PA66 Description: Nilamid A3 H ZC has outstanding impact performance, even at minus temperatures. It is widely used for components subjected to high shock loads. Applications include bicycle components, .. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | ISO 178, ASTM D790 |
Nilit Nilamid B3 H XB Unfilled, Impact Resistant PA6 Description: Nilamid B3 H XB is a high impact NYLON 6. The product has excellent impact properties above 0°C, combined with good maintaining mechanical characteristics. Application areas include au.. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | ASTM D790 |
Ineos Nova 3930 General Purpose Crystal Polystyrene
(discontinued **) High melt flow, Crystal clearApplications: Razor components, Personal care, Thin wall moldingExposure to gamma radiation in the 2.02-6.06 megarad range has no significant effect on the physical and .. |
|||
Flexural Yield Strength | 70.0 - 186 MPa | 10200 - 27000 psi | Average value: 123 MPa Grade Count:31 |
Overview of materials for Acetal Copolymer, 20% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, 20% Glass Fiber Reinforced". Specific grades with glass content between 15% and 24% ar.. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | 5% strain; ASTM D790 |
Metton LMR M1534 Liquid Molding Resin Different product numbers represent different formulations for customer specific needs such as liquid freezing point. Metton LMR is a tough and durable engineering plastic material used to produce .. |
|||
Flexural Yield Strength | 70.0 MPa @Strain 3.50 % |
10200 psi @Strain 3.50 % |
2 mm/min; ISO 178-A |
Lanxess Pocan® C 1202 000000 PET + PC PBT + PC, non-reinforced, injection molding, improved impact strength, low tendency to warp, UV-stabilizedInformation provided by LANXESS. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Xenoy® 5720U PBT+PC (Asia Pacific) Unfilled PBT+PC alloy. Outstanding low temperature impact/chemical resistance. UV stabilized version of XENOY |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Xenoy® 5720U PBT+PC (Europe-Africa-Middle East) Unfilled PBT+PC alloy. Outstanding low temperature impact/chemical resistance. UV stabilized version of XENOY |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Xenoy® HX5600HP PBT+PC (Asia Pacific) Xenoy HX5600HP is PBT based semi-crystalline blend with balanced flow and impact properties. Improved chemical resistance against lab disinfectants and chemicals for healthcare enclosure and housing.. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Xenoy® IQ1103 PBT+PC (Asia Pacific) Xenoy iQ*1103 resin - Environmentally responsible and sustainable low carbon footprint resin. Xenoy iQ1103 is an unreinforced, impact modified alloy of PC (polycarbonate) + Valox iQ* PBT (polybuty.. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL GTX GTX902E PPE+PA (Europe-Africa-Middle East) NORYL GTX902E is a low cost GTX grade especially developed for automotive (wheel)trims. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL GTX GTX964 PPE+PA (Europe-Africa-Middle East) NORYL GTX964 is an unfilled impact modified material with optimised processability. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Noryl GTX LMX171 PPO/PBT (Europe-Africa-Middle East) Noryl LMX171 is a PPO/PBT blend including conductive agent with a balanced heat/impact property profile. Noryl LMX differentiate from Noryl GTX by a lower moisture uptake (0.15%).This data was suppl.. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL PX1112 PPE+HIPS (Europe-Africa-Middle East) NORYL PX1112 is an unfilled medium heat resistant material. This grade offers improved impact resistance to meet the ECE-dashboard standard. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® ENH3500 PBT (Europe-Africa-Middle East) Unfilled PBT, Non-Brominated & Non-Chlorinated Flame Retardant |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® IQ357M PBT+PC (Europe-Africa-Middle East) Valox* Resin IQ357M: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified, easy flow product with mold release. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Xenoy® X5600WX PC+POLYESTER (Europe-Africa-Middle East) Unreinforced, opaque Polyester+PC alloy. Chemical resistance, dimensional stability and mechanical performance. UV Stabilized. Mold ReleaseThis data was supplied by SABIC-IP for the Europe-Africa-Mi.. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Thermotuf PK005EI2 PA 6 (Europe-Africa-Middle East) LNP* THERMOTUF* PK005EI2 is a compound based on PA 6 resin containing Impact Modifier, Mineral. Added features include: High Impact.This data was supplied by SABIC-IP for the Europe-Africa-Middle Ea.. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics Noryl ENV85 PPE+PS (Asia Pacific) Low heat, flame retardant, extrusion grade PPO/HIPS alloy.Internal flammability results only.Not a UL recognised material.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | ASTM D790 |
Eastman Drystar 0601 Copolyester, Injection Molded This product-line is designed to meet the needs of converters seeking value-added solutions to their drying requirements of copolyesters. Eastman’s copolyesters are highly valued for their excellen.. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | ASTM D790 |
E-Polymers TEKAMID® TB110HI , High Impact PA6, DAM High Impact resistance at low temperatureInformation provided by E-Polymers Co. Ltd. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
Eurostar Staramide PK005EI2 PA6, Mineral Fiber Filled, Impact Modified Injection Molded Staramide PK005EI2 is an Impact Modified Mineral Filled Polyamide 6 Injection Molding ResinInformation provided by Eurostar. |
|||
Flexural Yield Strength | 70.0 MPa | 10200 psi | ASTM Data |
BASF Capron® 8360 HS 34% Mineral-Filled Nylon 6 (Conditioned)
(discontinued **) Capron 8360 HS is a heat stabilized 34% mineral reinforced nylon 6 injection molding resin possessing a high level of toughness and ductility combined with excellent processability and surface aesth.. |
|||
Flexural Yield Strength | 70.0 - 140 MPa | 10200 - 20300 psi | Average value: 101 MPa Grade Count:22 |
Overview of materials for Melamine-Phenolic Copolymer This property data is a summary of similar materials in the MatWeb database for the category "Melamine-Phenolic Copolymer". Each property range of values reported is minimum and maximum values of ap.. |
|||
Flexural Yield Strength | 70.0 - 234.422 MPa @Temperature -40.0 - 121 °C |
10200 - 34000.1 psi @Temperature -40.0 - 250 °F |
Average value: 113 MPa Grade Count:22 |
Overview of materials for Polypropylene with 30% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Glass Fiber Filler". Specific grades with glass content between 25% and 34% are i.. |
|||
Flexural Yield Strength | 70.0 - 131 MPa | 10200 - 19000 psi | Average value: 105 MPa Grade Count:7 |
Overview of materials for Polybutylene Terephthalate (PBT), Aramid Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Aramid Fiber Filled". Each property range of values reported is minimu.. |